Análise experimental de pilares de concreto com armadura de bambu sob flexocompressão / Experimental analysis of concrete columns with bamboo reinforcement under eccentric compression / Análise experimental de pilares de concreto com armadura de bambu sob flexocompressão
Nzambi, Aaron Kadima LukanuLwa; Oliveira, Dênio Ramam Carvalho de; Coêlho, Euclydes Luiz Pires.
Resumo em português
Resumo Esta pesquisa avaliou o comportamento de flexocompressão na rigidez da conexão viga-pilar com o uso de armadura de bambu da espécie Bambusa vulgaris como alternativa de substituição à armadura convencional de aço, na expectativa de utilizar um material com viés ecológico. Foram confeccionados 4 pilares de concreto armado de comprimento 1.600 mm e de seções transversais de 140x140 mm² e de 140x310 mm² no trecho interno e nas extremidades do pilar respectivamente, simulando a conexão viga-pilar. Os pilares tinham como única variável a taxa de armadura longitudinal, de 1,03% para o pilar convencional, de 2,14%, 3,21% e 4,29% para os pilares com o bambu. Os resultados quanto à capacidade resistente mostraram que o pilar com a taxa de bambu de 4,29%, ou seja, com a área de armadura quatro vezes a área do aço, apresentou comportamento similar ao pilar com armadura convencional e teve o menor índice de ductilidade, reduzindo consideravelmente a propagação das fissuras. As estimativas teóricas apresentaram variabilidade de apenas 9%. Assim, o bambu, com taxa e aderência adequadas, revelou-se uma alternativa tecnicamente viável e sustentável ao aço na fabricação de elementos estruturais de concreto armado. vigapilar viga ecológico 1600 1 600 1.60 x 140x14 140x31 respectivamente vigapilar. pilar. longitudinal 103 03 1,03 214 2 14 2,14% 321 3 21 3,21 429 29 4,29 seja ductilidade fissuras 9 9% Assim adequadas revelouse revelou se 160 60 1.6 140x1 140x3 10 0 1,0 2,14 32 3,2 42 4,2 16 6 1. 140x 1, 2,1 3, 4, 2,
Resumo em inglês
Abstract This research evaluated the flexo-compression behavior in the rigidity of the beam-pillar connection with the use of bamboo armor of the species bamboo vulgaris as an alternative replacement to conventional steel reinforcement, in the expectation of using an alternative material with ecological biases. They have manufactured reinforced concrete pillars of length 1,600 mm and cross-sections (140 x 140) mm² and (140 x 310) mm² were made, respectively, in the internal stretch and at the ends of the pillar, simulating the beam-pillar connection. The pillars had as their only variable the longitudinal reinforcement rate, of 1.03% for the conventional pillar, of 2.14%, 3.21% and 4.29% for the pillars with the bamboo. The results regarding the resistant capacity showed that the pillar with the bamboo rate of 4.29%, that is, with the reinforcement area four times the steel area, presented similar behavior to the pillar with conventional reinforcement and had the lowest ductility index, considerably reducing the propagation of cracks. And the theoretical estimates showed variability of only 9%. Thus, bamboo, with an adequate rate and adhesion, revealed a technically viable and sustainable alternative to steel in the manufacture of reinforced concrete structural elements. flexocompression flexo compression beampillar beam biases 1600 1 600 1,60 crosssections cross sections 140 (14 310 made respectively 103 03 1.03 214 2 14 2.14% 321 3 21 3.21 429 4 29 4.29 is index cracks 9 9% Thus adhesion elements 160 60 1,6 (1 31 10 0 1.0 2.14 32 3.2 42 4.2 16 6 1, ( 1. 2.1 3. 4. 2.
Abstract This research evaluated the flexo-compression behavior in the rigidity of the beam-pillar connection with the use of bamboo armor of the species bamboo vulgaris as an alternative replacement to conventional steel reinforcement, in the expectation of using an alternative material with ecological biases. They have manufactured reinforced concrete pillars of length 1,600 mm and cross-sections (140 x 140) mm² and (140 x 310) mm² were made, respectively, in the internal stretch and at the ends of the pillar, simulating the beam-pillar connection. The pillars had as their only variable the longitudinal reinforcement rate, of 1.03% for the conventional pillar, of 2.14%, 3.21% and 4.29% for the pillars with the bamboo. The results regarding the resistant capacity showed that the pillar with the bamboo rate of 4.29%, that is, with the reinforcement area four times the steel area, presented similar behavior to the pillar with conventional reinforcement and had the lowest ductility index, considerably reducing the propagation of cracks. And the theoretical estimates showed variability of only 9%. Thus, bamboo, with an adequate rate and adhesion, revealed a technically viable and sustainable alternative to steel in the manufacture of reinforced concrete structural elements. flexocompression flexo compression beampillar beam biases 1600 1 600 1,60 crosssections cross sections 140 (14 310 made respectively 103 03 1.03 214 2 14 2.14% 321 3 21 3.21 429 4 29 4.29 is index cracks 9 9% Thus adhesion elements 160 60 1,6 (1 31 10 0 1.0 2.14 32 3.2 42 4.2 16 6 1, ( 1. 2.1 3. 4. 2.
Resumo Esta pesquisa avaliou o comportamento de flexocompressão na rigidez da conexão viga-pilar com o uso de armadura de bambu da espécie Bambusa vulgaris como alternativa de substituição à armadura convencional de aço, na expectativa de utilizar um material com viés ecológico. Foram confeccionados 4 pilares de concreto armado de comprimento 1.600 mm e de seções transversais de 140x140 mm² e de 140x310 mm² no trecho interno e nas extremidades do pilar respectivamente, simulando a conexão viga-pilar. Os pilares tinham como única variável a taxa de armadura longitudinal, de 1,03% para o pilar convencional, de 2,14%, 3,21% e 4,29% para os pilares com o bambu. Os resultados quanto à capacidade resistente mostraram que o pilar com a taxa de bambu de 4,29%, ou seja, com a área de armadura quatro vezes a área do aço, apresentou comportamento similar ao pilar com armadura convencional e teve o menor índice de ductilidade, reduzindo consideravelmente a propagação das fissuras. As estimativas teóricas apresentaram variabilidade de apenas 9%. Assim, o bambu, com taxa e aderência adequadas, revelou-se uma alternativa tecnicamente viável e sustentável ao aço na fabricação de elementos estruturais de concreto armado. vigapilar viga ecológico 1600 1 600 1.60 x 140x14 140x31 respectivamente vigapilar. pilar. longitudinal 103 03 1,03 214 2 14 2,14% 321 3 21 3,21 429 29 4,29 seja ductilidade fissuras 9 9% Assim adequadas revelouse revelou se 160 60 1.6 140x1 140x3 10 0 1,0 2,14 32 3,2 42 4,2 16 6 1. 140x 1, 2,1 3, 4, 2,