ABSTRACT In this work, the synthesis of MgxGa1-xFe2O4 magnetic nanoparticles (MNPs) by sol-gel method is presented. All synthesized samples were identified as a crystalline single phase and the saturation magnetization (Ms) values are within the range of 21,2 to 46,4 emu/g, while coercive field values are less than 100 Oe. The selected samples (x= 0,4 and 0,6) have an average particle size of 14 ± 4 nm, a near spherical shape and by solid state magnetic induction it was possible to demonstrate that a quantity of 6,0 mg of nanoparticles per mL of solution is enough to increase the temperature of the medium (H2O) up to 43,5 °C in less than 10 min. According to the presented results these synthesized nanoparticles are potential materials for their use in cancer treatment by magnetic hyperthermia therapy.
RESUMEN En este trabajo se documenta la síntesis de nanopartículas magnéticas (NPMs) de MnxGa1-xFe2O4, x=0,1 por el método de sol-gel identificando, para cada una de las muestras sintetizadas, la obtención de una única fase cristalina, valores de magnetización de saturación en el rango de 21,2 a 46,4 emu/g y valores de Hc menores a los 100 Oe. Las muestras seleccionadas (x= 0,4 y 0,6) poseen un tamaño promedio de 14 ± 4 nm y una forma cercana a la esférica y mediante la técnica de inducción magnética en estado sólido se encontró que una cantidad de 6,0 mg de nanopartículas por mL de solución es suficiente para incrementar la temperatura del medio (H2O) por encima de los 43,5 °C en un tiempo menor a los 10 min, haciendo a estos materiales potencialmente viables para su uso en el tratamiento del cáncer mediante la terapia de hipertermia magnética.