Abstract Obtaining collagen and hydrolysates from mechanically separated chicken meat residue is an excellent way to add value to this waste. The aims of this study were to obtain collagen hydrolysates from chicken MSM residue using Alcalase® and Flavourzyme® enzymes, as well characterizing the functional, structural and thermal stability properties. The highest degree of hydrolysis was obtained using Alcalase®, 36.11%, while using Flavourzyme® resulted in 12.02%. The DSC analysis of the collagen indicated a denaturation temperature of 46.47 °C. The FTIR spectra of the crude collagen showed absorption peaks that were characteristic of amide bands A, B, I, II and III. In the spectra of the hydrolysed the area of the amide bands was reduced, and some peaks appeared between 800 and 1,200 cm-1. The disappearance of high molecular weight bands in the SDS-PAGE analysis also confirmed the hydrolysis of collagen. After the hydrolysis, the collagen presented reduced viscosity, the capacity to form foam, and foam stability. The emulsifying activity index was high in the hydrolysates in relation to the crude collagen. Thus, the use of Alcalase® and Flavourzyme® to obtain hydrolysates from collagen derived from chicken MSM residue was shown to be viable, and potentially useful for industrial applications.

Abstract Ginger and white yam starches were investigated and compared with maize starch. Proximal composition, thermogravimetry, differential scanning calorimetry, microscopy, colourimetry, X-ray powder diffractometry and pasting profile were analysed. The unconventional starches presented higher protein and ash contents than the maize starch, that had the highest thermal stability. Higher gelatinisation temperatures were reported for ginger starch, and the enthalpy of the unconventional starches were similar. The maize starch presented the lowest gelatinisation values. For the corn starch the granules were polygonal and smaller than the unconventional starches, and oval shapes and larger diameters were found for the ginger and yam starches. The unconventional starches presented less brightness and a greater tendency to red and yellow. The maize and ginger starches had A-type diffraction patterns, while the white yam starch had a C-type pattern. The highest relative crystallinity was observed for the ginger starch and there were small differences between the yam and maize starches. Higher peak viscosity and final viscosity and lower pasting temperature were observed for the yam starch. Ginger starch showed the highest shear and stability of heating glue, so may be used in products processed under high temperatures; and yam starch can be used in acidic foods that require high viscosities.