Abstract The objective is to evaluate the effect of different surface treatments and storage on the shear strength of ultratranslucent zirconia. 36 blocks of ultra-translucent zirconia were fabricated (7x7x2mm) and sintered. Then, divided into 12 groups according to the “surface treatment” (C -Primer; Al -Sandblasting with Al2O3 + Primer; Si -Silicate + Primer; Gl -Glaze + HF + Primer; Z -Zirlink; Zp -Zirlink + Primer) and “storage” factors (ST-with 150 days/37º and without). After surface treatment, five cylinders (Ø=2mm; h=2.0mm) of resin cement (n=15) were constructed in each ceramic block; at the end, the shear strength test was performed (1mm/min, 50Kgf), and analysis of surface failures. 60 additional samples (2x2x2mm) were made for extras analysis (surface roughness, MEV, and EDS). Bond strength and surface roughness data were statistically evaluated by ANOVA (2 factors/1 factor), Tukey test (5%), and Weibull analysis, respectively. ANOVA (2-way) revealed that all factors were statistically significant for bond strength. The silicatization groups (SiST: 30.47AMPa; Si: 29.21AMPa) showed the highest bond strength values, regardless of storage (Tukey's test). While the groups treated with Zirlink (ZST: 2.76FMPa; Z: 5.27EFMPa) showed the lowest values, just similar to the GlST group (5.14EFMPa). The Weibull modulus (m) showed a statistical difference between groups (p=0.000). ANOVA (1 factor) revealed that the "surface treatment" factor (p=0.0000) was statistically significant for surface roughness. Therefore, the application of Zirlink and Glaze on pre-sintered zirconia did not promote efficient adhesion of the ultratranslucent zirconia to the resin cement, even when associated with a primer containing MDP. 3 ultra translucent 7x7x2mm xxmm x mm (7x7x2mm sintered Then 1 treatment C Primer -Primer Sandblasting AlO O Al2O Silicate “storage STwith ST 15 days37º daysº days 37º º without. without . without) Ø=2mm Ø2mm Ømm Ø 2mm (Ø=2mm h=2.0mm h20mm hmm h 2 0mm n=15 n15 n (n=15 block end 1mm/min, 1mmmin mmmin 1mm min (1mm/min 50Kgf, 50Kgf Kgf , 50Kgf) failures 6 2x2x2mm (2x2x2mm MEV EDS. EDS EDS) ( factors1 factors/ factor, 5%, 5 5% (5%) respectively 2way way (2-way SiST (SiST 30.47AMPa 3047AMPa AMPa 30 47AMPa 29.21AMPa 2921AMPa 29 21AMPa values Tukeys s test. test) ZST (ZST 2.76FMPa 276FMPa FMPa 76FMPa 5.27EFMPa 527EFMPa EFMPa 27EFMPa 5.14EFMPa. 514EFMPa 5.14EFMPa 14EFMPa (5.14EFMPa) m (m p=0.000. p0000 p p=0.000 0 000 (p=0.000) p=0.0000 p00000 0000 (p=0.0000 Therefore presintered pre MDP n=1 n1 (n=1 1mm/min (5% (5.14EFMPa p000 p=0.00 00 (p=0.000 n= (n= (5 p00 p=0.0 (p=0.00 (n p0 p=0. (p=0.0 p=0 (p=0. p= (p=0 (p= (p

Resumo O objetivo é avaliar o efeito de diferentes tratamentos superficiais e do envelhecimento na resistência ao cisalhamento da zircônia ultratranslúcida. Foram confeccionados 36 blocos de zircônia ultratranslúcida (7x7x2mm) e sinterizados. Em seguida, divididos em 12 grupos de acordo com o “tratamento de superfície” (C-Primer; Al-Jateamento com Al2O3+Primer; Si-Silicato+Primer; Gl -Glaze+HF+Primer; Z-Zirlink; Zp-Zirlink+Primer) e fatores de “armazenamento” (ST-com, 150 dias/37º e sem). Após o tratamento superficial, foram construídos cinco cilindros (Ø=2mm; h=2,0mm) de cimento resinoso (n=15) em cada bloco cerâmico; ao final foi realizado o ensaio de resistência ao cisalhamento (1mm/min, 50Kgf) e análise de falhas superficiais. Foram confeccionadas 60 amostras adicionais (2x2x2mm) para análises extras (rugosidade superficial, MEV e EDS). Os dados de resistência de união e rugosidade superficial foram avaliados estatisticamente por ANOVA (2 fatores/1fator), teste de Tukey (5%) e análise de Weibull, respectivamente. ANOVA (2 fatores) revelou que todos os fatores foram estatisticamente significativos para a resistência de união. Os grupos de silicatização (SiST: 30,47AMPa; Si: 29,21AMPa) apresentaram os maiores valores de resistência de união, independente do armazenamento (Tukey). Enquanto os grupos tratados com Zirlink (ZST: 2,76FMPa; Z: 5,27EFMPa) apresentaram os valores mais baixos, apenas semelhantes ao grupo GlST (5,14EFMPa). O módulo de Weibull (m) apresentou diferença estatística entre os grupos (p=0,000). A ANOVA (1 fator) revelou que o fator “tratamento superficial” (p=0,0000) foi estatisticamente significativo para rugosidade superficial. Portanto, a aplicação de Zirlink e do Glaze na zircônia pré-sinterizada não promoveu adesão eficiente da zircônia ultratranslúcida ao cimento resinoso, mesmo quando associada a primer contendo MDP. 3 7x7x2mm xxmm x mm (7x7x2mm sinterizados seguida 1 superfície CPrimer C Primer (C-Primer AlJateamento Al Jateamento Al2O3+Primer Al2O3Primer AlOPrimer Al2O3 SiSilicato+Primer SiSilicatoPrimer Si Silicato+Primer Silicato Si-Silicato+Primer Glaze+HF+Primer GlazeHFPrimer HF -Glaze+HF+Primer ZZirlink Z Z-Zirlink ZpZirlink+Primer ZpZirlinkPrimer Zp Zirlink+Primer Zp-Zirlink+Primer “armazenamento STcom, STcom ST com, (ST-com 15 dias37º diasº dias 37º º sem. sem . sem) Ø=2mm Ø2mm Ømm Ø 2mm (Ø=2mm h=2,0mm h20mm hmm h 2 0mm n=15 n15 n (n=15 cerâmico 1mm/min, 1mmmin mmmin 1mm min (1mm/min 50Kgf Kgf 6 2x2x2mm (2x2x2mm EDS. EDS EDS) ( fatores/1fator, fatores1fator fatoresfator fatores/1fator , 1fator fatores/1fator) 5% 5 (5% respectivamente SiST (SiST 30,47AMPa 3047AMPa AMPa 30 47AMPa 29,21AMPa 2921AMPa 29 21AMPa Tukey. (Tukey) ZST (ZST 2,76FMPa 276FMPa FMPa 76FMPa 5,27EFMPa 527EFMPa EFMPa 27EFMPa baixos 5,14EFMPa. 514EFMPa 5,14EFMPa 14EFMPa (5,14EFMPa) m (m p=0,000. p0000 p p=0,000 0 000 (p=0,000) p=0,0000 p00000 0000 (p=0,0000 Portanto présinterizada pré sinterizada MDP AlO Al2O SiSilicato SilicatoPrimer ZpZirlink ZirlinkPrimer n=1 n1 (n=1 1mm/min (5 (Tukey (5,14EFMPa p000 p=0,00 00 (p=0,000 n= (n= p00 p=0,0 (p=0,00 (n p0 p=0, (p=0,0 p=0 (p=0, p= (p=0 (p= (p

ABSTRACT Objectives: To evaluate the translucency, contrast ratio and masking ability of a translucent zirconia with different thicknesses. Methods: Disc shaped specimens (n= 3) with 10 mm (Ø) x 1.5 mm, 1 mm and 0.7 mm (thickness) were manufactured simulating all-ceramic simplified restorations. Substrate discs (n= 2; Ø: 10 mm; thickness: 2 mm) were simulated with composite resin shades: A2 (positive control) and C4; and metal alloys: silver (Ni-Cr) and golden (Cu-Al). Optical properties of the 9 translucent zirconia specimens placed on the 3 different substrates were analyzed by a spectrophotometer. The color variation (ΔE00) between each ceramic structure over the positive control substrate (A2) and over the dark backgrounds (C4, silvery, golden) were obtained as to their ceramic masking ability and subjected to non-parametric Kruskal Wallis test (5%). The translucency parameter (TP00) and contrast ratio (CR) of the different thicknesses of the ceramic discs were also collected and analyzed by one-way ANOVA and the Tukey test (5%). Results: The translucent zirconia showed greater opacity in the thickness of 1.5 mm, although it was not statistically different between 0.7 and 1.0 mm. All dark backgrounds significantly affected the final color of the simplified restoration in all evaluated thicknesses. However, the increase in ceramic thickness showed a decrease in ΔE00 values for all substrates. Conclusion: The translucent zirconia was not able to mask the dark substrates, independent of the evaluated thickness. Objectives Methods n= n (n Ø (Ø 15 5 1. 07 0 7 0. (thickness allceramic restorations shades A C4 C alloys NiCr Ni Cr (Ni-Cr CuAl. CuAl Cu Al . (Cu-Al) spectrophotometer ΔE (ΔE00 (A2 C4, (C4 silvery nonparametric non parametric 5%. 5% (5%) TP00 TP (TP00 CR (CR oneway one way Results However ΔE0 Conclusion (Cu-Al (ΔE0 (A (C (5% TP0 (TP0 (ΔE (5 (TP (

RESUMO Objetivos: Avaliar a translucidez, razão de contraste e capacidade de mascaramento de uma zircônia translúcida com diferentes espessuras. Métodos: Espécimes em forma de disco (n= 3) com 10 mm (Ø) x 1,5 mm, 1 mm e 0,7 mm (espessura) foram confeccionados simulando restaurações simplificadas em cerâmica pura. Discos de substrato (n= 2; Ø: 10 mm; espessura: 2 mm) foram simulados com as cores de resina composta: A2 (controle positivo) e C4; e ligas metálicas: prata (Ni-Cr) e ouro (Cu-Al). As propriedades ópticas dos 9 espécimes de zircônia translúcida posicionados nos 3 substratos diferentes foram analisadas por um espectrofotômetro. A variação de cor (ΔE00) entre cada espécime cerâmico sobre o substrato controle positivo (A2) e sobre os fundos escuros (C4, prateado, dourado) foi calculada quanto à capacidade de mascaramento da cerâmica e submetida ao teste não paramétrico de Kruskal Wallis (5%). O parâmetro de translucidez (TP00) e a razão de contraste (CR) das diferentes espessuras dos discos cerâmicos também foram coletados e analisados por ANOVA de uma via e teste de Tukey (5%). Resultados: A zircônia translúcida apresentou maior opacidade na espessura de 1,5 mm, embora não tenha sido estatisticamente diferente entre 0,7 e 1,0 mm. Todos os fundos escuros afetaram significativamente a cor final da restauração simplificada em todas as espessuras avaliadas. No entanto, o aumento da espessura da cerâmica mostrou uma diminuição nos valores de ΔE00 para todos os substratos. Conclusão: A zircônia translúcida não foi capaz de mascarar os substratos escuros, independente da espessura avaliada. Objetivos Métodos n= n (n Ø (Ø 15 5 1, 07 0 7 0, (espessura pura composta C4 C metálicas NiCr Ni Cr (Ni-Cr CuAl. CuAl Cu Al . (Cu-Al) espectrofotômetro ΔE (ΔE00 (A2 C4, (C4 prateado dourado 5%. 5% (5%) TP00 TP (TP00 CR (CR Resultados avaliadas entanto ΔE0 Conclusão avaliada (Cu-Al (ΔE0 (A (C (5% TP0 (TP0 (ΔE (5 (TP (

Abstract This laboratory study aimed to evaluate the influence of endodontic sealer and cervical limit of root filling on the discoloration of root canal treated teeth. Bovine incisors were randomly distributed into six experimental groups and control (n=21/group), according to the endodontic sealer used [AH Plus (AP); MTA Fillapex (MF) and Sealer Plus BC (SPB)] and the cervical limit of root filling [dental cervix (DC) or 2 mm in apical direction (2mm-AD)]. Tooth discoloration (ΔE) was evaluated by a digital spectrophotometer using the CIED2000 method. Color assessments were performed immediately before (baseline), 1 week, 1, 3, 6 months, and 1 year after obturation. Data were analyzed by ANOVA and Tukey’s post-hoc tests (α=5%). Teeth filled with the three sealers showed perceptible tooth discoloration (ΔE≥2.7) in 1 week, maintaining similar values over time. There was a significant difference between MF and SPB sealers in the 2mm-AD groups. In addition, 2mm-AD groups promoted significantly lower discoloration than DC groups for AH (3 months) and SPB (1 and 3 months) sealer,s. Teeth filled with AP, MF, and SPB sealers displayed discoloration from 1 week to one year, with differences between MF and SPB sealers. A cervical limit of filling material at 2 mm from the dental cervix seems more advisable, promoting lower crown discoloration. teeth n=21/group, n21group ngroup n=21/group , n 21 group (n=21/group) AP (AP) (MF (SPB) (DC 2mmAD. 2mmAD mmAD 2mm AD . (2mm-AD)] ΔE (ΔE CIED CIED200 method baseline, baseline (baseline) months obturation Tukeys Tukey s posthoc post hoc α=5%. α5 α α=5% 5 (α=5%) ΔE≥2.7 ΔE27 7 (ΔE≥2.7 time addition ( sealer,s advisable (n=21/group (AP (SPB (2mm-AD) CIED20 (baseline α=5 (α=5% ΔE≥2. ΔE2 (ΔE≥2. (2mm-AD CIED2 α= (α=5 ΔE≥2 (ΔE≥2 (α= ΔE≥ (ΔE≥ (α

Resumo O presente estudo laboratorial teve como objetivo avaliar a influência do cimento endodôntico e do limite cervical da obturação radicular na alteração de cor de dentes tratados endodonticamente. Incisivos bovinos foram distribuídos aleatoriamente em seis grupos experimentais e um controle (n=21/grupo), de acordo com o cimento endodôntico utilizado [AH Plus (AP); MTA Fillapex (MF) e Sealer Plus BC (SPB)] e o limite cervical da obturação [Colo dentário (CD) ou 2mm na direção apical (2mm-DA)]. A alteração de cor (ΔE) foi avaliada por um espectofotômetro digital usando o método CIED2000. As avaliações de cor foram realizadas imediatamente antes (baseline), 1 semana, 1, 3, 6 meses e 1 ano após a obturação. Os dados foram analisados pelos testes ANOVA e post-hoc de Tuckey (α=5%). Dentes obturados com os três cimentos apresentaram alteração de cor perceptível (ΔE≥2.7) em 1 semana, mantendo valores semelhantes ao longo do tempo. Houve uma diferença significativa entre os cimentos MF e SPB nos grupos 2mm-DA. Além disso, os grupos 2mm-DA promoveram uma alteração de cor significativamente menor do que o grupos CD para os cimentos AH (3 meses) e SPB (1 e 3 meses). Os dentes obturados com os cimentos AH, MF e SPB apresentaram alteração de cor entre 1 semana a um ano, com diferenças entre os cimentos MF e SPB. O limite cervical do material obturador a 2mm do colo dentário parece mais aconselhável, promovendo menor alteração de cor da coroa dentária. endodonticamente n=21/grupo, n21grupo ngrupo n=21/grupo , n 21 grupo (n=21/grupo) AP (AP) (MF (SPB) Colo (CD mm 2mmDA. 2mmDA mmDA DA . (2mm-DA)] ΔE (ΔE CIED2000 CIED baseline, baseline (baseline) posthoc post hoc α=5%. α5 α α=5% 5 (α=5%) ΔE≥2.7 ΔE27 2 7 (ΔE≥2.7 tempo DA. disso ( meses. aconselhável dentária (n=21/grupo (AP (SPB (2mm-DA) CIED200 (baseline α=5 (α=5% ΔE≥2. ΔE2 (ΔE≥2. (2mm-DA CIED20 α= (α=5 ΔE≥2 (ΔE≥2 CIED2 (α= ΔE≥ (ΔE≥ (α

Aim This study assessed the color and translucency stability of a polymer infiltrated ceramic network (PICN) and compared it with a resin composite (RC) and a feldspathic ceramic (FEL). Methods Disc-shaped samples of a PICN (Vita Enamic), a feldspathic ceramic (Vitablocks Mark II), and a resin composite (Brava block) were prepared from CAD/CAM blocks. PICN and RC surfaces were finished with a sequence of polishing discs and diamond paste. FEL samples received a glaze layer. The samples were subjected to 30-min immersions in red wine twice a day for 30 days. CIE L*a*b* coordinates were assessed with a spectrophotometer at baseline and after 15 and 30 days of immersion. Color alteration (∆E 00 ) and translucency parameter (TP 00 ) were calculated with CIEDE2000. Average roughness was measured before the staining procedures. Color difference and translucency data were analyzed with repeated-measures ANOVA and Tukey’s tests. Roughness was analyzed with the Kruskal-Wallis test. Results Roughness was similar among the experimental groups. All materials had their color alteration significantly increased from 15 to 30 days of staining. PICN reached an intermediate ∆E 00 between FEL and RC at 15 days. PICN revealed a color alteration as high as the composite after 30 days. No statistical difference was observed regarding translucency. Conclusion PICN was not as color stable as the feldspathic ceramic at the end of the study. Its color alteration was comparable to the resin composite when exposed to red wine. However, the translucency of the tested materials was stable throughout the 30-day staining.

Resumo O presente estudo objetivou investigar a influência do ambiente de teste no comportamento a fadiga estática (resistência à fratura e tempo para falha) de cerâmicas à base de dissilicato de lítio (LD) e zircônia estabilizada com ítria (YSZ). Espécimes de LD (IPS e.max CAD, Ivoclar Vivadent) e YSZ (IPS e.max ZirCAD MO, 3mol% Y2O3, Ivoclar Vivadent) foram obtidos e alocados aleatoriamente em três grupos: testado em ar, em líquido inerte (óleo de parafina) ou em água destilada. O teste de fadiga estática (n= 15) foi realizado usando o teste pistão sobre três esferas, ISO 6872, da seguinte forma: carga inicial 100 N para LD e 300 N para YSZ; tempo de aplicação de carregamento definido para 1 hora para cada etapa de carregamento; tamanho do passo de 50 N para LD e 100 N para YSZ, aplicados sucessivamente até a fratura. Dados de resistência à fadiga estática (MPa) e tempo até a fratura (horas) foram registrados. A análise fractográfica foi executada. A análise de sobrevivência corrobora a ausência de influência do ambiente de teste nos resultados de fadiga estática (resistência à fadiga, tempo de fratura e taxas de sobrevivência) para a YSZ. Para LD, os corpos de prova testados em ar apresentaram taxa de sobrevivência e resistência à fadiga estática estatisticamente superiores (p= 0,025). Em relação ao tempo de fratura, os espécimes LD testados em ar foram superiores aos testados em água destilada (p= 0,019) ou em ambiente inerte (p= 0,017). Não foram observadas diferenças estatísticas para o módulo de Weibull. Todas as falhas começaram no lado onde se concentra a tensão de tração (lado de baixo) durante o teste. Com base nisso, observa-se que o ambiente de teste não afetou os mecanismos de crescimento lento de trinca durante o teste de fadiga estática da cerâmica YSZ, mas desempenha um papel significativo na resistência à fadiga estática da cerâmica de vidro à base de dissilicato de lítio, indicando alta susceptibilidade ao crescimento lento e subcrítico de trincas.

Abstract It aims on evaluate the effect of the test environment on static fatigue behavior of lithium disilicate-based (LD), and yttrium oxide-stabilized zirconia (YSZ) ceramics. Specimens of LD (IPS e.max CAD, Ivoclar Vivadent) and YSZ (IPS e.max ZirCAD MO, 3 mol% Y2O3, Ivoclar Vivadent) were randomly allocated into three groups: tested in air, inert (paraffin oil, Sigma Aldrich) or distilled water. The static fatigue test (n=15) was performed using a piston-on-three ball assembly, adapted from ISO 6872, as follows: starting load 100 N for LD and 300 N for YSZ; loading application time set to 1 hour for each loading step; step size of 50 N for LD and 100 N for YSZ, applied successively until fracture. Data from static fatigue strength (MPa) and time to fracture (hours) were recorded. Fractographic analysis was executed. Survival analysis corroborates absence of influence of environment on static fatigue outcomes (fatigue strength, time to fracture and survival rates) for YSZ. For LD, specimens tested in air presented statistically superior survival rate and static fatigue strength (p= 0.025). In regards of time to fracture, LD tested in air were superior than when tested in distilled water (p=0.019) or inert (p=0.017) environments. No statistical differences for Weibull modulus were observed. Failures started on the tensile stress surface. Thus, the test environment did not affect slow crack growth (SCG) mechanisms during static fatigue test of YSZ ceramics, but it plays a significant role for the static fatigue behavior of lithium disilicate-based glass ceramics, indicating a high susceptibility to SCG.

Cromossomos em metáfases mitóticas e núcleos interfásicos em 9 populações de 3 espécies sul-americanas de Lathyrus (L. pubescens, L.nervosus e L.crassipes) e 6 populações da espécie cultivada L. odoratus foram analisados. Todas as populações apresentaram 2n = 2x = 14 cromossomos. As diferenças significativas observadas entre as populações dentro de cada espécie e entre as espécies foram: número de cromossomos metacêntricos, submetacêntricos e subtelocêntricos; número e localização das constrições secundárias; comprimento dos cromossomos (maior e menor); complemento total haplóide; razão braço longo/braço curto e índice centromérico. L. odoratus é a espécie com maior tendência simétrica em seu cariótipo, enquanto que nas três espécies sul-americanas os cariótipos têm tendência moderada para assimetria, sendo L. pubescens o mais assimétrico. Com nitrato de prata foi possível identificar as NORs e o número máximo de nucléolos por núcleo interfásico em cada espécie. Em L. pubescens e L. nervosus as NORs estão localizadas na constrição secundária do braço longo do par 7, em L. crassipes a NOR é proximal, localizada no par de cromossomos metacêntricos, e em L. odoratus foram observadas quatro NORs terminais nos braços curtos dos pares 4 e 5. As quatro espécies possuem número máximo de quatro nucléolos em cada núcleo interfásico, indicando quatro regiões com genes ribossomais ativos em cada espécie.

Mitotic metaphase chromosomes and interphase nuclei of nine populations of three South American species of Lathyrus (L. pubescens, L. nervosus and L. crassipes) and six populations of the cultivated species L. odoratus were analyzed. All populations had 2n = 2x = 14 chromosomes. There were significant differences among populations within each species and among species in the number of metacentric, submetacentric and subtelocentric chromosomes, the number and location of secondary constrictions, chromosome length (longest and shortest), total haploid complement, arm ratio, and centromeric index. L. odoratus showed the highest tendency towards karyotype symmetry whereas the three South American species showed a moderate tendency towards asymmetry, with L. pubescens being the most asymmetrical. Silver staining was used to identify the nucleolar organizer regions (NORs) and the number of nucleoli per interphase nucleus in each species. In L. pubescens and L. nervosus, the NORs were located on the secondary constriction of the long arm of pair 7, in L. crassipes, the NOR was proximal being located in the pair of metacentric chromosomes, and in L. odoratus there were four terminal NORs on the short arms of pairs 4 and 5. The four species had a maximum of four nucleoli per interphase nucleus, indicating the presence of four regions with active ribosomal genes in each case.

Doze populações de sete espécies de Adesmia DC. das séries subnudae, bicolores e psoraleoides, nativas do Rio Grande do Sul, Brasil, foram estudadas pela primeira vez, quanto ao comportamento meiótico: A. securigerifolia 9615 e A. riograndensis 9590 (subnudae), com 2n = 2x = 20 cromossomos; A. latifolia populações 1568, 1775, 15025, A. bicolor JB-UFSM, A. incana var. incana populações 9636, 9637, 10288, A. punctata var. hilariana populações 6885, 10812 (bicolores), todas com 2n = 2x = 20, com exceção da população 9637 de A. incana var. incana, tetraplóide com 2n = 4x = 40 e A. tristis 10757, com 2n = 2x = 20 (psoraleoides). As inflorescências foram fixadas em etanol:ácido acético (3:1) por 24 horas a 4°C e conservadas em etanol 70%. O material foi corado com orceína acética 1%. O comportamento meiótico das populações analisadas foi considerado normal. Os índices meióticos (MI) e as estimativas da viabilidade dos grãos de pólen situaram-se acima de 95%, com exceção de A. latifolia 1568 (MI = 89%). Os dados obtidos indicam plantas meioticamente estáveis e potencialmente férteis, provavelmente sem problemas para uso em programas de seleção, cruzamentos e produção de sementes viáveis.

Meiotic behavior in Adesmia DC. is described for the first time. The study encompassed twelve populations of seven Adesmia DC. species native to Rio Grande do Sul, Brazil. Populations with 2n = 2x = 20 are A. securigerifolia 9615, A. riograndensis 9590 (subnudae), A. latifolia 1568, 1775, 15025, A. bicolor JB-UFSM, A. incana var. incana 9636, 10288, A. punctata var. hilariana 6885, 10812, and A. tristis 10757. A. incana var. incana 9637 is a tetraploid with 2n = 4x = 40. The material was stained with 1% acetic orcein. The meiotic behavior of the populations studied was considered normal. The meiotic index (MI) and the estimates of pollen grain viability were above 95%, except for A. latifolia 1568 (MI = 89%). The present data indicate that these plants are meiotically stable and potentially fertile, apparently with no problems for use in programs of selection, crossing and viable seed production.

Populações de espécies de Adesmia DC. das séries bicolores e psoraleoides, nativas do Rio Grande do Sul, Brasil, foram estudadas para determinação do número cromossômico (11 populações de 5 espécies) e também quanto aos cariótipos (5 populações de 4 espécies). Todas as espécies estudadas quanto ao número cromossômico são diplóides (2n=2x=20), mas em A. incana var. incana foram encontradas duas populações diplóides e uma tetraplóide (2n=4x=40). A. incana não é uma espécie unicamente tetraplóide, como vinha sendo considerada até agora. A. bicolor 9614 parece ser a mais antiga entre as populações analisadas devido a sua alta simetria cariotípica e A. tristis 10814 parece ser a mais recente, devido ao seu cariótipo mais assimétrico.

Populations of Adesmia DC. species bicolores and psoraleoides series, nativo from Rio Grande do Sul, Brazil, were studied to determine the chromosome numbers (in 11 populations of 5 species) and Karyotypes (in 5 of these population in 4 species). All species studied regarding to the chromosome numbers were diploid (2n=2x=20) and in A. incana var. incana besides two diploid races there was one tetraploid race (2n=4x=40). A. incana should not be considered as a tetraploid species, as has been considered in the literature. A. bicolor 9614 seemed to be more ancient among the analized populations due to the high Karyotype symmetry. A. tristis seemed be more recent among the analysed populations due to the karyotype was highly asymmetry.