Abstract The innumerous advantages of heterogeneous catalysts employed in biodiesel production have stimulated the search for a solid catalyst capable of replacing the industrially used homogeneous catalysts. This paper investigates the effect of the sol-gel method in the catalytic activity and stability of Li-MgAl mixed oxides prepared by the “in situ” lithium addition to a MgAl hydrotalcite. The analyses based on N2 physisorption, thermogravimetric analysis, X-ray diffractometry, scanning electron microscopy and temperature-programmed desorption of CO2 were carried out to elucidate the properties of the catalysts. Considerable differences in the physico-chemical properties of the catalysts were observed with the Li addition. Li reduced the surface area and increased the crystallite size of the oxides. Furthermore, Li-MgAl mixed oxides prepared by the calcination of the sol-gel MgAl hydrotalcites presented substantial morphological differences when compared to the same oxides obtained by heat treatment of hydrotalcites synthesized via the conventional co-precipitation route. Furthermore, Li increased the number and strength of the base sites which resulted in the increase of the oxide reactivities towards the transesterification reaction between methyl acetate and ethanol. The activity was dependent on the Li loading on the catalysts. The catalyst containing only 5 wt.% Li turned out to be highly active (( 85% conversion at 50°C, ethanol/methyl acetate molar ratio = 6/1, 4 wt.% of catalyst and 30 min of reaction). Stability tests showed that the Li-MgAl catalysts lose activity after 3 reuse cycles.

In this work, composites based on activated carbon/iron oxide (AC/Fe) were prepared in two different proportions (AC/Fe 5/1 and 1/1) and evaluated in the removal of the organic dye methylene blue (MB). Physical-chemical properties of the composites were determined by X-ray diffraction (XRD), adsorption/dessorption of N2 isotherm, temperature programmed reduction (TPR) and scanning electron microscopy (SEM). Results showed that goethite (α- FeOOH), with nanometer particle size, was formed over carbon surface for both composites. These materials showed high efficiency to remove MB from solution by combined adsorption and oxidation process. The AC/Fe 1/1 showed to be more active in (MB) oxidation then AC/Fe 5/1.