Abstract This study aimed to evaluate the osteogenic potential of hydroxyapatite (HA), Alginate (Alg), and Gelatine (Gel) composite in a critical-size defect model in rats. Twenty-four male rats were divided into three groups: a negative control with no treatment (Control group), a positive control treated with deproteinized bovine bone mineral (DBBM group), and the experimental group treated with the new HA-Alg-Gel composite (HA-Alg-Gel group). A critical size defect (8.5mm) was made in the rat's calvaria, and the bone formation was evaluated by in vivo microcomputed tomography analysis (µCT) after 1, 15, 45, and 90 days. After 90 days, the animals were euthanized and histological and histomorphometric analyses were performed. A higher proportion of mineralized tissue/biomaterial was observed in the DBBM group when compared to the HA-Alg-Gel and Control groups in the µCT analysis during all analysis periods. However, no differences were observed in the mineralized tissue/biomaterial proportion observed on day 1 (immediate postoperative) in comparison to later periods of analysis in all groups. In the histomorphometric analysis, the HA-Alg-Gel and Control groups showed higher bone formation than the DBBM group. Moreover, in histological analysis, five samples of the HA-Alg-Gal group exhibited formed bone spicules adjacent to the graft granules against only two of eight samples in the DBBM group. Both graft materials ensured the maintenance of defect bone thickness, while a tissue thickness reduction was observed in the control group. In conclusion, this study demonstrated the osteoconductive potential of HA-Alg-Gel bone graft by supporting new bone formation around its particles. HA, HA , (HA) Alg, Alg (Alg) Gel (Gel criticalsize Twentyfour Twenty four group, group) HAAlgGel . 8.5mm 85mm mm 8 5mm (8.5mm rat s calvaria (µCT 15 45 9 days performed tissuebiomaterial biomaterial However immediate postoperative Moreover HAAlgGal Gal conclusion particles (HA (Alg 4

Resumo Este estudo teve como objetivo avaliar o potencial osteogênico de um compósito de hidroxiapatita (HA), alginato (Alg) e gelatina (Gel) em um modelo de defeito de tamanho crítico em ratos. Vinte e quatro ratos machos foram divididos em três grupos: um controle negativo sem tratamento (grupo controle), um controle positivo tratado com osso bovino desproteinizado (grupo DBBM) e o grupo experimental tratado com o novo compósito HA-Alg-Gel (grupo HA-Alg-Gel). Um defeito de tamanho crítico (8,5mm) foi feito na calvária dos ratos, e a formação óssea foi avaliada por análise de microtomografia computadorizada in vivo (µCT) após 1, 15, 45 e 90 dias. Após 90 dias, os animais foram eutanasiados e análises histológicas e histomorfométricas foram realizadas. Uma maior proporção de tecido mineralizado/biomaterial foi observada no grupo DBBM quando comparado aos grupos HA-Alg-Gel e controle na análise de µCT durante todos os períodos de análise. Entretanto, não foram observadas diferenças na proporção tecido mineralizado/biomaterial no dia 1 (pós-operatório imediato) em relação aos períodos posteriores de análise em todos os grupos. Na análise histomorfométrica, os grupos HA-Alg-Gel e controle apresentaram maior formação óssea do que o grupo DBBM. Além disso, na análise histológica, cinco amostras do grupo HA-Alg-Gal exibiram espículas ósseas formadas adjacentes aos grânulos do enxerto contra apenas duas das oito amostras do grupo DBBM. Ambos os materiais de enxerto garantiram a manutenção da espessura óssea do defeito, enquanto uma redução da espessura do tecido foi observada no grupo controle. Em conclusão, este estudo demonstrou o potencial osteocondutor do enxerto ósseo de HA-Alg-Gel, promovendo a formação de osso novo ao redor das suas partículas. HA, HA , (HA) Alg (Alg Gel (Gel controle, controle) HAAlgGel HAAlgGel. . HA-Alg-Gel) 8,5mm 85mm mm 8 5mm (8,5mm (µCT 15 4 9 dias realizadas mineralizadobiomaterial mineralizado biomaterial Entretanto pósoperatório pós operatório imediato histomorfométrica disso histológica HAAlgGal Gal conclusão HAAlgGel, Gel, partículas (HA

Abstract This study aimed to evaluate the effect of nicotine administration on the osseointegration of a superhydrophilic implants surface on rat tibiae. Thirty-two rats were used and divided into 2 groups according to the administration or not of nicotine: HH - Installation of implants with superhydrophilic surfaces in healthy animals; and HN - Installation of implants with superhydrophilic surfaces in animals subjected to nicotine administration. The animals were euthanized 15 and 45 days after implant placement (n = 8). Osseointegration was assessed by means of biomechanical analyses (removal torque), microcomputed tomography (volume of bone around the implants- %BV/TV), and histomorphometry (bone-implant contact -%BIC and the bone area between implant threads -%BBT). The animals subject to the nicotine administration presented lower removal torque than the control animals at the 45-day period (21.88 ± 2.80 Ncm vs. 17.88 ± 2.10 Ncm). The implants placed in the control rats presented higher %BIC (54.26 ± 6.59% vs. 39.25 ± 4.46%) and %BBT (50.57 ± 5.28% vs. 32.25 ± 5.24%) than the implants placed in nicotine animals at 15-day period. The nicotine administration reduces the osseointegration at 15 days, however, the superhydrophilic surface equalized the osseointegration in nicotine-exposed animals compared with healthy animals after 45 days of implant placement. tibiae Thirtytwo Thirty two 1 4 n 8. 8 . 8) torque, , torque) volume %BV/TV, BVTV %BV/TV BV TV %BV/TV) boneimplant BIC %BBT. BBT -%BBT) 45day day 21.88 2188 21 88 (21.8 280 80 2.8 vs 1788 17 17.8 210 10 2.1 Ncm. Ncm) 54.26 5426 54 26 (54.2 659 6 59 6.59 3925 39 25 39.2 4.46% 446 46 50.57 5057 50 57 (50.5 528 5 28 5.28 3225 32 32.2 5.24% 524 24 15day however nicotineexposed exposed -%BBT 21.8 218 (21. 2. 178 17. 54.2 542 (54. 65 6.5 392 3 39. 4.46 44 50.5 505 (50. 52 5.2 322 32. 5.24 21. (21 54. (54 6. 4.4 50. (50 5. (2 (5 4. (

Resumo O objetivo deste estudo foi avaliar o efeito da administração de nicotina na osseointegração de implantes com superfície modificada por jateamento de oxidos e ataque ácido instalados em tíbia de ratos. Foram utilizados 32 ratos que foram divididos em 2 grupos de acordo com a administração ou não de nicotina: HH - Instalação de implantes com superfícies superhidrofílicas em animais sadios; e HN - Instalação de implantes com superfícies superhidrofílicas em animais submetidos à administração de nicotina. Os animais foram eutanasiados 15 e 45 dias após a colocação do implante (n = 8). A osseointegração foi avaliada por meio de análises biomecânicas (torque de remoção), microtomografia (volume de osso ao redor dos implantes - %BV/TV) e histomorfometrica (contato osso-implante -%BIC e área óssea entre roscas do implante -%BBT). Os animais submetidos à administração de nicotina apresentaram menor torque de remoção do que os animais controle no período de 45 dias (21,88 ± 2,80 Ncm vs. 17,88 ± 2,10 Ncm). Os implantes colocados nos ratos controle apresentaram maiores %BIC (54,26 ± 6,59% vs. 39,25 ± 4,46%) e %BBT (50,57 ± 5,28% vs. 32,25 ± 5,24%) do que os implantes colocados nos animais submetidos a administração de nicotina no período de 15 dias. A administração de nicotina prejudicou a osseointegração no período de 15 dias. Entretanto, a superfície superhidrofílica equalizou a osseointegração em animais expostos à nicotina em comparação com animais saudáveis após 45 dias da colocação do implante. 3 sadios 1 4 n 8. 8 . 8) remoção, , remoção) volume %BV/TV BVTV BV TV contato ossoimplante BIC %BBT. BBT -%BBT) 21,88 2188 21 88 (21,8 280 80 2,8 vs 1788 17 17,8 210 10 2,1 Ncm. Ncm) 54,26 5426 54 26 (54,2 659 6 59 6,59 3925 39 25 39,2 4,46% 446 46 50,57 5057 50 57 (50,5 528 5 28 5,28 3225 32,2 5,24% 524 24 Entretanto -%BBT 21,8 218 (21, 2, 178 17, 54,2 542 (54, 65 6,5 392 39, 4,46 44 50,5 505 (50, 52 5,2 322 32, 5,24 21, (21 54, (54 6, 4,4 50, (50 5, (2 (5 4, (

Abstract Objective To evaluate the effect of different protocols of low-level intensity laser therapy (LLLT) irradiation on the osseointegration of implants placed in grafted areas. Methodology 84 rats were randomly allocated into six groups: DBB: defect filled with deproteinized bovine bone; HA/TCP: defect filled with biphasic ceramic of hydroxyapatite/β-tricalcium phosphate ; DBB-LI: defect filled with DBB and treated with LLLT after implant placement; HA/TCP-LI: defect filled with HA/TCP and treated with LLLT after implant placement; DBB-LIB: defect filled with DBB and treated with LLLT after graft procedure and implant placement; and HA/TCP-LIB: defect filled HA/TCP and treated with LLLT after graft procedure and implant placement. The bone defects were made in the tibia and they were grafted. After 60 days, the implants were placed. The rats were subsequently subjected to euthanasia 15 and 45 days after implant placement. The pattern of osseointegration and bone repair in the grafted area was evaluated by biomechanical, microtomographic, and histometric analyses. Furthermore, the expression of bone biomarker proteins was assessed. Results The LLLT groups presented higher removal torque, mineralized tissue volume, and a greater degree of osseointegration, especially when LLLT was performed only after implant placement, and these findings were associated with higher expression of BMP2 and alkaline phosphatase. Conclusion LLLT performed on implants placed in grafted areas enhances the osseointegration process.

Resumo Introdução A utilização de substitutos ósseos em procedimentos de enxertia de forma alternativa ao uso do osso autógeno tem sido indicada, entretanto a comparação direta entre esses biomateriais tem sido pouco explorada. Objetivo Avaliar o efeito de diferentes biomateriais osteocondutores sobre o reparo de defeitos críticos em calvárias (DCC) de ratos. Material e método Foram utilizados 40 ratos que foram submetidos a confecção de um DCC com 8 mm de diâmetro. Os animais foram aleatoriamente divididos em 5 grupos com 8 animais, de acordo com o tipo de biomaterial utilizado para preencher os DCC: Grupo COA (coágulo); Grupo AUT (osso autógeno); Grupo OBD (osso bovino desproteinizado); Grupo HA/ TCP (cerâmica bifásica composta de hidroxiapatita e β fosfato tricálcio); Grupo TCP (β fosfato tricálcio). Foram executadas análise microtomográfica para avaliação do comprimento linear remanescente (DLL) do DCC e o volume dos tecidos mineralizados (MT) dentro do DCC nos períodos de 3, 7, 15 e 30 dias após cirurgia. Adicionalmente, foi executado análise histométrica para avaliar a composição do tecido ósseo reparado (% Osso e % Biomaterial) no período de 30 dias. Resultado O grupo COA apresentou o menor DLL e MT dentro do DCC e maior % osso do que os outros grupos. O grupo OBD apresentou maior volume de tecidos mineralizados e maior % biomaterial do que o grupo os grupos AUT e TCP. Os grupos OBD e AUT apresentaram maior % osso que o grupo TCP. Conclusão O OBD promoveu melhor padrão de aumento de disponibilidade óssea e qualidade do osso reparado em comparação ao TCP e HA/TCP, porém biologicamente inferior ao grupo AUT.

Abstract Introduction The use of bone substitutes in grafting procedures as an alternative of the use of autogenous bone graft has been indicated, however, the direct comparison between these biomaterials has been little explored. Objective To evaluate the effect of different osteoconductive bone substitutes on the bone repair in critical-sized defects (CSDs) in rat calvaria. Material and method One CSD with an 8 mm diameter was made in each of the 40 rats used in this study. The animals were randomly allocated into 5 groups (n=8), according to the type of bone substitute used to fill the CSD: COA (Coagulum); AUT (autogenous bone); DBB (deproteinized bovine bone graft); HA/TCP (biphasic ceramic composed of hydroxyapatite and β-phosphate tricalcium); and TCP (β-phosphate tricalcium). A microtomographic analysis was performed to evaluate the remaining defect linear length (DLL) of the CSD and the volume of the mineralized tissues (MT) within the CSD at 3, 7, 15 and 30 days after the surgical procedure. In addition, a histometric analysis was performed to evaluate the composition of the repaired bone tissue (% Bone and % Biomaterial) at the 30-day period. Result It was shown that the COA had the lowest DLL and MT within the CSD. In addition, the COA presented the highest % of bone in CSD. The DBB had a higher MT and a higher % of bone substitute particles in the CSD than the AUT and TCP groups. The DBB and AUT groups presented higher % of bone in the CSD than the TCP group. Conclusion The use of the DBB promoted a better pattern of bone volume gain and formation compared to TCP and HA / TCP but was biologically inferior to the AUT.

Resumo Objetivo O objetivo desse estudo foi de comparar os achados clínicos obtidos no tratamento de recessões gengivais utilizando o enxerto de tecido conjuntivo subepitelial (SECT), a matriz dérmica acelular (ADM) e as proteínas derivadas da matriz do esmalte (EMP). Material e método Doze pacientes que apresentavam recessões gengival classe I e II de Miller nos caninos e pré-molares superiores foram randomicamente alocados para receber o SECT, ADM ou EMP. Análises clínicas foram executadas antes e 3 meses após os procedimentos cirúrgicos. Foram avaliados os seguintes parâmetros: porcentagem de recobrimento radicular, altura e comprimento da recessão gengival, profundidade de bolsa a sondagem, nível clínico de inserção, altura e espessura da gengiva queratinizada. O teste de Kruskal-Wallis complementado pelo teste de Dunn foram usados para avaliar as diferenças entre os grupos em cada período enquanto que o teste de Wilcoxon foi utilizado para avaliar as diferenças dentro de cada grupo variando-se o período de avaliação. Os teste foram aplicados com nível de confiança de 95%. Resultado Os grupos SECT e ADM apresentaram maior porcentagem de recobrimento radicular e maior redução da altura e comprimento das recessões do que o grupo EMP (p<0,05). Conclusão O SECT e a ADM são mais efetivos no tratamento de recessões gengivais que o EMP.

Abstract Objective The aim of this study was to compare clinical findings obtained in the treatment of gingival recessions using subepithelial connective tissue graft (SECT), acellular dermal matrix (ADM), and enamel matrix proteins (EMP). Material and method Twelve patients with Miller class I and II recession in the canines or upper premolars were randomly divided into groups to receive treatments using SECT, ADM, or EMP. Clinical measurements were performed before and three months after surgical procedures. The data evaluated were as follows: percentage of root coverage, height and width of gingival recession, probe depth, clinical attachment level, and height and thickness of keratinized gingiva. The Kruskal-Wallis test complemented by Dunn’s test was used to perform the between-group, analysis and the Wilcoxon test was used to perform the within-groups analysis. The tests were applied at the 95% confidence level. Result The SECT and ADM groups had a higher percentage of root coverage and greater reduction in the height and width of gingival recessions compared to the EMP group (p<0.05). Conclusion The SECT and ADM are more effective in treating gingival recessions than EMP.