The present work focused on the screening process of different inorganic oxides and different temperatures for the epoxidation reaction of macaw palm vegetable oil without using solvent, a promising Brazilian biomass that can substitute other vegetable oils (e.g., soybean oil) in technological applications. This oil has an iodine value of 108.48 g of I2 per 100 g being categorized as a semi-dry oil. The epoxidized vegetable oil can be applied in manifold areas in polymer science. The epoxidation reaction here presented avoided organic solvents and organic acids and aimed to produce a greener route using metal oxides or niobium phosphate as a peroxide-activating catalyst. The experimental parameters were maintained as 10 mol% of catalyst loading and a time of 24 h; however, the temperature for some catalysts was changed to improve the epoxide conversion. Experiments were measured by proton nuclear magnetic resonance (1H NMR). Experiments using titanium oxide (TiO2) as a catalyst reached a conversion greater than 84.7%, while experiments using aluminium oxide (Al2O3) or lanthanum oxide (La2O3) achieved conversions of 22.6 and 30.1%, respectively. Furthermore, it was observed that both niobium compounds instantly react with hydrogen peroxide to form peroxy derivatives. solvent e.g., eg e (e.g. applications 10848 108 48 108.4 I semidry semi dry science peroxideactivating activating 1 mol 2 h however 1H H NMR. NMR . NMR) TiO2 TiO (TiO2 847 84 7 84.7% Al2O3 AlO Al O (Al2O3 La2O3 LaO La (La2O3 226 22 6 22. 301 30 30.1% respectively Furthermore derivatives e.g. (e.g 1084 4 108. (TiO 8 84.7 Al2O (Al2O La2O (La2O 3 30.1 e.g 84. 30.

Vegetable oils are alternatives to producing renewable monomers since they are biomass. It is possible to react them with anhydrides by heating to provide monomers with high reactivity. However, after the reaction of grape seed oil with itaconic anhydride, it was observed the occurrence of parallel reactions that had not been observed when the same oil was reacted with maleic anhydride. Some articles in the literature have reported that temperature and bases can isomerize itaconic anhydride into citraconic anhydride, which is more stable at room temperature. However, they have not focused on completely understanding how this phenomenon occurred nor studied it in processes that involve microwave irradiation. Therefore, this paper presents a complete characterization and investigation about the thermal behavior of itaconic anhydride and how it can affect the monomer synthesis performed under heating. biomass reactivity However irradiation Therefore