Cobalt blue pigments were prepared by self-propagating combustion followed by sol-gel method using aluminum nitrate and cobalt nitrate as the raw material. X ray diffraction (XRD), scanning electron microscopy (SEM), fiber optic spectrometer and colorimetric analysis were used to investigate the effect of reaction temperature, metal ion concentration and dispersant upon the gel formation. The results show that the formation of gel network could be promoted by increasing the concentration of metal ion (0.01~0.2 mol/L) and sol-gel reaction temperature (80~90°C), and the disper-sibility and stability of the pigment powder could be improved with dispersing agent. The dried gel precursor was calcined at 1250 °C to form 200~500 nm cobalt aluminum with spinel structure with highly negative value of b*.

Al films and TiO2 films were separately coated on AZ31 magnesium alloy substrates by means of magnetron sputtering method. The surface properties of the samples were explored and compared. Scanning electron microscope (SEM) observed the compact structure characteristics of as-deposited Al films and TiO2 films. After heat treatment under 200ºC for half an hour the films kept the compact structure characteristics and there didn’t exist structural defects on the surface of the films. Nano-indentation measurement results display that the micro-hardness of as-deposited Al film and TiO2 film reaches about 1.90 Gpa and 1.51 Gpa, separately. Al film is a bit harder than TiO2 film. Finally, the corrosion experiments in simulated body fluid initially indicate the different corrosion properties for Al film and TiO2 film. Al film presents more effective anti-corrosion properties than TiO2 film.