Abstract A series of dynamic tests were conducted on a closed-cell aluminum alloy foams in order to determine experimental failure surface under impact loading conditions. Quasi-static tests have also been performed to investigate failure mechanism under different stress paths. Three typical types of deformation modes can be observed, which corresponds to the different failure mechanism. The failure loci of the foam in principal stress plane are explored from quasi-static to dynamic loading conditions. A significant strength enhancement is identified experimentally. The expansion of the failure locus from the quasi-static to the dynamic test is almost isotropic. A modified failure criterion for the metallic foam is proposed to predict failure locus as a function of strain rate. This rate-dependence failure criterion is capable of giving a good description of the biaxial failure stresses over a wide range of the strain rates.

Abstract Finite element analysis was used to investigate the impact behavior of the foam-cored sandwich shells under the ballistic impact. The ballistic limit, failure mode of the face-sheet and energy absorption of the uniform/graded core were discussed in this paper. Based on the impact phase diagrams, the effects of several factors (i.e. projectile shape and diameter, face-sheet curvature and thickness) on the normal/oblique impact behavior were analyzed in detail. Results indicate that blunter and larger projectiles, higher impact velocity and thicker face-sheets can significantly raise the impact-resistance performance of the targets. In addition, the behavior of ballistic impact becomes more complex as the result of the increasing oblique angle.

This paper presents an experimental investigation on the yield behavior of Nomex honeycombs under combined shearcompression with regard to out-of-plane direction. Four different types of specimens were designed in order to investigate the influence of in-plane orientation angle on the yield behavior of honeycombs under combined loads. Two different failure modes of honeycomb specimens, i.e. the plastic buckling and the extension fracture of cell walls, are observed under combined shear-compression. The experimental results validate that the in-plane orientation angle has a significant influence on the developments of the experimental yield surface. The experimental yield surfaces are compared with a phenomenological yield criterion capable of accounting for anisotropic behavior. The comparative analytical results indicate the experimental yield surfaces are approximately consistent with the theoretical yield surfaces in the normal-shear stress space. These experimental results are useful to develop constitutive models of Nomex honeycombs under combined shear-compression.