Abstract Au/TiO2 (1wt% Au), Cu/TiO2 (1wt% Cu) and AuCu/TiO2 (1wt% AuCu) catalysts with different Au:Cu mass ratios were prepared in one-step synthesis using sodium borohydride as reducing agent. The resulting catalysts were characterized by X-ray diffraction (XRD), X-ray Dispersive Energy (EDX), Transmission Electron Microscopy (TEM) and Temperature Programmed Reduction (TPR) and tested for the preferential oxidation of carbon monoxide (CO-PROX reaction) in H2-rich gases. EDS analysis showed that the Au contents are close to the nominal values whereas for Cu these values are always lower. X-ray diffractograms showed only the peaks of TiO2 phase; no peaks of metallic Au and Cu species or oxides phases were observed. TPR and high-resolution TEM analysis showed that AuCu/TiO2 catalysts exhibited most of Au in the metallic form with particles sizes in the range of 3-5 nm and that Cu was found in the form of oxide in close contact with the Au nanoparticles and well spread over the TiO2 surface. The AuCu/TiO2 catalysts exhibited good performance in the range of 75-100 °C and presented a better catalytic activity when compared to the monometallic ones. A maximum CO conversion of 98.4% with a CO2 selectivity of 47% was obtained for Au0.50Cu0.50/TiO2 catalyst at 100oC.

Au nanoparticles supported on TiO2 were prepared by a liquid-phase reduction method using HAuCl4.3H2O as the Au precursor, TiO2 as the support, a solution of ethylene glycol/water as solvent and reducing agent and sodium citrate as reducing agent and stabilizer. The Au/TiO2 catalysts were prepared using different routes and characterized by Energy-dispersive X-ray spectroscopy, X-ray diffraction and Transmission Electron Microscopy and tested for preferential oxidation of carbon monoxide in hydrogen-rich stream (CO-PROX reaction). The way that the Au precursor, the TiO2 support and the sodium citrate is added to the ethylene glycol/water solution strongly influences the Au nanoparticle sizes and the catalytic activity of the obtained materials.

TiO2 thin films were prepared by the sol-gel method using different acids (HCl and HAc), with a parallel evaluation of the gel ageing effects on the film properties. After the thermal treatments, the resulting materials were characterized through gravimetric analysis, UV-VIS spectrophotometry (from which optical parameters such as band gap was derived), XRD, morphological surface analysis (AFM) and photocatalytic activity. The majority of the obtained thin films parameters were similar independent of the acid type and the ageing time of the gel. Nevertheless, a visible effect of the surface morphology properties on the films and their photocatalytic activity was observed.

In this study the factors that affect the extraction of pesticide residues from water samples for their determination by solid-phase micro-extraction (SPME) and GC/MS were optimized. The fiber polymer, the extraction mode, the ionic strength, the stirring rate, the pH and the extraction time were the most significant parameters evaluated. The recovery obtained with the proposed method ranged from 94 to 110% and the sensitivity of the method, determined by calculating the detection limit (DL), ranged from 0.004 to 0.1 mug l-1. The results obtained with spiked real samples, at the 0.1 mug l-1 level, showed acceptable conformity with the expected values.

Polychlorinated biphenyls (PCBs) are a class of 209 chemical compounds with the molecular formula C12H10-nCl n, where 1 <= n <= 10. They were commercially produced as complex mixtures for various uses, being employed principally as dielectric fluids in capacitors and transformers. They are not easily degraded due their chemical and physical stability and tend to bioaccumulate in the organisms. After the discovery of their xenobiotic activity, restrictions were imposed for their use, as well as for their discards. Nowadays the development of recovery processes for contaminated environment urges to be done due to the extension of reached areas.

Some modifications made at silanization step and the introduction of r-nitrobenzil bromide as an alternative reagent to the 8-hydroxiquinolein immobilization in silica gel were important points that brought up the reduction of synthesis time, efficency improvement of the immobilization process and better hydrolysis stabilization to the final materials. The caracterization was made by infrared spectroscopy, elementary analysis, complexing capacity and acid-base properties.