In many applications, such as fuel storage tanks and fuel lines, galvanized steel is used as a construction material which comes into contact with biodiesel. Considering that biodiesel is more corrosive than petroleum diesel, studies that aim to increase the corrosion resistance of galvanized steel in this environment are required. The present work investigates how the chemical conversion treatment in the oxalic acid solution affects the corrosion resistance of galvanized steel in soybean biodiesel (B100) in the absence and presence of the natural additives the extract the turmeric, clove, ginger, stone breaker, and rosemary. The results obtained indicate that the conversion treatment reduces the corrosion rate of the zinc coating in soybean biodiesel in the absence and presence of additives, and in this condition the effect of the conversion treatment depends on the additive used. applications lines diesel required B100 B (B100 turmeric clove ginger breaker rosemary B10 (B10 B1 (B1 (B

This paper evaluates the effect of adding glycerol to the electrodeposition bath on the deposition efficiency and characteristics of Ni-Mo coating in concentrations ranging from 0.07 to 0.82 mol.L-1. Evaluation of the corrosion resistance was performed by means of weight loss tests in four different periods of immersion. Electrochemical techniques, such as obtaining polarization curves, linear polarization resistance, corrosion current density, corrosion potential, and electrochemical impedance spectroscopy were applied. Corrosion measurements were obtained in 0.5 mol.L-1 NaCl acid solution and 0.5 mol.L-1 NaOH alkaline solution. The morphology and microstructures of electrodeposited were analyzed using Scanning Electron Microscopy and Spectrometry X-Ray Diffraction. The effect of glycerol on Ni-Mo hardness was evaluated by Vickers microhardness measurements. The presence of glycerol in the electrodeposition bath increased the grain size and decreased the hardness of the coating. However, it promoted the formation of a more compact and less porous coating, increasing the corrosion resistance of the coating. Moreover, the addition of 0.82 mol.L-1 glycerol increases current efficiency, thereby reducing the amount of energy consumed during electroplating.

Abstract This work investigates the effect of the addition of glycerol on the microstructure, corrosion resistance, and efficiency of the electrodeposition process of Cu coating in an acid sulphate solution. The morphology and microstructures of electrodeposits were analyzed using Scanning Electron Microscopy (SEM), Spectrometry X-Ray Diffraction (XRD) and laser scanning confocal microscopy (LSCM). Evaluation of the corrosion resistance was performed in 2.0 mol⋅L−1 NaCl by means of weight loss tests and electrochemical techniques. The addition of glycerol resulted in a decrease in grain and crystallite sizes, a decrease in roughness and an increase in the tensile strain of the coating. The deposition efficiency and the corrosion resistance increased with the addition of glycerol exhibiting a maximum value at the concentration of 0.42 mol⋅L−1, increasing the efficiency of electrodeposition by approximately 96%. This is related to the roughness of the coating, which is minimal at this concentration.

Abstract The use of natural additives in biodiesel has been investigated, however, there is limited information in the literature in relation to their influence on corrosion resistance and oxidative stability. This work aims to investigate the oxidative stability of biodiesel and the corrosion resistance of carbon steel (AISI 1020) in contact with soybean biodiesel solutions (B100) in the presence and absence of natural additives such as: rosmarinic acid, curcumin, gingerol, eugenol, thymol and quercetin. Corrosion and microscopy tests were used to assess corrosion resistance. The Rancimat technique was used to study oxidative stability. The results obtained indicate that curcumin was the best additive in relation to oxidative stability, while rosmarinic acid showed better performance in inhibiting corrosion. The effect of these substances is related to the presence of phenolic compounds or the existence of oxygen in its molecular structure.

Abstract The Zn coatings obtained through electrodeposition are used to protect steel substrates from corrosion. In general, organic additives are added to the deposition bath in order to improve deposition characteristics such as corrosion resistance, hardness and deposition efficiency. Despite of the literature present information about the various organic additives effects on Zn coating properties there is no analysis of organic compounds with free electron-containing radicals, such as formic acid and cyclohexylamine. The formic acid has oxygen atoms with free electrons, whereas cyclohexylamine contains nitrogen with free electrons. Aiming at overcoming this gap, this manuscript presents an analysis of the effect in addition of formic acid mixture and cyclohexylamine on the deposition flow efficiency, corrosion resistance, hardness, roughness and micro-structure of Zn coating on carbon steel AISI 1020. The corrosion resistance evaluation was performed by potentiodynamic polarization determined by polarization resistance and weight loss tests as well. The analisys of morphology and electrodeposited microstructures were made by the Scanning Electron Microscopy (SEM) and Spectrometry X-Ray Diffraction (XRD). The Zn coatings were obtained from chloride deposition baths at constant pH 5. Results showed that corrosion resistance in the 0.5 mol/L NaCl solution of Zn coatings increases with the addition of the mixture of the formic acid and / or cyclohexylamine. Also, the corrosion resistance is higher with mixture than with additives alone. The addition of the mixture formic acid and cyclohexylamine increases the basal plane presence (0 0 2). However, the basal plane presence (0 0 2) does not increase when formic acid and cyclohexylamine are added alone which indicates a synergic effect of formic acid and cyclohexylamine in in the plan promotion (0 0 2). Also, was observed that an addition of formic acid mixture and cyclohexylamine increases the current deposition efficiency, decreases the roughness and raises the Zn coating hardness.

Zinc electrodeposition is an economical process of Zn coating compared to conventional galvanic process. The galvanizing process is used in various industrial sectors to protect ferrous alloys during the corrosion process. In buildings, the galvanizing process is widely used to coat mortar protective screens. The electrodeposition of zinc has a relatively low cost compared to other coating materials for the same purpose; however, its corrosion resistance is lower than that of most protective deposits. This study evaluated the effect of adding glycerol to the electrodeposition bath on the corrosion resistance, deposition efficiency, morphology and microstructure of the zinc electrodeposit in concentrations ranging from 0.03 to 0.82 M. The electrodeposition was performed on carbon steel AISI 1020 with a current density of 10 mA.cm-2. The electroplating solution composition was 0.10 M ZnCl2, 2.80 M KCl and 0.32 M H3BO3. Electrodeposition time was 17.56 min, 5 µm thick coating, equivalent to the mass of 7.166E-3 g of zinc on the steel surface. Evaluation of the corrosion resistance was performed by means of the electrochemical tests of Anodic Voltammetry, Potentiodynamic Polarization and Electrochemical Impedance Spectroscopy (EIS) as well as Weight Loss tests in NaCl 0.5 M in 4 (four) different period of immersion. The morphology and microstructures of electrodeposited were analyzed using the techniques of Scanning Electron Microscopy (SEM) and Spectrometry X-Ray Diffraction (XRD). The presence of glycerol in the electrodeposition bath decreased the deposition efficiency; however, it increased corrosion resistance and promoted the formation of more compact and refined electrodeposited coatings. Moreover, the results showed that the corrosion rate does not vary linearly with the addition of glycerol.

Reinforced concrete is the main structural material used in the world in the construction of bridges, roads and commercial and residential buildings. One effective method for preventing corrosion of steel reinforcement is the application of galvanic coatings to the reinforcement itself. The present study evaluated the performance of three groups of reinforcing steel bars (black steel, used as a reference and rebars electroplated with Zinc and Zinc-Nickel alloys) to corrosion and adherence to the concrete matrix. For the analysis of corrosion, the specimens were subjected to two different accelerated corrosion tests: salt spray exposure and wet and dry semi-cycles. The corrosion potential was measured for the qualitative monitoring of the corrosion process and the corrosion rate was estimated. In order to evaluate the steel-concrete adherence, the pullout test was used, in accordance with RILEM-CEB-FIP. The results showed that Zinc and Zinc-Nickel coatings increased the durability of the reinforcing bars and the accelerated corrosion test of wetting and drying cycles proved to be more aggressive compared to the salt spray method to evaluate the corrosion process in the reinforced concrete specimens. Additionally, galvanized reinforcement reduced adherence to the concrete matrix.

Based on the Fe60Cr8Nb8B24 alloy, reported in the literature as good Glass Forming Ability (GFA), in this study the GFA of two new compositions was proposed, Fe68-xCrxNb8B24 (x=10,12). They were evaluated as good candidates to be new compositions of Bulk Metallic Glasses (BMG) with better corrosion resistance due to the high Cr content. Rapidly solidified glassy ribbons were processed, and based on their thermal characteristics, the critical thickness of the glassy structure formation (Zc) was estimated. The critical thickness (Zc) obtained experimentally using the wedge-shaped casting method was evaluated and it presented a much lower value than that estimated theoretically. However, the GFA of the compositions analyzed was ranked and this ranking (i.e. whichever has the most or least GFA) is in agreement with the result predicted theoretically. The GFA of Fe58Cr10Nb8B24, which presented a maximum thickness of the amorphous region of wedge-shaped samples of about 0.6 mm (but estimated it would be 3.56 mm), offered good prospects to be a new Fe-based glass former alloy which has better resistance to corrosion than the Fe60Cr8Nb8B24 alloy reported.

In the present work the effect of substituting Mo with Nb on the glass forming ability and corrosion resistance of Fe-Co-Cr-M-Si-B-Y (M=Mo, Nb) ribbons with high corrosion resistance is investigated. The X-ray powder diffraction pattern indicates that the alloy containing both Nb and Mo presented greater glass forming ability than the alloy containing either of these elements separately. The results obtained indicate that Mo is more effective in enhancing corrosion resistance than the Nb in 4.0 M HCl solution. The alloy containing both Nb and Mo presented greater overall corrosion resistance than the alloy containing only one of these elements.

The corrosion properties of a 22.5 wt. (%) Cr duplex stainless steel were investigated after long-term aging of 3000, 5000 and 7000 hours at 300 and 400 ºC. The corrosion resistance was measured based on mass loss in a FeCl3 10 wt. (%) solution and electrochemical measurements in a 0.1 M H2SO4 solution. The results indicate that the corrosion resistance decreased steadily up to 5000 hours of aging. However, the samples subjected to 7000 hours of aging showed better corrosion resistance than those aged for 3000 and 5000 hours. This effect is attributed to the phase transformation that occurs during aging, a finding which was confirmed by hardness, transmission electron microscopy and X-ray photoelectron spectroscopy measurements.

Electric-arc furnace dust (EAFD) is a by-product of steel production and recycling. This fine-grained material contains high amounts of zinc and iron as well as significant amounts of potentially toxic elements such as lead, cadmium and chromium. Therefore, the treatment and stabilization of this industrial residue is necessary. Concrete is a well-known suitable environment for stabilization/solidification of materials which have leachable elements in need of fixation. The effect of the EAFD content on the mechanical and chemical performance of Portland cement concrete is investigated in this paper. The effect of the EAFD content on the setting time of cement slurry was also analyzed. The axial compressive strength of the concrete samples increases with the EAFD addition in the range of 10 to 20 wt. (%) EAFD; also the tensile strength increases with the EAFD addition. An increase in EAFD content significantly increases the setting time of the concrete. The acetic acid leaching and water solubilization tests indicate low mobility of the potentially toxic elements from the EAFD concrete composite. The results of the immersion tests show that the addition of EAFD to the concrete seems to reduce chloride penetration, which may help prevent pitting corrosion in reinforced concrete.