The use of niobium containing materials' has gained much attention of the scientific community in the late years due its various applications in diverse fields. NbC is a highly versatile material. Copper addition may alter several of its properties, such as morphology, crystal structure etc. as well as enhance its catalytic behavior. Nanostructured NbC with copper addition synthesis' presented here had the precursor [(NH4)3[NbO(C2O4)3]xH2O] as starting material, which was doped with Cu(NO3)2 at 5% and 10% (molar) ratios. Doped NbC was obtained via gas solid reaction in fixed bed reactor at lower temperature (980°C) and with shorter reaction time (2h) than traditional methods. Reaction products' were characterized by XRD, crystal sizes were estimated according to HWL method, and SEM, XRF, BET and laser particle size analysis were performed. XRD indicated the formation of NbC and Cu phases with cubic crystal structure of ~20nm. SEM showed slight morphological change upon increasing copper content, indicating a less porous structure, which is consistent with BET data (43.7m2/g for 5%Cu-NbC and 37m 2/g for the 10% Cu-NbC). Crystal size calculations showed that increasing dopant content particle sizes were also increased, probably due to the presence of the dopant, in some extent, in the crystal structure.

The objective of this work is obtaining W-30 wt% Cu composite powder from ammonium paratungstate hydrated (APT) and hydrated copper nitrate and investigating the influence of some production process parameters of W- 30 wt% Cu in particles form which results in high sinterability and densification of W-30 wt% Cu composite. To achieve this objective, the powder was obtained by manually mixing the APT and copper nitrate and reducing under a hydrogen atmosphere at 800 °C and then compacting at 500 MPa and sintering in a tubular furnace at 1200 °C for 60 minutes. The obtained materials were characterized by XRD, SEM, EDS, particle size analysis, density and microhardness measurements. The composite powder showed a good homogenization of Cu in W with very fine and agglomerated particles and a mean crystallite size of 25.64 nm. SEM coupled with EDS with mapping analysis revealed a homogeneous distribution of Cu and W in the sintered sample. The composite had a relative density of 96.77% and a microhardness of 523.66 HV. Therefore the method of obtaining the composite powder is feasible to sinter W-30 wt% Cu powder due to a greater dispersion and homogenization of phases and the average particle size.

The present paper's objective was to synthesize and characterize both the oxalic niobium precursor (NH4)3NbO(C2O4)3.H2O, and the product of its doping with Cu and calcining, CuNb2O6. In order to obtain the niobium precursor, commercially available niobium oxide (Nb2O5) was subject to fusion with potassium bisulfate (KHSO4). Once leached with water, the powder was complexed with oxalic acid and ammonium oxalate. The as produced material was manually mixed with copper nitrate Cu(NO3)2.2H2O (25% Cu molar) and calcined at 1000°C in a muffle furnace. CuNb2O6 was then obtained. The precursor was characterized by XRD, SEM, FT-IR, XRF, TG/DTG. The calcination product was characterized by XRD, XRF and SEM. Results show that single phase CuNb2O6 could be obtained by this method without Nb2O5 contamination.