Mechanical spectroscopy measurements have been extensively used in the last decades to obtain information about many aspects of the behavior of solutes in metallic materials. Metals of body-centered cubic lattice that contain heavy interstitial elements (oxygen, nitrogen and carbon) in solid solution, present anelastic relaxation peaks when submitted to cyclic tensions, due to process know stress-induced ordering. Internal friction and frequency as a function of temperature were performed between 300 K and 650 K in a polycrystalline sample of Nb, for three distinct conditions, using a torsion pendulum inverted Kê-type operating in a frequency oscillation between 1Hz and 10 Hz range, with a heating rate of 1 K/min and pressure lower than 2 x 10-5 mbar. The experimental spectra obtained for each condition of the sample, were decomposed by the successive subtraction method in elementary Debye peaks. The following metal-interstitial interactions were identified: Nb-O and Nb-N for all conditions of the sample. From the anelastic relaxation parameters obtained (relaxation strength, peak temperature, activation energy and relaxation time) and lattice parameter (obtained from x ray diffraction), the determination of the oxygen and nitrogen interstitial diffusion coefficient in Nb was possible, for each condition of the sample.

Measurements of internal friction as a function of temperature were performed in samples of Nb containing different amounts of substitutional (Zr) and interstitial (O, N) solutes. These data were resolved using the method of successive subtraction, into a series of constituent Debye peaks corresponding to different interactions. For each relaxation process we obtained the height (Q-1max) and temperature (Tp) of the peak, the activation energy (E) and the relaxation time (t0). The height, shape and temperature of the peaks depend on the concentration of interstitial and substitutional elements. With the addition of substitutional solute one can observed interactions between the two types of solutes (substitutional and interstitial), showing that the random distribution of the interstitial atoms was affected by presence of substitutional atoms. The peaks observed were associated with matrix-interstitial (Nb-O, Nb-N) and substitutional-interstitial (Zr-O) interaction processes.