Abstract Polyphenols interact with salivary proteins and thus can improve the pellicle’s erosion protective properties. This effect could be exploited to create rinsing solutions with polyphenols as active ingredients for erosion prevention. Different from the current gold standard for erosion protective rinsing solutions, these rinses would not rely on stannous ions. This would offer alternatives for patients with concerns regarding the composition of rinsing solutions and preferring bio-products. Objective To develop an erosion-preventive rinsing solution containing natural polyphenol-rich extracts. Methodology Solutions were prepared with polyphenols from either grapeseed extract or cranberry extract, 500 ppm fluoride added, and additionally flavors and sweeteners. Controls were deionized water, 500 ppm fluoride solution, and the gold standard rinse in the field (Sn2+/F-). In total, 135 enamel specimens (n=15/group) were subjected to five cycles of salivary pellicle formation (30 min, 37°C), modification with the solutions (2 min, 25°C), further salivary pellicle formation (60 min, 37°C), and erosive challenge (1 min, 1% citric acid, pH 3.6). Relative surface microhardness (rSMH), surface reflection intensity (rSRI), and amount of calcium release (CaR) were investigated. Data were analyzed with Kruskal-Wallis and Wilcoxon rank sum tests (α=0.05). Results The polyphenol solutions containing fluoride, as well as additional flavors, protected enamel better than fluoride alone, and similar to the Sn2+/F- solution, when investigating both rSMH and CaR. When measuring rSRI, Sn2+/F- showed the best protection, while the polyphenol solutions were similar to fluoride. Conclusion For two of the three assessed parameters (rSMH and CaR), both developed polyphenol-rich rinsing solutions were able to protect enamel from erosion, improving/potentializing the effect of fluoride and matching the protection offered by the current gold standard rinsing solution.

Resumo Este estudo desenvolveu e testou géis experimentais contendo íons fluoreto (F-) e estanho (Sn2+) para o controle da erosão dentária. Os espécimes polidos, de esmalte e dentina, foram previamente erodidos (solução de ácido cítrico a 1%, 10 min) e alocados aleatoriamente em 5 grupos (n = 10): Placebo - gel de hidroxipropilmetilcelulose (HMC); F + Sn + HMC - 7.500 ppm F- / 15.000 ppm Sn2+; F + HMC - 7.500 ppm F-; Gel de flúor fosfato acidulado comercial (12.300 ppm F-); e Controle - sem tratamento. Após o tratamento (aplicado por 60 s), os espécimes foram submetidos a uma ciclagem de erosão-remineralização (5 min em solução de ácido cítrico a 0,3%, 60 min em saliva artificial, 4 × / dia, 20 dias). A perda de superfície (SL, em µm) foi determinada após o 5º, 10º e 20º dias de ciclagem (α = 0,05). Para o esmalte, após 5 e 10 dias, o F + Sn + HMC apresentou a menor PS, não diferindo do gel comercial. Após 20 dias, não foram encontradas diferenças entre os grupos comercial, F + HMC e F + Sn + HMC. O placebo não diferiu do controle em nenhum momento, e ambos os grupos apresentaram a maior PS, comparado aos demais grupos. Para dentina, no 5º dia , F + Sn + HMC, F + HMC e comercial não diferiram significativamente, apresentando menor PS que o grupo controle e placebo. No 10º dia, F+Sn+HMC e comercial apresentaram a menor PS comparado ao grupo controle e placebo. No 20º dia, apenas o gel comercial apresentou PS menor que o controle e o placebo. Assim, o gel experimental F + Sn + HMC foi capaz de controlar a progressão da erosão dentária.

Abstract: This study synthesized and tested experimental gels containing fluoride (F-) and stannous (Sn2+) ions for the control of dental erosion. Enamel and dentin polished specimens were eroded (1% citric acid solution, 10 min) and randomly allocated into 5 groups (n=10): Placebo - Hydroxypropyl Methylcellulose (HMC) gel; F+Sn+HMC - 7,500 ppm F- / 15,000 ppm Sn2+; F+HMC - 7,500 ppm F-; Commercial acidulated phosphate fluoride gel (12,300 ppm F-); and Control - no treatment. After treatment (applied for 60 s), specimens underwent an erosion-remineralization cycling (5 min in 0.3% citric acid solution, 60 min in artificial saliva, 4×/day, 20 days). Surface loss (SL, in µm) was determined after the 5th, 10th and 20th days of cycling (α=0.05). For enamel, after 5 and 10 days, F+Sn+HMC presented the lowest SL, which did not differ from the commercial gel. After 20 days, no differences were found between commercial, F+HMC, and F+Sn+HMC groups. Placebo did not differ from the control at any time points, and both groups presented the highest SL when compared to the other groups. For dentin, on the 5th day, F+Sn+HMC, F+HMC and commercial did not differ significantly, showing lower SL than the control and the placebo. On the 10th day, F+Sn+HMC and commercial presented the lowest SL compared to control and placebo. After 20 days, only the commercial gel showed lower SL than the control and placebo. Thus, the experimental F+Sn+HMC gel was able to control the progression of tooth erosion.

Abstract Objective The aim of this study is to test, in vitro, the anti-cariogenic effect of experimental hybrid coatings, with nano clays of halloysite or bentonite, loaded with sodium fluoride or with a combination of sodium fluoride and stannous chloride, respectively. Methodology The varnish Fluor Protector (1,000 ppm of F-) was used as positive control and no treatment was the negative control. Enamel specimens (5 mm × 5 mm) were obtained from bovine teeth. The specimens (n=10) had their surfaces divided into two halves (5 mm × 2.5 mm each), in which one half received one of the treatments (Hybrid; Hybrid + NaF; Hybrid + NaF + SnCl2; Hybrid + NaF Loaded; Hybrid + NaF + SnCl2 Loaded). The specimens were submitted to a cariogenic challenge using a biofilm model (S. mutans UA159, for 5 days). Enamel surfaces both under and adjacent to the treated area were analyzed for mineral loss and lesion depth, by transverse microradiography. The pH of the medium was measured twice a day, and the fluoride release was analyzed. Additional specimens were submitted to confocal analysis. Results Data were statistically analyzed by two-way ANOVA followed by Tukey test (α=0.05). None of hybrid groups were able to reduce the lesion depth; the Hybrid + NaF group, however, was able to reduce mineral loss differing from the negative control (p=0.008). The groups showed no significant difference in the pH measurement and fluoride release. Confocal analysis confirmed that for all groups the biofilm growth was similar. Conclusion None of the hybrid groups reduced lesion depth, but the Hybrid + NaF group was able to promote protection against mineral loss.

Abstract Objective To evaluate the efficacy of Nd:YAG laser associated with calcium-phosphate desensitizing pastes on dentin permeability and tubule occlusion after erosive/abrasive challenges. Methodology Dentin specimens were exposed to 17% ethylene diamine tetra-acetic acid (EDTA) solution for 5 min and randomly allocated into five groups: G1, control (no treatment); G2, Nd:YAG laser (1 W, 10 Hz, 100 mJ, 85 J/cm2); G3, Laser + TeethmateTM Desensitizer; G4, Laser + Desensibilize Nano P; and G5, Laser+Nupro®. Specimens underwent a 5-day erosion-abrasion cycling. Hydraulic conductance was measured post-EDTA, post-treatment, and post-cycling. Post-treatment and post-cycling permeability (%Lp) was calculated based on post-EDTA measurements, considered 100%. Open dentin tubules (ODT) were calculated at the abovementioned experimental moments using scanning electron microscopy and ImageJ software (n=10). Data were analyzed using two-way repeated measures ANOVA and Tukey’s test (α=0.05). Results G1 presented the highest %Lp post-treatment of all groups (p<0.05), without significantly differences among them. At post-cycling, %Lp significantly decreased in G1, showed no significant differences from post-treatment in G3 and G4, and increased in G2 and G5, without significant differences from G1 (p>0.05). We found no significant differences in ODT among groups (p>0.05) post-EDTA. At post-treatment, treated groups did not differ from each other, but presented lower ODT than G1 (p<0.001). As for post-cycling, we verified no differences among groups (p>0.05), although ODT was significantly lower for all groups when compared to post-EDTA values (p<0.001). Conclusion All treatments effectively reduced dentin permeability and promoted tubule occlusion after application. Combining Nd YAG laser with calcium-phosphate pastes did not improve the laser effect. After erosive-abrasive challenges, treatments presented no differences when compared to the control.

Composite resins might be susceptible to degradation and staining when in contact with some foods and drinks. This study evaluated color alteration and changes in microhardness of a microhybrid composite after immersion in different colored foods and determined whether there was a correlation between these two variables. Eighty composite disks were randomly divided into 8 experimental groups (n = 10): kept dry; deionized water; orange juice; passion fruit juice; grape juice; ketchup; mustard and soy sauce. The disks were individually immersed in their respective test substance at 37 ºC, for a period of 28 days. Superficial analysis of the disk specimens was performed by taking microhardness measurements (Vickers, 50 g load for 45 seconds) and color alterations were determined with a spectrophotometer (CINTRA 10- using a CIEL*a*b* system, 400-700 nm wavelength, illuminant d65 and standard observer of 2º) at the following times: baseline (before immersion), 1, 7, 14, 21 and 28 days. Results were analyzed by ANOVA and Tukey's test (p < 0.05). Both variables were also submitted to Pearson's correlation test (p < 0.05). The passion fruit group underwent the greatest microhardness change, while the mustard group suffered the greatest color alteration. Significant positive correlation was found between the two variables for the groups deionized water, grape juice, soy sauce and ketchup. Not all color alteration could be associated with surface degradation.