Abstract In this paper, the crystallization, fusion, and activation energy (Ea) of PBT/TiO2 were thoroughly evaluated using DSC. Increasing the rates shifted the peaks of melt crystallization to lower temperatures while the fusions were almost unaffected. TiO2 hindered the melt crystallization of PBT and lower crystallization rates, i.e., CMAX and K’ were acquired, in general, the crystallinity degree (Xc) was 4% higher in PBT/TiO2 which is in the marginal error. Pseudo-Avrami and Mo models were applied to evaluate the melt crystallization kinetics; both fitted the melt crystallization quite well; deviations were observed at the beginning and the crystallization end most due to the nucleation and spherulites impingement during the secondary crystallization. Ea was evaluated using the Friedman model, considering the values of Ea less energy has to be removed from PBT/TiO2 when compared to PBT, specifically at 1% of TiO2.

Abstract Compounds of poly(3-hydroxybutyrate) (PHB) and titanium dioxide (TiO2) with filler content between 1% and 10% were prepared in a laboratory internal mixer. The effect of heating and cooling rates on the crystallization and melting of PHB/TiO2 compounds was investigated by differential scanning calorimetry (DSC). Melt and cold crystallization rates rise with increasing cooling/heating rates. A higher cooling rate translates to a lower melt crystallization temperature, while a higher heating rate results in a higher cold crystallization temperature. TiO2 promotes melt crystallization of PHB, behaving as a nucleant agent. The total crystallinity developed after melt and cold crystallization decreases for low levels of TiO2, i.e. 2% per weight, and is almost independent of the heating/cooling rate. The melting temperatures and rates are minimally affected by both the heating rate and filler content. The results suggest that the desired PHB microstructure can be controlled by filler content and adjusted heating/cooling rate.

The effect of alcaline and hot water surface treatments of piassava Attalea funifera fibers was investigated. The efficiency of each treatment was evaluated by Fourier transform infrared spectroscopy, X-ray diffractometry, optical microscopy, scanning electron microscopy and atomic force microscopy. The alkaline treatments were effective in removing the superficial lignin layer from the fiber, while the hot water treatment was not. Treatment with hot water and NaOH caused fiber defibrillation. NaOH was most effective in promoting both, a decrease in fiber diameter and an increase in fiber surface area. Treatment with Ca(OH)2 led to the formation of a CaCO3 layer deposited on the fiber, preventing defibrillation. The crystalline structure of the fiber was not altered by any of the treatments, maintaining type I cellulose.

ABSTRACT Films of Poly(?-caprolactone) (PCL) and PCL/Zinc Oxide (ZnO) were obtained by solution processing. Thermal behaviour and morphological structure were analysed by means of Thermogravimetry (TGA), Differential Scanning Calorimetry (DSC), Optical Microscopy (OM) and Scanning Electron Microscopy (SEM). The addition of ZnO to PCL decreased the degradation temperature about 50-70°C; the films are thermally stable up to 200°C, making them suitable for packaging hot grilled chicken. ZnO did not promote significant alterations of the PCL fusion and melt crystallization, however the crystallinity increased; probably ZnO acts as nucleating agent during PCL crystallization as OM images showed greater amount of small spherulites on PCL/ZnO films. According to SEM, the methodology utilized is adequate for producing films in concentrations up to 5% ZnO.