The present study reports the deposition of coating using Plasma Electrolytic Oxidation (PEO) onto grade 4 titanium to produce novel surface features. Samples were treated in an electrolytic solution of calcium acetate and sodium glycerolphosphate. The temporal evolution of hydroxyapatite coatings with high Ra roughness and a maximum thickness of 120 µm was obtained. X-ray spectra revealed the presence of hydroxyapatite, rutile and calcium phosphate. Cell growth measurement by MTT assay showed that the coatings were not toxic because cells grew on all samples.

Surface modification techniques based on the grafting of chemical functional groups and immobilization of bioactive molecules have been used to improve biocompatibility and clinical performance of bioabsorbable scaffolds in tissue engineering and medicine regenerative applications. This study aimed at developing and characterizing a biomimetic surface to stimulate bone regeneration by a simple and low-cost method of surface biofunctionalization of the poly (L-co-D,L lactic acid)-PLDLA scaffolds. The method was obtained by grafting reaction of carboxyl groups (-COOH) on their surface via acrylic acid (AAc) polymerization process, followed by immobilization of collagen type I (Col). Such approach resulted in a surface morphology markedly modified after treatment, with increase of pores and roughness on PLDLA-AAc surfaces and a network of fibrillar collagen deposition in non-specific areas of PLDLA-Col surfaces. The cytocompatibility of collagen-immobilized scaffolds was significantly improved in terms of cellular adhesion, proliferation, collagen synthesis and maintenance of osteoblast-like phenotype, indicating, therefore, the fundamental role of collagen protein over the biological interactions that occur by bio-recognition mimetic mechanisms at biomaterials interface. These results indicate that the surface modification method used here may be useful as a strategy to develop biofunctional scaffolds, which provide a more successful clinical application of biomaterials in the tissue engineering field.

AA 2024 aluminum alloy is widely employed in aeronautic and automobilist industries. Its hardness and low density are attractive properties for such industrial areas. However, since it contains copper, it undergoes severe corrosion in aggressive media as saline or low Earth orbit environments. In this work, it was investigated the properties of films deposited by PECVD on AA 2024 aluminum alloy as well as the corrosion resistance of the film/substrate systems under different corrosive atmospheres. Films were prepared in a plasma atmosphere composed of 50% of oxygen and 50% of hexamethyldisiloxane resulting in a total gas pressure of 4.0 Pa. Plasma ignition was promoted by the application of radiofrequency signal (13.56 MHz) to the sample holder while grounding the topmost electrode. The plasma excitation power, P, was changed from 10 to 80 W in the six different set of experiments. Film thickness, measured by profilometer, increases by 5 times as P was elevated from 10 to 80 W. As demonstrated by the infrared spectra of the samples, films are essentially organosilicons with preservation of functional groups of the precursor molecule and with creation of different ones. The oxide proportion and the structure crosslinking degree are affected by the plasma excitation power. According to the results obtained by sessile drop technique, hydrophilic to moderately hydrophobic films are produced with changing P from 10 to 80 W. The corrosion resistance, evaluated by salt spray and electrochemical impedance spectroscopy, EIS, experiments, in general increases after film deposition. It is demonstrated that film deposition improves, in up to 36 times, the resistance of the alloy to salt spray attack. It is also shown an improvement of about 240 times in the alloy resistance under NaCl solution by the EIS data. Micrographs acquired by Scanning Electron Microscopy after the corrosion tests furnish further information on the importance of the layer physical stability on its barrier properties. Furthermore, films highly protect the alloy against the oxygen attack. Interpretations are proposed based on the modification of the plasma kinetics with P, altering film structure, composition and properties.

In this work, thin polymer films were prepared from acetylene and argon radiofrequency (13.56 MHz, 80 W) glow discharges. Post-deposition treatment was performed by plasma immersion ion implantation in nitrogen or helium glow discharges (13.56 MHz, 70 W). In these cases, samples were biased with 25 kV negative pulses. Exposure time to the bombardment plasma, t, ranged from 900 to 7200 s. Chemical composition of the film surfaces was investigated by X-ray Photoelectron Spectroscopy and the resistance to oxidation by the etching process, in reactive oxygen plasmas. Oxygen and nitrogen were detected in all the samples. While the concentration of the former continuously changed with t, that of N kept practically constant in small proportions. The film is predominantly formed by sp² states, but the proportion of sp³ hybridization slightly increased with t. The etching rate dropped under certain conditions of nitrogen bombardment whereas helium implantation has not significantly improved it. These results are ascribed to the crosslinking degree of the polymeric chains, ruled by the total amount of energy delivered to the film.