ABSTRACT Chemical and physical methods have been generally used for modifying the surface of titanium implants with the aim of achieving better osseointegration. In this work, an evaluation of the effect of different chemicals and thermochemical treatments on the surface modification of titanium was carried out. Plates of commercially pure titanium were polished and treated with four different methods. Scanning electron microscopy, atomic force microscopy, energy-dispersive X-ray spectroscopy, infrared spectroscopy, X-ray diffraction and drop shape analysis were used to characterize the modified titanium surface. Our results showed that the AEPTTT surface exhibited the highest Ra values followed by AEAT, AEPT, polished Ti and AE samples. In addition, the AEAT and AEPTTT treatments developed the largest surface area, while the AE treatment produced the lowest surface area. Furthermore, the AEAT treatment created the most hydrophilic surface, which is known to positively affect the osseointegration rate of dental implants.

The biomimetic method is used for the deposition of calcium phosphate coatings (Ca - P) on the surface of different biomaterials. However, the application of this method requires long exposure times in order to obtain a suitable layer thickness for its use in medical devices. In this paper, we present a fast approach to obtain apatite coatings on titanium, using a combination of supersaturated calcification solution (SCS) with chemical modification of the titanium surface. Also, it was evaluated the effect of four different surface treatments on the apatite deposition rate. Commercially pure titanium plates were activated by chemical or thermochemical treatments. Then, the activated samples were immersed in a solution with high content of calcium and phosphate ions at 37 ºC for 24 h, mimicking the physiological conditions. The coatings were studied by Fourier transform infrared spectroscopy (FTIR), X-ray diffraction (XRD), scanning electron microscopy (SEM) and energy dispersive X-ray spectroscopy (EDX). The use of SCS solutions allowed the formation of crystalline hydroxyapatite coatings within a period of 24 h with a thickness between 1 and 5.3 µm. Besides, precipitates of hydroxyapatite nanoparticles with a globular configuration, forming aggregates with submicrometer size, were found in SCS solutions.