Pt-Y/C catalysts were prepared by a modified formic acid method and their structural characteristics and activity for oxygen reduction reaction (ORR) were evaluated. X-ray diffraction analysis showed that no alloy was formed between the metals and X-ray photoelectron spectroscopy (XPS) experiments showed that yttrium is presented as Y2O3, Y(OH)3 and Y-O-Pt species. CO stripping voltammetry and in situ X-ray absorption spectroscopy confirmed the interaction between Pt nanoparticles and yttrium species. The Pt-Y/C 7:3 material showed the higher specific activity (103 µA cmPt2) for ORR. Following repetitive potential cycling, the activity for the ORR of the Pt-Y/C 7:3 catalyst declined in a similar proportion to the Pt/C material. Transmission electron microscopy analysis after stability for both catalysts showed that Pt/C particle size slightly increased and that for Pt-Y/C 7:3 remained the same. XPS made in ultrathin catalyst layer, agreeing with energy-dispersive X-ray spectroscopy analysis, revealed that the intensities of the Y 3d peaks were suppressed relative to the initial one and that yttrium in the form of Y2O3 and Y(OH)3 were dissolved, while the species Y–O–Pt still remain in the catalyst, maintaining the higher activity.

A oxidação eletroquímica do metanol foi estudada sobre ligas de Pt:Mo dispersa em carbono, preparadas utilizando um método recentemente desenvolvido neste laboratório. Análises de EDX confirmaram que a redução simultânea dos sais precursores de Pt e Mo conduzem a presença destes metais nas composições nominais inicialmente calculadas. A adição de Mo sobre Pt causa um aumento da corrente de oxidação, mas não produz um efeito catalítico para oxidação do metanol. A partir dos dados de polarização em várias concentrações de metanol foram obtidos diagramas de Tafel que apresentaram duas inclinações. A técnica de espectroscopia de massa diferencial aplicada "on line" a um experimento voltamétrico foi utilizada para investigar a distribuição de produtos e intermediários formados na oxidação de metanol.

The electrocatalytic oxidation of methanol on Pt:Mo dispersed on carbon prepared using an alternative method recently developed in this laboratory was investigated. The EDX analysis confirmed that the simultaneous reduction of the precursor salts of Pt and Mo leads to the presence of these materials at the nominal composition initially calculated. The addition of Mo to Pt causes an increase of the oxidation currents, but does not improve the catalytic effect for methanol oxidation. Tafel plots for various methanol concentrations showed the presence of two slopes. On line differential electrochemical mass spectrometry (DEMS) was used to investigate the distribution of products and intermediates in methanol oxidation.

This paper describes in detail a technique employed to grow quasi-spherical single crystals of noble metals for electrochemical applications, using platinum as an example. The metal beads were formed by melting the extremity of a wire in an oxygen / butane flame. X-ray techniques were used to check the crystallization and to determine the orientation of the crystals. Treatment with a pure hydrogen flame followed by a cooling procedure in a hydrogen / argon atmosphere were used for conditioning the well-defined platinum single crystal surfaces. Finally, electrochemical characterization of the Pt(111), Pt(110) and Pt(100) surfaces was done in diluted sulfuric acid solution in the hydrogen adsorption / desorption potential region.

Studies of the kinetics of electrocatalytic reactions on well oriented single crystal surfaces have demonstrated the influence of surface structure on the rate and mechanisms of many electrochemical processes. The preparation and characterization of these surfaces is the first step in this type of studies. In this paper, a methodology employed in order to ensure the quality and cleanliness of single crystals and their utilization as rotating electrodes is described.