Multicomponent ( Al2O3, CaO, SiO2, MgO) calcium aluminate-based glasses containing Nd3+ were prepared in order to evaluate their possibilities as laser host materials. The refractive index, UV-visible-near IR absorption spectrum, IR and visible luminescence spectra, and fluorescence decay time were measured. Judd-Ofelt model was used to obtain experimental intensity parameters ( omega2, omega4 and omega6), emission cross-section, radiative lifetimes, emission branching ratios and quantum efficiency.

Domestic microwave oven was modified for laboratory applications. Electronic system was made for controlling magnetron irradiation time. Exhaustion and air circulation systems were installed to clean the internal oven atmosphere during operation. The cavity walls were coated with aluminized thermal paint to avoid chemical corrosion. These modifications allowed the usage of the oven for drying and processes using reflux.