Thin solid films of Nb2O5 and Nb2O5:Li+ were prepared by the sol-gel process using the sonocatalytic method. The films reported here were prepared from a NbCl5 as precursor and butanol as solvent. Through the addition of lithium salt LiCF3SO3 to the precursor solution, films with different electrochemical performance were obtained. The electrochemical and optical responses of the films were determined from the cyclic voltammetry and chronoamperometry measurements using a 0.1 M LiClO4/PC as electrolyte. The electrochromic properties of the films were investigated using in situ spectroelectrochemical method. They exhibit a gray coloration under Li+ insertion with a reversible variation of the transmittance in the visible and near infrared range between 20% and 80%.

Amylopectin-rich starch samples (Amidex 4001 Corn Products Brasil Ingredientes Industriais Ltda.) were grafted with polyethers with the purpose of obtaining new materials for application as solid polymeric electrolytes. Grafting reaction was performed by the addition of starch dissolved in DMSO to toluene poly(propylene oxide) diisocyanate (Resibras) dissolved in the same solvent. This reaction produced a film with good mechanical properties. The film samples were characterized by 13C-NMR, FTIR, DSC, X-Ray and SEM. The FTIR spectrum shows a sharp NH band and a very small urethane band. The 13C-NMR spectrum revealed a peak at 20 ppm, that can be attributed to the CH3 of the polyether chain, and two small peaks at 117 and 140 ppm, attributed to the aromatic ring. The X-ray diffractograms also indicated that after the grafting reaction, the samples of amylopectin-rich starch are more amorphous. Moreover, the glass transition temperature (Tg) dropped from 50 °C to -11 °C. These results indicate formation of grafted products and the low Tg of the samples suggests that polyether-grafted starch is a good candidate to obtain solid polymeric electrolytes.

The sols for thin electrochromic coatings of Nb2O5 were obtained by synthesis of the niobium butoxide from BuONa and NbCl5. The ~300nm thick films were deposited by dip-coating technique from the alkoxide solution and calcined at 560ºC in O2 atmosphere during 3 hours. The particles size of niobium oxide (V) powder (~20mm) was obtained from x-ray diffraction using the Scherrer equation. The coatings were characterized by cyclic voltammetry and cronoamperommetry techniques. The spectral variation of the optical transmittance were determined in situ as a function of the cyclical potencial and memory effect. The insertion process of lithium is reversible and change the film color from transparent (T=80%) to dark blue (T=20%).