Abstract The objective of this research was to develop a more sustainable composite and still keep its characteristics. Fibers treated with NaOH at 5% w/w for 2 hours were incorporated into natural rubber in different proportions (0 phr, 24 phr, 36 phr, 48 phr and 60 phr). The mechanical properties of the composites suffered changes, increasing the hardness, young’s modulus and decreasing its tensile strength. All the physical properties were not statistically different. The coloration became less dark in the WF60/CB0 treatment, and the electrical properties presented better resistivity with the increase in the concentration of fibers in the composite. This presents a possibility of using WF for the production of wood-rubber composites for the production of rubber artifacts which do not require high rolling resistance. Based on the results from this research, we recommended the WF24/CB36 mix to produce antistatic floors. characteristics 5 ww w 0 ( 3 4 6 phr. . phr) changes hardness youngs young s strength WF60CB0 WFCB WF60 CB0 CB WF60/CB treatment woodrubber wood resistance WF24CB36 WF24 CB36 WF24/CB3 floors WF60CB WF6 WF24CB3 WF2 CB3 WF24/CB WF24CB

ABSTRACT Purpose: To study the influence of silver nanoparticles (AgNP) on tissue reaction when incorporated into a polymeric matrix of polyacrylic acid-based (Carbopol®) gel as a proposal for a new low-cost type of biomaterial that is simple to manufacture for use as an antimicrobial and antioxidative dressing. Methods: In-vivo tests of implantation in the subcutaneous tissue of the back of rats were performed using polyethylene tubes in three situations: empty, only the gel, and gel incorporated with AgNP. Then, the tissue reaction was studied by counting inflammatory cells. Additionally, in-vitro tests of the antioxidative and antimicrobial activity of AgNP were performed. The radical 2,2 diphenyl-1 picrylhydrazyl (DPPH) was used to test the antioxidative activity of AgNP using electron spin resonance. The antimicrobial activity of AgNP was determined by minimum inhibitory concentration against the microorganisms: Staphylococcus aureus, Pseudomonas aeruginosa, and Escherichia coli. Results: The results indicated that AgNP presents antioxidative activity and was able to inhibit the growth of the microorganisms tested. The addition of AgNP in Carbopol® did not alter the tissue inflammatory response (p>0.05, Kruskal-Wallis’s test). Conclusions: The new biomaterial is promising for future use as a dressing for its beneficial properties for regenerative processes.