The automotive industry is constantly under several challenges in many aspects, such as development of new materials and improvement their manufacturability. In order to achieve light weight, reduced emissions and ensure conductor safety, advanced high strength steels (AHSS) are able to fulfill these requirements. Dual phase steels (DP) are well suited for light weighing car body constructions. The gas tungsten arc welding (GTAW) process is focused in literature as an alternative choice for joining AHSS steels; this study is held to disclose the exhibited microstructural constituents. In addition, quantitative determinations of the volume % of phases in the various weld regions were made. The relative amounts of lower bainite (LB), upper bainite (UB), and polygonal ferrite (PF) in the heat affected zone (HAZ) were determined by image analysis from optical microscopy (OM) and scanning electron microscopy (SEM). It was found that GTAW promoted the development of significant amounts of LB in the HAZ (50.89 %). In contrast atomic force microscopy (AFM) leads to quantify the different phases by the morphology, height and roughness, it was found that martensite (M) dropped down to 7.5% in the intercritical zone (IZ) although PF increases to 92.5% compared with the base metal (BM).

Resumo O avanço no desenvolvimento de peças automotivas exige novos materiais de baixo custo com propriedades mecânicas superiores e com maior resistência ao desgaste em comparação com os materiais existentes. Por exemplo, compósitos com matriz de alumínio (AMC) mostram melhores propriedades mecânicas como resistência à abrasão e ao desgaste, alta resistência e estabilidade química e dimensional. A indústria automotiva tem centrado em AMC para uma variedade de aplicações em peças automotivas, a fim de melhorar a economia de combustível, minimizar as emissões dos veículos, melhorar as opções de design e aumentar o desempenho. A Resistência ao desgaste é um fator importante a determinar para a vida útil dos componentes automotivos, em geral naqueles componentes submetidos a sistemas mecânicos como freios e suspensões. O processo de soldagem por fricção e mistura mecânica (FSW - Friction Stir Welding) surge como um processo capaz de unir AMC, principalmente com a capacidade de soldar sem comprometer seu reforço cerâmico. O objetivo deste estudo é focado na análise de características de desgaste da junta soldada por FSW de matriz de alumínio reforçados com 20 por cento em peso de compósito de carboneto de silício (A359 / SiC / 20p). O procedimento experimental consistiu em cortar amostras em pequenas placas e realizar três soldas nestas placas utilizando uma máquina FSW com uma ferramenta com ombro de 20 mm de diâmetro e pino de 8 mm de diâmetro. As características de desgaste das três juntas soldadas e metal base foram analisados aplicando carga constante de 5 N e uma velocidade de rotação de 100 rpm utilizando um aparelho de teste Pin-on-disk, usando uma esfera de aço de com safira com 6 mm de diâmetro. Os resultados experimentais indicam que as três juntas soldadas apresentaram baixo coeficiente de fricção comparado com o metal base. Os resultados determinaram que os parâmetros do processo FSW afetam a resistência ao desgaste das juntas soldadas, devido a diferentes modificações microestruturais durante a soldagem, que provoca uma baixa resistência ao desgaste na zona soldada.

Abstract Advancement in automotive part development demands new cost-effective materials with higher mechanical properties and improved wear resistance as compared to existing materials. For instance, Aluminum Matrix Composites (AMC) shows improved mechanical properties as wear and abrasion resistance, high strength, chemical and dimensional stability. Automotive industry has focused in AMC for a variety of applications in automotive parts in order to improve the fuel economy, minimize vehicle emissions, improve design options, and increase the performance. Wear resistance is one of the most important factors in useful life of the automotive components, overall in those components submitted to mechanical systems like automotive brakes and suspensions. Friction Stir Welding (FSW) rises as the most capable process to joining AMC, principally for the capacity to weld without compromising their ceramic reinforcement. The aim of this study is focused on the analysis of wear characteristics of the friction-stir welded joint of aluminum matrix reinforced with 20 percent in weight silicon carbide composite (A359/SiC/20p). The experimental procedure consisted in cut samples into small plates and perform three welds on these with a FSW machine using a tool with 20 mm shoulder diameter and 8 mm pin diameter. The wear features of the three welded joints and parent metal were analyzed at constant load applying 5 N and a rotational speed of 100 rpm employing a Pin-on - Disk wear testing apparatus, using a sapphire steel ball with 6 mm diameter. The experimental results indicate that the three welded joints had low friction coefficient compared with the parent metal. The results determine that the FSW process parameters affect the wear resistance of the welded joints owing to different microstructural modifications during welding that causes a low wear resistance on the welded zone.