ABSTRACT Objective: This cross-sectional study evaluated the bone thickness on mini-implants insertion site, the factors that influence the digital planning of MARPE appliance (miniscrew-assisted rapid palatal expansion), and its different designs. Methods: A total of 135 plannings were assessed regarding the size of the expander screw used, the positioning and the type of the mini-implant rings, and their location in relation to the teeth. Bone thickness measurements were assessed in the region of the mini-implants’ trajectory. Differences between the sexes was verified using the ANOVA test (5% significance). Results: 73 cases were planned with 4 mini-implants and 62 cases, with 6 mini-implants. In 90% of cases, teeth #16 and #26 were used as supports, and the most used expander screw was 13mm (64.1% of cases). The anterior mini-implants of conventional MARPE showed more pronounced insertion in bone in males (5.9 ± 2mm; p= 0.025). The extra mini-implants (anterior region) were inserted with greater bone thickness in males (11.1 ± 2.3mm) compared to females (9.9 ± 1.8mm; p=0.041). A greater bone thickness was observed in males (10.1 ± 2.1 mm) when using mini-implants in the paramedian region. Conclusion: Additional rings allow more pronounced bone insertion. Male patients had greater bone thickness, which may be related to greater difficulty in opening the sutures. The alveolar process region seems to be a satisfactory site for mini-implants to those patients with reduced bone thickness in the paramedian posterior region. MARPE appliance must be customized for each patient, due to bone thickness and anatomical variations. Objective crosssectional cross sectional miniimplants mini implants miniscrewassisted miniscrew assisted expansion, expansion , expansion) designs Methods 13 miniimplant implant trajectory 5% 5 (5 significance. significance . significance) Results 7 miniimplants. implants. 90 16 #1 26 #2 supports mm 64.1% 641 64 1 (64.1 cases. cases) 5.9 59 9 (5. 2mm p 0.025. 0025 0.025 0 025 0.025) 11.1 111 11 (11. 2.3mm 23mm 2 3mm 9.9 99 (9. 1.8mm 18mm 8mm p=0.041. p0041 p=0.041 041 p=0.041) 10.1 101 10 (10. 21 2. Conclusion sutures patient variations ( # 64.1 (64. 5. 002 0.02 02 11. (11 9. (9 p004 p=0.04 04 10. (10 64. (64 00 0.0 (1 p00 p=0.0 (6 0. p0 p=0. p=0

RESUMO Objetivo: Avaliar os fatores que influenciam o planejamento digital do expansor MARPE (miniscrew-assisted rapid palatal expansion), a espessura óssea no local de inserção dos mini-implantes, e os diferentes possíveis desenhos desse aparelho. Métodos: Foram avaliados 135 planejamentos quanto ao tamanho do parafuso expansor utilizado, posicionamento, tipo dos anéis dos mini-implantes, e sua localização em relação aos dentes de apoio. As medidas de espessura óssea foram avaliadas na região de inserção dos mini-implantes. As diferenças entre os sexos foram verificadas por meio do teste ANOVA (5% de significância). Resultados: Os planejamentos tiveram uma distribuição de 73 casos com quatro mini-implantes e 62 casos com seis mini-implantes. Em 90% dos casos, os dentes #16 e #26 foram usados como dentes de apoio, e o parafuso expansor mais usado foi o de 13 mm (64,1% dos casos). Os mini-implantes anteriores do MARPE convencional mostraram uma inserção com maior espessura óssea em homens (5,9 ± 2mm; p= 0,025). Os mini-implantes extras (região anterior) foram inseridos com maior espessura óssea nos homens (11,1 ± 2,3 mm), em comparação com as mulheres (9,9 ± 1,8 mm; p=0,041). Foi observada maior espessura óssea em homens (10,1 ± 2,1 mm) na região paramediana. Conclusões: Anéis adicionais permitem uma inserção óssea mais pronunciada. Os pacientes do sexo masculino apresentaram maior espessura óssea, o que pode estar relacionado à maior dificuldade de abertura das suturas. Objetivo miniscrewassisted miniscrew assisted expansion, expansion , expansion) miniimplantes, miniimplantes mini implantes, implantes aparelho Métodos utilizado posicionamento apoio miniimplantes. implantes. 5% 5 (5 significância. significância . significância) Resultados 7 6 90 16 #1 26 #2 1 64,1% 641 64 (64,1 casos. casos) 5,9 59 9 (5, 2mm p 0,025. 0025 0,025 0 025 0,025) anterior 11,1 111 11 (11, 23 2 3 2, mm, 9,9 99 (9, 18 8 1, p=0,041. p0041 p=0,041 041 p=0,041) 10,1 101 10 (10, 21 paramediana Conclusões pronunciada suturas ( # 64,1 (64, 5, 002 0,02 02 11, (11 9, (9 p004 p=0,04 04 10, (10 64, (64 00 0,0 (1 p00 p=0,0 (6 0, p0 p=0, p=0

Resumo Avaliar a resistência à flexão (FS) e o módulo de flexão (FM) de uma cerâmica comercial 3Y-TZP após envelhecimento artificial, e com ou sem dois tempos de aplicação de plasma não térmico (NTP). Além disso, a transformação de fase cristalina e a nano-topografia de superfície após a aplicação de NTP, durante diferentes períodos de envelhecimento, foram avaliadas. Noventa barras 3Y-TZP (45x4x3 mm) foram feitas para testes de FS e FM, e distribuídas em nove grupos (n=10): sem NTP/sem envelhecimento (Controle); sem NTP/4h de envelhecimento; sem NTP/30h de envelhecimento; 10sNTP/sem envelhecimento; 10sNTP/4h; 10sNTP/30h; 60sNTP/sem envelhecimento; 60sNTP/4h e 60sNTP/30h. O envelhecimento artificial acelerado foi simulado em autoclave (134º C a 2 bar) por até 30 horas. FS e FM foram avaliados em máquina de ensaio universal e os dados analisados pela ANOVA e teste de Tukey (α = 0,05). A mudança de volume da fase monoclínica de zircônia (MPV) foi avaliada usando difração de raios-X e nano-topografia de superfície foi avaliada utilizando microscopia de força atômica (baseline até 30h). A aplicação do NTP não influenciou a FS e FM da zircônia. Comparado ao Controle (“sem NTP/sem envelhecimento”), a FS das amostras de zircônia tratadas por 30 horas em autoclave (“sem NTP/30h de envelhecimento”) aumentou. O envelhecimento artificial por 30 horas aumentou significativamente a FM da zircônia, independente do tempo de aplicação do NTP. O MPV tendeu a aumentar em função do aumento do tempo de envelhecimento para todos os grupos, que pode ter resultado nas irregularidades superficiais observadas com 30 horas de envelhecimento. O NTP não afetou as propriedades da zircônia testadas, mas o envelhecimento por 30 horas pode alterar a FS, FM e MPV da zircônia.

Abstract To evaluate the flexural strength (FS) and flexural modulus (FM) of a commercial 3Y-TZ0P ceramic after artificial aging and either without or with two application times of non-thermal plasma treatments (NTP). In addition, changes in crystalline phase transformation and surface nano-topography after NTP application, during different aging periods, were evaluated. Ninety 3Y-TZP bars (45x4x3 mm) were made for FS and FM testing, and assigned to nine groups (n=10): no NTP/no aging (Control); no NTP/4h aging; no NTP/30h aging; 10s NTP/no aging; 10s NTP/4h aging; 10s NTP/30h aging; 60s NTP/no aging; 60s NTP/4h aging and 60s NTP/30h aging. Artificial accelerated aging was simulated using an autoclave (134º C at 2 bar) for up to 30h. FS and FM were assessed using a universal testing machine and data analyzed using a ANOVA and Tukey test (α=0.05). The volume change in zirconia monoclinic phase (MPV) was evaluated using X-ray diffraction and surface nano-topography was assessed using atomic force microscopy (baseline until 30h-aging). NTP application did not influence the FS and FM of zirconia. Compared to the Control (no NTP/no aging), the FS of zirconia samples treated for 30 hours in autoclave (“no NTP/30h aging” group) increased. Artificial aging for 30 hours significantly increased the FM of zirconia, regardless of NTP application. MPV tended to increase following the increase in aging time, which might result in the surface irregularities observed at 30h-aging. NTP did not alter the zirconia properties tested, but 30h-aging can change the zirconia FS, FM and MPV.