ABSTRACT This work was developed aiming to evaluate the effects of strands orientation and veneer inclusion on the physical and mechanical properties of the boards. The boards were manufactured with density of 0,70 g/ cm3 and face to core ratio of 50:50, using phenol-formaldheyde resin. The values of MOE and MOR of the oriented strandboards were significactivelly high in comparison to no-oriented strandboards. The veneer inclusion in the non-oriented strandboards contributed to increase in MOE and MOR on the axial direction of the board and decrease on the cross direction. The veneer inclusion on the oriented strandboard did not contribute significactivelly to increase of MOE and MOR. The effects of strands orientation and veneer inclusion did not increase significativelly the water absorption. On the other hand, the veneer inclusion contributed to reducing of thickness sweeling.

RESUMO Este trabalho foi desenvolvido com objetivo de avaliar a influência da orientação das partículas “strand” e inclusão laminar sobre as propriedades físico-mecânicas das chapas. Foram fabricadas chapas com densidade de 0,70g/cm3 e composição face:miolo de 50:50, utilizando resina fenolformaldeído. Os valores de MOE e MOR das chapas com partículas orientadas foram significativamente superiores em comparação às chapas com partículas não-orientadas. A inclusão laminar em chapas com partículas não-orientadas contribuiu para o aumento nos valores de MOE e MOR na direção paralela ao plano da chapa e redução na direção perpendicular. Para as chapas com partículas orientadas, a inclusão laminar não contribuiu significativamente para o incremento nos valores de MOE e MOR. A orientação ou não das partículas e o reforço laminar não influenciaram nos valores de absorção de água. A inclusão laminar contribuiu para a redução nos valores de inchamento em espessura das chapas.