Abstract: Brachystegia spiciformis and Pericopsis angolensis are two hardwood species found in the Miombo woodlands. The wood features, kraft pulping and strength pulp properties of both species were evaluated in order to determine their potential as raw material for papermaking. Brachystegia spiciformis wood density was 640 kg m-3 and Pericopsis angolensis was 795 kg m-3. Pericopsis angolensis wood has higher cell wall thickness and occluded fibre lumen as remarkable anatomical properties. Runkel ratio, slenderness ratio, and the coefficients of flexibility and rigidity in Brachystegia spiciformis were 1,5; 65,7; 41,2% and 29,4% while in Pericopsis angolensis these values were 17,6; 59,9; 5,4% and 47,3%, respectively. Brachystegia spiciformis has a higher cellulose content, lower hemicellulose and lignin content, and higher S/G ratio than Pericopsis angolensis. In kraft pulping, a higher demand of active alkali was needed for both species, and pulps with high kappa number (24-27) and low pulp yield (40%) were obtained. Pericopsis angolensis pulps reached tensile, tear and burst indexes of 99,6 Nm g-1; 5,9 mN.m2 g-1 and 4,9 kPa.m2 g-1, respectively. Brachystegia spiciformis pulps reached tensile, tear and burst indexes of 100,3 Nm g-1; 10,7 mN.m2 g-1 and 6,1 kPa.m2 g-1, respectively. As a conclusion, Brachystegia spiciformis wood has better pulpability than Pericopsis angolensis wood, according to its pulps properties, despite of the similar pulp yield between both species. Both species may be suitable for unbleached wrapping papers and rigid cardboards manufacturing.

As galactoglucomananas são as principais frações de hemiceluloses presentes nas madeiras moles e contêm, principalmente, as hexoses galactose, glicose e manose. O isolamento eficiente e seletivo dessas hemiceluloses é um obstáculo crítico a superar para sua utilização. Os objetivos deste trabalho foram extrair e caracterizar soluções aquosas ácidas e neutras de hemiceluloses de cavacos de madeira de Pinus radiata, bem como avaliar sua viabilidade para a produção de bioetanol. As hemiceluloses em P. radiata representam 26 g/100 g de madeira (base seca), e as hexoses são responsáveis por aproximadamente 64% dessa quantidade. De acordo com as diferentes condições de extração, cerca de 50% da fração hemicelulósica foi solubilizada e recuperada depois de uma precipitação com etanol. As frações recuperadas de hemiceluloses estavam na forma de oligômeros com peso molecular médio (Mw) variando entre 4x10³ e 4x10(5) g/mol. Os oligômeros hemicelulósicos foram hidrolisados com ácido sulfúrico diluído e os hidrolisados concentrados até aproximadamente 70 g/L hexosas e fermentados pela levedura Saccharomyces cerevisiae. Os resultados de fermentação indicaram que os açúcares obtidos dos extratos ácidos e neutros foram fermentados com rendimentos máximos de etanol de 63% e 54% (22 g/L e 19 g/L), respectivamente. A conversão de hemiceluloses da madeira em etanol é viável, porém seu baixo rendimento faz que o processo não seja economicamente atrativo, razão por que melhorias no processo ou usos alternativos das hemiceluloses devem ser avaliados.

Galactoglucomannans are the major hemicellulosic fraction present in softwoods, and is mainly composed by the hexoses: galactose, glucose and mannose. The efficient and selective isolation of these hemicelluloses is regarded as one of the most critical obstacles to overcome for their utilization. The objective of the current work was to extract and characterize acidic and neutral aqueous solutions of hemicelluloses from Pinus radiata wood chips and investigate their feasibility for bioethanol production. Hemicelluloses in P. radiata represented 26 g/100 g wood (o.d.w.) and hexoses are responsible for approximately 64% of this amount. According to the different extraction conditions, approximately 50% of the hemicellulosic fraction was solubilized and recovered after precipitation with ethanol. The recovered hemicellulosic fractions were in the form of oligomers with weight-average molecular weigth (Mw) varying from 4x10³ to 4x10(5) g/mol. Hemicellulosic oligomers were hydrolyzed with dilute sulfuric acid and the hydrolysates concentrated until approximately 70 g/L of hexoses and fermented by Saccharomyces cerevisiae yeast. Fermentation results showed that sugar obtained from acid and neutral extractions were fermented to ethanol with maximum yields of 63% and 54% (22 g/ L and 19 g/L), respectively. The conversion of wood hemicellulosic substrates to ethanol is feasible but the low ethanol yields obtained make the process not economically attractive and optimization of the process or alternatives uses for hemicelluloses should be evaluated.

Madeira de tração e oposta de árvores de Eucalyptus globulus foram analisadas quanto a suas características químicas e produção de polpa Kraft. A caracterização química da madeira de tração (TW) de Eucalyptus globulus Labill. mostrou um conteúdo similar de celulose, alto conteúdo de xilanas e baixo conteúdo de lignina quando comparada com a madeira oposta (OW) de uma mesma árvore. O conteúdo de lignina foi 16% menor e contém 32% mais unidades siringila em TW que em OW. O aumento das unidades siringila favoreceu a formação de ligações β-O-4 que também foram mais altas em TW que em OW (84% vs. 64%, respectivamente). O efeito destas características foi avaliado na produção de polpas Kraft de ambos tipos de madeira. A um número kappa de 16, as polpas Kraft obtidas de TW demandaram menos álcali ativo na deslignificação e apresentaram rendimento de polpa levemente maior ou similar que as polpas obtidas com OW. O comprimento das fibras, o coarseness e a viscosidade também foram maiores em polpas de madeira de tração que oposta. Quando as polpas foram refinadas a 30°SR, as polpas TW necessitaram 18% mais revoluções no refinador PFI para atingir o mesmo grau de refino que as polpas OW. As propriedades de resistência mecânica (índices de tração, rasgo e estouro) foram levemente maiores ou similares em polpas de madeira de tração quando comparadas com polpas de madeira oposta. Depois de uma sequência de branqueamento OD0(EO)D1, ambas polpas alcançaram até 89% de alvura ISO. As polpas branqueadas de TW apresentaram viscosidade mais alta e menor conteúdo de ácidos hexenurônicos que as polpas de OW. Os resultados mostraram que TW apresenta alto teor de xilanas e menor teor de lignina que ocasionam uma diminuição no consumo de álcali, aumento das propriedades de resistência mecânica e comportamento similar no branqueamento em comparação com polpas de OW.

Tension (TW) and opposite wood (OW) of Eucalyptus globulus trees were analyzed for its chemical characteristics and Kraft pulp production. Lignin content was 16% lower and contained 32% more syringyl units in TW than in OW. The increase in syringyl units favoured the formation of β-O-4 bonds that was also higher in TW than in OW (84% vs. 64%, respectively). The effect of these wood features was evaluated in the production of Kraft pulps from both types of wood. At kappa number 16, Kraft pulps obtained from TW demanded less active alkali in delignification and presented slightly higher or similar pulp yield than pulps made with OW. Fiber length, coarseness and intrinsic viscosity were also higher in tension than in opposite pulps. When pulps where refined to 30°SR, TW pulps needed 18% more revolutions in the PFI mill to achieve the same beating degree than OW pulps. Strength properties (tensile, tear and burst indexes) were slightly higher or similar in tension as compared with opposite wood pulps. After an OD0(EO)D1 bleaching sequence, both pulps achieved up to 89% ISO brightness. Bleached pulps from TW presented higher viscosity and low amount of hexenuronic acids than pulps from OW. Results showed that TW presented high xylans and low lignin content that caused a decrease in alkali consumption, increase pulp strength properties and similar bleaching performance as compared with pulps from OW.