Nowadays, the main reasons for replacement of resin-based composite restorations are fracture or problems with the integrity of their interface, such as marginal staining, microleakage, or secondary caries. The aim of the present study was to evaluate the influence of the organic matrix on polymerization stress (PS), degree of conversion (DC), elastic modulus (E), flexural strength (FS), Knoop hardness (KHN), sorption (SP), and solubility (SL). In order to obtain a material which combines better mechanical properties with lower PS, seven experimental composites were prepared using BisGMA to TEGDMA molar ratios of 2:8, 3:7, 4:6, 5:5, 6:4, 7:3 and 8:2 and 40% of silica. PS was obtained in a universal testing machine, using acrylic as bonding substrate. DC was determined using Fourier Transform Raman spectroscopy. E and FS were obtained by the three-point bending test. KHN was measured by a microindentation test using a load of 25 g for 30 s. SP and SL were assessed according to ISO 4049. The data were submitted to one-way ANOVA. The increase in BisGMA concentration resulted in the decrease of PS, DC, E, FS and KHN. However, it did not change the SP and SL values. FS, E and KHN showed a strong and direct relationship with the DC of the materials. The composite material with a BisGMA to TEGDMA molar ratio of 1:1 was the one with better mechanical properties and lower PS.

The purpose of this study was to evaluate the flexural strength of a direct composite, for indirect application, that received heat treatment, with or without investment. One indirect composite was used for comparison. For determination of the heat treatment temperature, thermogravimetric analysis (TGA) and differential scanning calorimetry (DSC) were performed, considering the initial weight loss temperature and glass transition temperature (Tg). Then, after photoactivation (600 mW/cm² - 40 s), the specimens (10 x 2 x 2 mm) were heat-treated following these conditions: 170ºC for 5, 10 or 15 min, embedded or not embedded in investment. Flexural strength was assessed as a means to evaluate the influence of different heat treatment periods and investment embedding on mechanical properties. The data were analyzed by ANOVA and Tukey's test (α = 0.05). TGA showed an initial weight loss temperature of 180ºC and DSC showed a Tg value of 157°C. Heat treatment was conducted in an oven (Flli Manfredi, Italy), after 37°C storage for 48 h. Flexural strength was evaluated after 120 h at 37°C storage. The results showed that different periods and investment embedding presented similar statistical values. Nevertheless, the direct composite resin with treatments presented higher values (178.7 MPa) compared to the indirect composite resin (146.0 MPa) and the same direct composite submitted to photoactivation only (151.7 MPa). Within the limitations of this study, it could be concluded that the heat treatment increased the flexural strength of the direct composite studied, leading to higher mechanical strength compared to the indirect composite.