Forming semiconductor heterojunction is promising for improved photocatalytic performance due to synergistic combination of the best properties of each material. The present study reports a simple hydrothermal strategy to form n-n heterojunction of Ta2O5 nanotubes and BiVO4 microstructures. The Ta2O5/BiVO4 heterojunctions were characterized by Raman spectroscopy, UV Vis diffuse reflectance spectroscopy (DRS), X-ray diffraction (XRD), scanning electron microscopy (SEM) and their photocatalytic activity was evaluated by hydrogen production and photodegradation of methylene blue (MB) dye in aqueous medium under AM 1.5 G (100 mW cm2) condition. The heterojunctions have optical absorption in the visible region (200 500 nm) with crystal structures defined as monoclinic for BiVO4 and orthogonal for Ta2O5. For MB photodegradation, the Ta2O5/BiVO4 obtained via hydrothermal route showed a photodegradation of 72.3%, compared to 28.3% presented by the sample produced through the mechanical mixture, with the maintenance of 86.4% of its photocatalytic performance after 3 cycles of photodegradation. For H2 production, hydrothermally prepared Ta2O5/BiVO4 generated 10.2 μmol g-1 of H2 in 3 h; while Ta2O5 nanotubes and mechanical Ta2O5/BiVO4 mixture shows 6.82 and 2.80 μmol g-1, respectively. The results suggest that Ta2O5/BiVO4 is a promising material for applications in photocatalysis, promoting sustainable energy production through hydrogen and for the treatment of effluents containing cationic dyes.

The growth of titanium dioxide nanotubes (TiO2) via anodization process depends on the controlling parameters such as applied potential, anodization time, and electrolyte composition. In the present work, the Taguchi method was applied to evaluate statistically the influence of the anodization parameters on the morphology of anodized TiO2 films. Mixture of ethylene-glycol and glycerol was used as an electrolyte and the settings of the experimental design were parameterized on the basis of four important anodization factors consisting of chemical pretreatment, amount of fluoride, water content and applied potential. Samples were characterized by XRD and FEG-SEM. Based on 4 variables at 3 different settings, full factorial plan requires 34 = 81 tests. In this work the experiment was designed on the basis of an L9 (34) orthogonal array (4 variables, 3 levels, 9 tests). The optimum conditions were found on the basis of smaller-is-better and larger-is-better analyses. The signal-to-noise ratio was employed to find optimal process parameters levels and to analyze the influence of these parameters on the tubular length, internal and external diameters and formation of nanograss on the film surface. Hence, it is clearly shown that the performance of TiO2 nanotubes can be evaluated by the Taguchi method.

The evolution of TiO2 nanotubular morphology, synthesized in a mixture of fluorinated ethylene glycol and glycerol electrolyte, was studied as a function of the anodization time. The samples were characterized by FEG-SEM, XRD, XPS, UV-Vis and EIS. The formation of single-or double-walled TiO2 nanotube structure can be efficiently controlled by the anodization time. For anodization times less than 30 minutes, a compact oxide layer is formed, followed by double-walled nanotube formation up to 120 minutes and single-walled nanotubes up to 240 minutes. XPS analyses show that the samples obtained with short anodization time have a high carbon content and oxygenated surface species compared to the longer-time anodized sample; however, binding energy peaks for Ti 2p remained invariant. The performances of TiO2 nanotubular photoelectrodes were evaluated in photoelectrochemical water splitting where TiO2 nanotubes anodized for 120 minutes presented the best performance that was related to their optimal morphology and charge transportation.