Polymeric porous membranes with a high control of morphology and porous size were fabricated from colloidal crystals made of silica particles. This fabrication process allows different morphologies according to the particle sizes and number of layers on the templates. Silica particles with a narrow size distribution were synthesized by two methods. Colloidal crystals were obtained by vertical deposition of the particles on a glass substrate and by the Langmuir-Blodgett technique to create templates of different particle sizes. To produce the membrane, polystyrene (PS) and styrene (St)-vinyl benzyl thymine (VBT) copolymers were used. The procedure involved the infiltration of monomers in the templates and then, the polymerization by UV radiation. The proposed method represents a relatively simple alternative, both versatile and economically attractive to manufacture macroporous polymers.

Se elaboraron membranas poliméricas porosas con elevado control de la morfología y de los tamaños de poros a partir de cristales coloidales constituidos por partículas de sílice. El método empleado permite obtener diferentes morfologías dependiendo del tamaño de las partículas y del número de capas involucradas en los depósitos. Para la síntesis de las partículas se emplearon dos métodos, originándose distintos tamaños. Los cristales coloidales se obtuvieron por deposición vertical de las partículas sobre un sustrato de vidrio y por la técnica de Langmuir-Blodgett. Se fabricaron membranas de poliestireno (PS) y de copolímero de estireno (St)-vinil bencil timina (VBT). El procedimiento involucró la infiltración de los monómeros seguida por la polimerización por irradiación con luz UV. El método propuesto provee una alternativa relativamente simple, muy versátil y a la vez económica para la elaboración de polímeros macroporosos.

In this work, the synthesis of polyurethane flexible foam is realized with the experimental design Taguchi, using castor oil with and without maleinization. The kinetic reaction of oil esterification was monitored by estimating the number of acid groups (ASTM D4662 - 03), and the mechanical properties of the foam were studied, including density, tensile resistance, % elongation, resilience and hardness (Norm NTC 2019 Icontec). The influence of various synthesis parameters was investigated, namely amount and type of catalyst, molar ratio of castor oil (CO) - maleinizated castor oil (MACO), amount of water and surfactant used. The foams were analyzed using FTIR and scanning electron microscopy (SEM). The results showed first order kinetics with respect to the anhydride. The maleinizated castor oil (MACO) increased the mechanical resistance of the foam due to the greater interweaving by the incorporation of acid groups.

En este trabajo se realiza la síntesis de espumas flexibles de poliuretano empleando un diseño experimental Taguchi, utilizando aceite de castor con y sin maleinización, se estudia la cinética de la reacción de esterificación del aceite por cuantificación de los grupos ácido (ASTM D4662 - 03) y se evalúan las propiedades mecánicas de las espumas (densidad, resistencia tensil, % elongación, resiliencia y dureza. Norma NTC 2019 Icontec) obtenidas en función de las variables de síntesis (cantidad y tipo de catalizador, relación molar aceite castor (CO) - aceite maleinizado (MACO), cantidad de agua y surfactante empleado). Se realizan análisis de FTIR y SEM para las espumas. Los resultados mostraron una cinética de primer orden con respecto al anhídrido. El aceite maleinizado (MACO) incrementa la resistencia mecánica de las espumas, debido al mayor entrecruzamiento por la incorporación de grupos ácido.