Abstract Cellulose nanocrystals (CNC) and nanofibrils (CNF) were obtained by acid hydrolyzis and mechanical treatment, respectively, of cellulosic fibers from paper. Additionally, surface modification was performed for CNC by neutralization (NaOH) and oxidation (TEMPO). The thermal stability, surface properties and rheological behavior of these nanomaterials were compared. A clear difference in CNC surface was found upon neutralization and oxidation treatments, leading to distinct thermal behaviors. Optical and rheological properties were found to be predominantly by the particles size, being strongly affected by inertial effects.

This paper present the most relevant advances in the fields of: i) cellulose fibres surface modification; ii) cellulose fibres-based composite materials; and iii) nanocomposites based on cellulose whiskers or starch platelet-like nanoparticles. The real breakthroughs achieved in the first topic concern the use of solvent-free grafting process (plasma) and the grafting of the matrix at the surface of cellulose fibres through isocyanate-mediated grafting or thanks to "click chemistry". Concerning the second topic, it is worth to mention that for some cellulose/matrix combination and in the presence of adequate aids or specific surface treatment, high performance composite materials could be obtained. Finally, nanocomposites allow using the semi-crystalline nature and hierarchical structure of lignocellulosic fibres and starch granules to more deeply achieve this goal profitably exploited by Mother Nature

Solid lithium-conducting nanocomposite polymer electrolytes based on poly(oxyethylene) (POE) were prepared from high aspect ratio cellulosic whiskers and lithium imide salt, LiTFSI. The cellulosic whiskers were extracted from tunicate -a sea animal- and consisted of slender parallelepiped rods that have an average length around 1 µm and a width close to 15 nm. High performance nanocomposite electrolytes were obtained. The filler provided a high reinforcing effect while a high level of ionic conductivity was retained with respect to unfilled polymer electrolytes. Cross-linking and plasticizing of the matrix as well as preparation of the composites from an organic medium were also investigated.