Polyaniline is a conducting polymer that has recently been studied regarding its potential in the removal of contaminants by heterogeneous photocatalysis. Since it is a polymer with a high absorption capacity of photons in the visible region, it promotes the photosensitization of catalysts that are typically inactive in solar systems. The increasing number of publications applying photocatalysis and composite catalysts based on polyaniline highlights the importance of this subject. This review systematizes the most important and specific contributions of composite catalysts formed by polyaniline. The main mechanisms proposed for photosensitization, which show the synergism between the phases of the composite, are summarized. Moreover, the relevance of morphology and conductivity of the composite catalyst, operating parameters (eg. pH, and light source contaminant) are some of the aspects discussed, revealing how these differ from traditional catalysts. Future prospects for the continuation and improvement of this issue mainly involve a greater variety of contaminant removal tests and understanding of relations between the structure of the material and its photocatalytic property.

ABSTRACT Conducting polymers presents many potential applications such as biosensors and biofuelcells. However, to be used in those devices, a thin film must be deposited onto a conducting and biocompatible substrate. In this work, carbon nanotubes (CNT) were mixed in a poly (lactic acid) - PLA - matrix with different compositions (from 0.25 to 5.0 %) in order to form conducting composites suitable to the deposition of a conducting polymer. Thermal properties of PLA/CNT composites were evaluated by Thermogravimetry (TG) and Differenctial Scanning Calorimetry (DSC), and the electrical properties were evaluated by 2-probe method and by Electrochemical Impedance Spectroscopy (EIS). Thermal analysis showed and influence of CNT quantities on PLA crystallization, which also showed an influence on conductivity of the tested materials. Besides, the conductivity of PLA/NTC 1% film showed similar values of the conducting polymer (Pani) itself.

Neste trabalho, foi estudada a miscibilidade de misturas de um PHB constituído de frações de alta e baixa massa molar com um PLA de alta massa molar. Os materiais extrudados foram analisados pelas técnicas de calorimetria exploratória diferencial (DSC), espectroscopia dielétrica (DE) e análises dinâmico-mecânicas (DMA). A partir dos resultados observou-se o distinto comportamento cristalino das frações de PHB, assim como a miscibilidade parcial do PLA com o PHB de baixa massa molar.

In this work, the miscibility of a PHB formed by high and low molar mass fractions and a low molar mass PLA was studied. The extruded materials were analyzed by differential scanning calorimetry (DSC), dielectric spectroscopy (DS) and dynamic mechanical analysis (DMA). From these results, it was observed an unique behavior from the PHB fractions, and the partial miscibility of PLA onto low molar mass PHB.

In this work, the improvement of mechanical properties in biodegradable materials was obtained through the incorporation of natural and also biodegradable plasticizers and nucleation agents into the PHBV copolymer. PHBV production with different quantities of additives was obtained by extrusion followed by injection. The additives in the copolymer were efficient, resulting in an adequate processing due to the presence of nucleate and an improvement of the mechanical properties of the resulting material provided by the action of the plasticizer. The formulation with the minimum amount of additive content, 5% epoxidized cottonseed oil and 0.1% Licowax, was the most effective showing 35% reduction in the elastic modulus, and 18% in the PHBV crystallinity; 58% increase in impact resistance and 46% increase in elongation. Furthermore, it is important to emphasize that the natural additives were very efficient for biodegradation, showing a mass loss higher of pure PHBV.

O poli(hidroxibutirato) - PHB - e o poli(ácido lático) - PLA - são dois poliésteres termoplásticos com grande potencial para uso em aplicações industriais, sendo viáveis nos principais métodos de processamento e totalmente biodegradáveis. Porém, devido às suas propriedades mecânicas limitadas, necessitam de modificações para melhorar seu desempenho e tornarem-se industrialmente competitivos. Foram estudadas propriedades e características destes dois polímeros e suas misturas poliméricas, avaliando a possibilidade do uso na preparação de filmes finos por extrusão para embalagens. Verificou-se a possibilidade de produção de filmes finos de misturas PHB/PLA, através das técnicas de extrusão de filmes, planos e tubulares soprados. Porém, para viabilizar a produção industrial destes filmes, modificações devem ser realizadas no processo de produção e/ou no preparo da mistura polimérica através da aditivação, com o objetivo de reduzir a alta adesividade dos filmes durante o seu processamento.

Poly(hydroxybutyrate) - PHB - and poly(latic acid) - PLA - are thermoplastic polyesters with huge potential for industrial applications since they are fully biodegradable and can be processed by usual methods. However, due to their limited mechanical properties, they need to be modified to achieve better performance and become industrially competitive. The properties of both polymers and their mixtures were evaluated in order to investigate their application for thin films extrusion, for packages. PHB/PLA thin films were produced by extrusion and blow film techniques. To allow for an industrial production process, the preparation of the polymer blend should be changed in order to decrease their high adhesion during processing.

PHB was characterized after different industrial processes by Differential Scanning Calorimetry (DSC), Fourier Transform Infrared Spectroscopy (FTIR), Melt Flow Index (MFI), Complex Dielectric Relaxation (CDR) and Size Exclusion Chromatography (SEC). Some properties of PHB were investigated before and after processing, in order to understand how temperature and other extrusion or injection conditions affect the polymer degradation. All the processed samples showed an increasing in the melt flow index, a decreasing of the dynamic crystallization temperature, and a reduction in the molar mass, suggesting some degradation. The molar mass reduction after processing, predicted when only thermal degradation is considered, was calculated in function of the kinetic parameters, such as constant thermal degradation and residence time during the industrial processing. It was found that the real molar mass reduction was higher than the theoretical value, indicating an important contribution of the shearing of polymeric chains during processing in the PHB degradation.