Abstract Objective: In this study, a comparative evaluation of the physicochemical properties of Cention N and other direct restorative materials was performed. Three restorative materials—a resin-modified glass ionomer (Fuji II LC), an alkasite-based resinous material (Cention N), and a resin composite (Tetric N Ceram)—were characterized in terms of degree of conversion, Knoop hardness number (KHN) ratio, flexural strength, elastic modulus, water sorption, water solubility, microshear bond strength to dentin, immediate microleakage, and radiopacity. Methodology: The microshear bond strength to dentin and microleakage of Cention N were evaluated with and without the application of an adhesive system (Tetric N Bond Universal). A one-way ANOVA test was used to analyze the data in terms of degree of conversion, KHN ratio, water sorption, water solubility, microshear bond strength to dentin, and radiopacity. A two-way ANOVA test (carried out considering the material type and ethanol aging as factors) was used to analyze the data in terms of flexural strength and elastic modulus. The Kruskal–Wallis test was used to statistically analyze the data on microleakage. A significance level of α=0.05 was used for all tests. Results: Fuji II LC was found to have the highest degree of conversion, water sorption, and microleakage, as well as the lowest flexural strength. Cention N had the highest solubility; when used with an adhesive system, it achieved bond strength and microleakage similar to those of the Tetric N Ceram composite. Tetric N Ceram had the highest degree of conversion, KHN ratio, and radiopacity. Conclusion: The properties of Cention N validate its efficacy as an alternative direct restorative material when used in conjunction with an adhesive system.

Abstract Bruxism is the repetitive muscle-mandibular behavior characterized by clenching and/or grinding of the teeth, which reflects the presence of one or more underlying conditions or factors. The objective of this descriptive study was to determine the association between bruxism and stress self-perceived during the pandemic, as well as their frequency by gender and academic area. An interrogation and self-perceived stress scale PSS-14 were applied to students from the different areas of the Institute of Health Sciences (ICSa) to determine the presence or absence of stress and bruxism symptom, a Chi-square was used for the comparison between variables, considering a value of p<0.005 as significant, a two-way ANOVA was performed to evaluate the difference between the symptoms before and during the isolation of the pandemic. The total number of participants was 825, a final sample of 420 students was obtained, made up of 297 (70.72%) women and 123 (29.28%) men, with an average age of 20±1.75 years. We found an association between the frequency of bruxism and severe stress generated during the social isolation of the COVID-19 pandemic, with a high perception of stress in the medicine area and a high frequency of bruxism in the área of nutrition p>0.005. ICSa students between 18 and 24 age perceive symptoms of bruxism and high levels of stress caused during the pandemic.

Resumen El bruxismo es el comportamiento músculo-mandibular repetitivo caracterizado por apretamiento y/o rechinamiento de los dientes, que refleja la presencia de una o varias condiciones o factores subyacentes. Se realizó un estudio descriptivo con el objetivo de determinar la asociación del nivel de estrés y síntomas de bruxismo autopercibidos durante la pandemia, así como su frecuencia por género y área académica. Se aplicó un interrogatorio y escala de estrés percibido PSS-14 a los estudiantes de las distintas áreas del Instituto de Ciencias de la Salud (ICSa) para determinar la presencia o ausencia de estrés y síntomas de bruxismo, se utilizó una Chi-cuadrada para la comparación entre variables, considerando significativo un valor de p<0,005, así como ANOVA de dos vías para evaluar la diferencia entre los síntomas antes y durante el aislamiento de la pandemia. De los 825 participantes se obtuvo una muestra final de 420 estudiantes compuesta por 297 (70.72%) mujeres y 123 (29.28%) hombres, con un promedio de 20±1.75 años de edad. Existe una asociación entre la frecuencia de bruxismo y estrés severo generados durante el aislamiento social de la pandemia COVID-19, prevaleciendo percepción alta de estrés en el área de medicina y alta percepción en la frecuencia de síntomas de bruxismo en el área de nutrición p>0.0001. Los estudiantes de 18 a 24 años de edad del ICSa perciben síntomas de bruxismo y altos niveles de estrés originados durante la pandemia.

ABSTRACT Introduction: Differences in the mechanical properties of ceramic and resin-based materials pose the question of which of the two will perform better in the long run. Objectives: Evaluate the flexural resistance and color stability of different indirect esthetic restorative materials. Methods: The materials selected were Filtek™ Z250 XT (3M ESPE), Ceramage (SHOFU Dental), VITA VM® LC and VITA ENAMIC® (VITA Zahnfabrik), IPS e.max® (Ivoclar-Vivadent) and Zolid FX (Amann Girrbach AG). The flexural resistance assay (n = 10) was conducted in a universal mechanical testing machine. Color readings (n = 5) were taken with a VITA Easyshade V® spectrophotometer. Results: All-ceramic materials had better mechanical performance (p < 0.001). Color stability results show that Ceramage, IPS e.max® and Zolid FX displayed a statistically significant difference (p ≤ 0.002) with respect to Filtek Z250 XT, VITA VM® LC and VITA ENAMIC®. Conclusions: All-ceramic materials exhibited greater flexural resistance and color stability than polymer-based materials. However, indirect esthetic materials with polymers in their composition, such as Ceramage, are presented as a valid alternative, due to their appropriate mechanical properties and their color stability, which is similar to that of ceramic materials.

RESUMEN Introducción: Las diferencias en las propiedades mecánicas de los materiales cerámicos y a base de resina plantean la interrogante sobre cuál puede tener un mejor desempeño a largo plazo. Objetivos: Evaluar la resistencia flexural y estabilidad de color de diferentes materiales restauradores estéticos indirectos. Métodos: Los materiales seleccionados fueron Filtek™ Z250 XT (3M ESPE), Ceramage (SHOFU Dental), VITA VM® LC y VITA ENAMIC® (VITA Zahnfabrik), IPS e.max® (Ivoclar-Vivadent) y Zolid FX (Amann Girrbach AG). El ensayo de resistencia flexural (n = 10) fue realizado en una máquina universal de ensayos mecánicos. Las lecturas de color (n = 5) se midieron en un espectrofotómetro VITA Easyshade V®. Resultados: Los materiales totalmente cerámicos mostraron un mejor desempeño mecánico (p < 0,001). Los resultados de estabilidad de color muestran que Ceramage, IPS e.max® y Zolid FX, mostraron una diferencia estadísticamente significativa (p ≤ 0,002) con Filtek Z250 XT, VITA VM® LC y VITA ENAMIC®. Conclusiones: Los materiales totalmente cerámicos presentaron una mayor resistencia flexural y estabilidad de color que los materiales de base polimérica. A pesar de ello, los materiales estéticos indirectos con polímeros en su composición, como Ceramage, se presentan como una alternativa válida, ya que además de tener propiedades mecánicas adecuadas, poseen una estabilidad de color semejante a los materiales cerámicos.

Abstract The objective of this study was to formulate an experimental light-cured periodontal dressing containing alpha-humulene and to compare its physical, antimicrobial, and cytotoxicity properties with commercial gold standards (Barricaid® and Periobond®). Two periodontal dressing formulations were developed (a and b). The formulations were divided into 5 groups according to the alpha-humulene concentration as follows: Ea - control group, Ea1 - 1%, Ea5 - 5%, Ea10 - 10%, and Ea20 - 20%; Eb - control group, Eb1 - 1%, Eb5 - 5%, Eb10 - 10%, and Eb20 - 20%. Materials characterization was performed using the degree of conversion, cohesive strength, sorption, and solubility assays. Antimicrobial assay was performed using the modified direct contact test against E. faecalis and S. aureus. Cytotoxicity was assessed by the cell viability experiment using L929 fibroblasts. In general, the cohesive strength values of materials decreased as the alpha-humulene concentration increased. All the experimental dressings showed antimicrobial activity against both bacteria tested. Cell viability results for the Ea, Ea1, Eb, and Eb1 groups showed moderate cytotoxic effect. The formulations containing alpha-humulene showed similar behavior to the commercial references. Thus, formulations containing alpha-humulene have potential to be used as periodontal dressing.

Abstract The objective of this study was to evaluate the biocompatibility and mechanical properties of two commercially available and one experimental periodontal dressing materials. The cytotoxicity of Periobond ® , Barricaid ® and one experimental periodontal dressing based on Exothane ® 8 monomer was tested on 3T3/NIH mouse fibroblast. Genotoxicity was assessed by micronuclei formation, and cell alterations were analyzed using light microscopy. Both biological assays were performed using the eluate obtained from specimens after 24, 72, or 168 hours of incubation. Mechanical characterization was assessed through the ultimate tensile strength and the water sorption and solubility tests. The significance level of α = 0.05 was used for all statistical analyses. All the materials promoted a cell viability lower than 60% in all evaluated times. In general, the cell viability was significantly reduced after 72 and 168h of specimens’ incubation. Considering the factor material, there were not statistical differences in the cell viability (p = 0.156). The genotoxicity was not statistically significant among the groups in the different periods of time (p > 0.05). Differences in the ultimate tensile strength values were not statistically significant different among the groups (p = 0.125). Periobond ® showed the higher water sorption values (p < 0.001). Regarding solubility, there were no statistical differences between the groups (p = 0.098). All the periodontal dressing materials evaluated in this study exerted a cytotoxic effect against mouse fibroblasts, and their toxicity became more evident over time. Among the materials evaluated, the experimental light-cure type has shown overall similar properties to the commercial references.

Resumen: Objetivos: Evaluar y comparar la relación entre la resistencia de unión inmediata a esmalte y microfiltración de dos sistemas restauradores a base de resina compuesta. Métodos: 40 terceros molares se dividieron aleatoriamente en dos grupos: 20 molares restaurados utilizando el sistema Adper Single bond 2 + Filtek Z250 XT (3M ESPE; ST PAUL, MN, USA); y 20 molares restaurados con el sistema Tetric N Bond + Tetric N Ceram (Ivoclar Vivadent; Schaan, Liechtenstein). La mitad de los dientes de cada grupo se utilizaron para un ensayo de microtracción, mientras que la otra mitad fueron utilizados para un ensayo de microfiltración (n = 10). Resultados: Las medias y el desvío padrón de la resistencia de unión a microtracción fueron de 27.93 (±9.55) para Adper Single bond 2 + Filtek Z250 XT MPa y 33.12 (±8.18) MPa para Tetric N Bond + Tetric N Ceram (p = 0,049). En cuanto a los valores de microfiltración, no hubo diferencias estadísticamente significativas entre los grupos (p = 0,478). No fue observada una correlación significativa entre la resistencia de unión a la microtracción y la microfiltración (R2= 0.0909; p = 0.196). Conclusiones: No se encontró una relación entre los valores de resistencia de unión y el grado de microtracción.

Abstract: Objectives: To evaluate and compare the relationship between enamel bond strength and microleakage of two composite based restorative systems. Methods: 40 third molars were randomly divided into two groups: 20 molars restored with the Adper Single bond 2 + Filtek Z250 XT (3M ESPE; ST PAUL, MN, USA) system and 20 with the Tetric N Bond + Tetric N Ceram (Ivoclar Vivadent; Schaan, Liechtenstein) system. Half of the teeth in each group were used for a bond strength test, while the other half were used for the microleakage test. Results: The means and standard deviation of the bond strength resistance were 27.93 (± 9.55) MPa for Adper Single bond 2 + Filtek Z250 XT system and 33.12 (± 8.18) MPa for Tetric N Bond + Tetric N Ceram system (p = 0.049). Regarding the microleakage values, there were no statistically significant differences between the groups (p = 0.478). No significant correlation was observed between Microtensile bond strength and microleakage (R2 = 0.0909, p = 0.196). Conclusions: It was not found a relationship between adhesive bond values and the degree of microleakage.

Resumo: Objetivos: Avaliar e comparar a relação entre a resistência de união imediata ao esmalte e a microfiltração de dois sistemas restauradores baseados em resina composta. Métodos: 40 terceiros molares foram divididos aleatoriamente em dois grupos: 20 molares restaurados usando o sistema Adper Single bond 2 + Filtek Z250 XT (3M ESPE; ST PAUL, MN, EUA); e 20 molares restaurados com o sistema Tetric N Bond + Tetric N Ceram (Ivoclar Vivadent; Schaan, Liechtenstein). Metade dos dentes de cada grupo foi utilizada para um teste de resistência de união à microtração, enquanto a outra metade foi utilizada para um teste de microfiltração (n = 10). Resultados: As mídias e o padrão de resistência de união à microtração foram 27,93 (± 9,55) para Adper Single bond 2 + Filtek Z250 XT MPa e 33,12 (± 8,18) MPa para Tetric N Bond + Tetric N Ceram (p = 0,049). Em relação aos valores de microfiltração, não houve diferença estatisticamente significativas entre os grupos (p = 0,478). Não houve correlação significativa observada entre a resistência de união à microtração e a microfiltração (R2= 0,0909; p = 0,196). Conclusões: Não foi encontrada relação entre os valores de resistência de união e o grau de microfiltração.

Resumo O objetivo deste estudo foi avaliar a influência de três tratamentos térmicos adicionais de baixo custo, disponíveis no consultório dentário, nas propriedades mecânicas, químicas e ópticas de uma resina composta fotoativada indicada para restaurações diretas porém usada como restaurador indireto. A resina composta direta TPH3 (Dentsply) foi fotoativada usando um diodo emissor de luz e submetida a três tratamentos térmicos adicionais experimentais: forno seco a 170 °C por 5 min, autoclave a 121 °C por 6 min ou forno de micro-ondas a 450 W por 3 min. A resina composta sem qualquer tratamento térmico adicional foi usada como grupo controle negativo. Uma resina composta indireta (Vita CM LC, Vita Zahnfabrik) foi testada como referência comercial. Resistência à flexão, módulo de elasticidade, microdureza, grau de conversão de C=C, rugosidade antes e após abrasão por escovação simulada, parâmetro de translucidez e diferença de cor (ΔE00) foram avaliados. Os dados foram analisados considerando α=0.05. A resina composta indireta apresentou menor conversão de C=C e desempenho mecânico. A resistência à flexão foi significativamente mais alta no grupo forno seco comparado ao controle. A rugosidade não foi diferente entre os grupos antes ou após a escovação, porém os tratamentos térmicos adicionais causaram aumento na conversão de C=C, microdureza e módulo de elasticidade, sem afetar o parâmetro de translucidez ou mostrar alteração de cor visível (ΔE00<1,8). Estes resultados sugerem que o uso de métodos térmicos adicionais de polimerização representam alternativa econômica e simples para aprimorar as propriedades mecânicas e químicas de resinas compostas diretas quando utilizadas como restauradores indiretos.

Abstract The aim of this study was to evaluate the influence of three low-cost additional thermal treatments, available in the dental office, on the mechanical, chemical and optical properties of a light-cured resin composite indicated for direct restorations but used as indirect restorative. The direct resin composite TPH3 (Dentsply) was light-polymerized using a light-emitting diode curing unit and submitted to three experimental additional thermal treatments: dry heat at 170 °C for 5 min, autoclave at 121 °C for 6 min, or microwave oven at 450 W for 3 min. The resin composite without any thermal treatment was used as negative control group. An indirect resin composite (Vita CM LC, Vita Zahnfabrik) was tested as a reference. Flexural strength, elastic modulus, microhardness, degree of C=C conversion, roughness before and after simulated toothbrush abrasion, translucency parameter and color difference (ΔE00) were evaluated. Data were analyzed at α=0.05. The indirect resin composite presented lower C=C conversion and mechanical performance. The flexural strength was significantly higher in the dry oven group compared with the control. The roughness was not different among groups before or after brushing, but the thermal treatments caused an increase in C=C conversion, microhardness, and elastic modulus without affecting the translucency parameter or showing visible color alteration (ΔE00<1.8). These results suggest that the use of additional thermal methods of polymerization represents an economical and simple alternative to enhance the mechanical and chemical properties of direct resin composites when used as indirect restoratives.

Abstract Currently, there is no consensus in terms of defining the minimum radiant exposure values necessary for achieving adequate properties of composite resin. In addition, the long-term influence that radiant exposure has on the properties of composite resins is still questionable. Objective: The objective of this study was to evaluate the effect of radiant exposure and UV accelerated aging on the physico-chemical and mechanical properties of micro-hybrid and nanofilled composite resins. Material and Methods: A nanofilled (Filtek Supreme; 3M ESPE) and a micro-hybrid composite resin (Filtek Z250; 3M ESPE) were investigated under different radiant exposures (3.75, 9, and 24 J/cm2) and UV accelerated aging protocols (0, 500, 1000, and 1500 aging hours). The degree of conversion (DC), flexural strength (FS), modulus (M), water sorption (WS), and solubility (WL) were evaluated. The results obtained were analyzed using two-way ANOVA and Tukey's test. Comparisons were performed using a significance level of α=0.05. Results: The DC, FS, and M were found to be significantly influenced by both radiant exposure and accelerated aging time. The DC and EM increased with radiant exposure in the no-aging group (0-hour aging) for both micro-hybrid and nanofilled composites, whereas no correlation was found after accelerated aging protocols. WS and WL of micro-hybrid and nanofilled composite resins were scarcely affected by radiant exposure (p>0.05), whereas they were significantly reduced by accelerated aging (p<0.001). Conclusions: Although increasing radiant exposure affected the degree of conversion and mechanical properties of micro-hybrid and nanofilled composites, no influence on the hydrolytic degradation of the material was observed. In contrast, UV accelerated aging affected both the physico-chemical and mechanical properties of the composites.