This study evaluated the effect of antioxidant agents on microtensile bond strengths (mTBS) of composite to bleached enamel. Fifteen freshly extracted human third molars were selected and randomly assigned to 6 groups (n = 5): (NB) enamel not bleached, (B) bleached enamel, (BR7) bleached enamel and restored 7 days later, (BSA) bleached enamel+sodium ascorbate, (BMC) bleached enamel+malvidin chloride, (BPC) bleached enamel+pelargonidin chloride. The groups were bleached with 38% hydrogen peroxide (HP - Opalescence Xtra Boost) and restored with Single Bond+Filtek Z350. The specimens were thermocycled and submitted to a microtensile load at 1 mm/min crosshead speed. The data were evaluated by ANOVA and Tukey test at 5% of significance. The mean and standard-deviation for all groups were: NB: 30.95(±11.97)a; BSA: 30.34(±8.73)a, BPC: 22.81(6.00)b, BR7: 21.41(±6.12)b, B: 14.10(±4.45)c, BMC: 13.25(±6.02)c. Sodium ascorbate reversed the bond strengths to enamel immediately after bleaching.

OBJETIVO: Esta pesquisa verificou os efeitos da tecnologia Grander na alteração da tensão superficial e ângulo de contato de um sistema adesivo autocondicionante. METODOLOGIA: O sistema adesivo autocondicionante Xeno III (Dentsply) e a água destilada foram modificados pelo contato físico com a unidade flexible do sistema Grander para revitalização de águas por 48 horas, resultando em 4 grupos: Grupo 1 - sistema adesivo Xeno III em condições de normalidade; Grupo 2 - sistema adesivo Xeno III modificado pelo sistema Grander; Grupo 3 - água destilada em condições de normalidade; Grupo 4 - água destilada modificada pelo sistema Grander. A tensão superficial dos líquidos foi verificada em goniômetro utilizando cinco medidas para cada gota de líquido. O ângulo de contato foi medido com o goniômetro sobre os substratos placa de titânio e dentes bovinos. Os dados foram submetidos aos testes ANOVA e Tukey (5%). RESULTADOS: Houve redução significativa da tensão superficial da água com a modificação pelo sistema Grander. Não houve redução da tensão superficial e ângulo de contato para o sistema adesivo Xeno III. CONCLUSÃO: A tecnologia Grander não interferiu com a tensão superficial e o ângulo de contato para o sistema adesivo Xeno III.

PURPOSE: The objective of this study was to evaluate the influence of the Grander technology in reducing the surface tension and contact angle of a self-etch adhesive system. METHODS: Distilled water and Xeno III self-etch adhesive system (Dentsply) were modified by physical contact with the Flexible unit Grander system to revitalize water, for 48 hours, resulting in four groups: Group 1 - Xeno III under normal conditions; Group 2 - Xeno III modified by Grander; Group 3 - distilled water under normal conditions; Group 4 - distilled water system modified by the Grander system;. Surface tension and contact angle (dentin substrate and titanium plate) of the adhesive system and water in normal and Grander-modified conditions was measured with a goniometer. Data were analyzed by ANOVA and Tukey test (5%). RESULTS: Grander technology reduced the surface tension of water but not of the adhesive system Xeno III. The contact angle property of the adhesive ystem was not affected. CONCLUSION: Grander technology did not interfere with the surface tension and contact angle physical properties of the Xeno III self-etch adhesive system.