Titanium oxides such as rutile and anatase, are materials that stand out for exhibiting properties that act in biomedical and photocatalytic applications, among others. It is extreme importance to idealize new techniques that produce such compounds, being indispensable the improvement of characterizations for these materials. For this purpose, titanium comercially pure (CP) grade II cylindrical samples were oxidized ionically using titanium cage electric shields, oxidized at 350 ° C in 3 and 8 hours. Through Grazing Incidence X-ray Diffraction (GIXRD) analysis, was observed on the surface of the treated samples the formation of a TiO2 film with the anatase, rutile and brookite phases, the latter phase cited being difficult to produce in conventional thermochemical treatments. All samples treated showed a significant increase in wettability using distilled water. The higer value was for the sample with a 8 hours treatment time, in which this condition presented phases with greater intensity in the analysis of GIXRD

This research used the "cathodic cage (CC)" technique for TiO2 film deposition on duplex stainless steel substrate. This technique uses a multiple hollow cathode effect. Duplex stainless steel substrates were treated at temperatures of 300°C, 350°C and 400°C, giving a temperature value ratio (Ts/Tm) of 0.27 to 0.31 (Ts being the substrate temperature and Tm the melting temperature of the deposited material). Treatment times of 1, 2 and 4 hours were administered and polycrystalline TiO2 films were obtained. The films were analyzed by optical microscopy (OM), X-ray diffraction (XRD), Raman spectroscopy and scanning electron microscopy (SEM). During analysis, the formation of uniform films and the possibility of controlling the TiO2 phase were observed. It was also shown that with longer treatment times and higher temperatures the rutile phase predominates. For treatment times of 4 hours at all temperatures, the rutile structure was present. With treatment times of less than 4 hours, anatase was present. In addition, results showed that this simple, low cost technique can be an alternative method for depositions of TiO2 films, with the advantage of high levels of control over porosity, thickness and phase composition (anatase and rutile).

Thin nitride and titanium dioxide films were produced using an innovative technique called cathodic cage depositon. Uniformity, three-dimensionality and high rate deposition are some of the advantages of this technique. In this study we discuss the influences of temperature, treatment time and gaseous atmosphere on the characteristics of the deposited films. The TiN (titanium nitride) and TiO2 (titanium dioxide) films were produced using a high deposition rate of 2,5 µm/h at a work temperature and pressure of 400°C and 150 Pa respectively. EDS technique was used to identify the chemical composition of the thin film deposited, whilst Raman spectroscopy indicated the phases present confirmed by DRX analysis. The thickness of the deposited films was studied using electron microscopy scanning. The results based on the deposition parameters confirm the great efficiency and versatility of this technique, which allows a uniform three-dimensional film deposition on any material without the appearance of stress. Compared to other techniques, cathodic cage deposition enables deposition at lower temperatures and higher pressures.

AISI 409 ferritic stainless steel samples were nitrided using the cathodic cage plasma nitriding technique (CCPN), with the addition of methane to reduce chromium precipitation, increase hardness and wear resistance and reduce the presence of nitrides when compared to plasma carbonitriding. Microhardness profiles and X-Ray analysis confirm the formation of a very hard layer containing mainly ε-Fe3N and expanded ferrite phases.