To solve chipping of veneer porcelain in zirconia dental prosthesis it has been studied different cooling rates in firing schedules to control residual stresses generated by differences in thermal properties between the ceramics. However, cooling rates may affect the porcelain, irrespectively of interaction with zirconia. This study analyzed the effect of cooling rate on the three-point flexural strength (FS), residual stress, Vickers hardness (VH) and V-notch fracture toughness (SEVNB) on a feldspathic porcelain (Vita VM9) indicated for covering zirconia. Bar-shaped specimens were sintered according manufacturer's schedule firing and cooled at different rates (slow, normal or fast). Specimens were tested for FS (n=30), VH (n=15) and SEVNB tests (n=15). Weibull analysis were performed from FS values to measure reliability and probability of failure (PF). One-way ANOVA was significant for VH (p<0.001), and Tukey's test showed that slow cooling led to higher values. There was no significant difference for FS (p=0.654) and SEVNB (p=0.734). Fast cooling led to the lowest PF, but cooling rate factor was not significant for Weibull modulus. All cooling group showed residual tensile stress (MPa): Slow = 34.81; Normal = 27.04; Fast = 18,98. It was concluded that cooling rate produce minor changes in the porcelain properties.

ZrO2(Y2O3)-based ceramics are widely used as biomaterials due to high fracture toughness, resulting from the tetragonal-monoclinic phase transformation in which the ceramic is submitted during crack propagation. In this context, studies involving the possibility of optimization of the tetragonal phase are important for the properties improvement of this ceramic. This study investigated the recovery of tetragonal phase from a previously transformed ZrO2(3 mol% Y2O3) ceramic. Zirconia samples were sintered at 1450 °C, at 1530 °C - 2 h and at 1600 °C - 4 h, in order to obtain materials with distinct microstructural features. The sintered samples were characterized by relative density, X-ray diffraction and scanning electron microscopy. Samples sintered at 1450 °C, 1530 °C - 2 h and 1600 °C - 4 h, presented relative densities of 94.2, 99.6 and 99.7% with grains size averages of 0.28, 0.49 and 1.31 µm, respectively. All samples were submitted to milling to induce the tetragonal→monoclinic phase transformation presenting 5, 50 and 65 vol% of monoclinic phase. Subsequently, heat treatments between 400 °C and 1200 °C were conducted to retransform monoclinic in tetragonal phase. It has been found that the smaller the grain size after sintering, the lower the necessary annealing temperatures for fully recovering of tetragonal phase. Annealing temperatures of 950, 1100 and 1200 °C were sufficient to recover almost fully the tetragonal phase.

Este estudo investigou o efeito do peróxido de carbamida a 16% (Whiteness Perfect/FGM) na dureza Vickers e resistência à flexão dos compósitos restauradores Filtek Z100 (híbrida), Filtek Z350 (nanoparticulada), Brilliant (micro-híbrida) e Opallis (micro-híbrida). Espécimes em forma de disco (4x2 mm; n=5) e de barra (12x2x1 mm; n=10) de cada material restaurador foram distribuídos aleatoriamente em 2 grupos: (G1) 16 semanas em água destilada; (G2) armazenamento em água destilada durante 16 semanas, com aplicação do peróxido de carbamida a 16% por 6 h diárias nas últimas 4 semanas. As propriedades mecânicas foram avaliadas em microdurômetro Vickers e máquina de ensaios mecânicos. Os dados foram analisados por ANOVA a 2 critérios e teste de Tukey (α=0,05). Filtek Z100 apresentou o maior valor de dureza, seguido por Filtek Z350 e, finalmente, por Brilliant e Opallis (p=0,00). Filtek Z100 e Brilliant mostraram o maior valor de resistência à flexão, seguido por Filtek Z350 e Opallis (p=0,00). O clareamento diminuiu significantemente a dureza das resinas Brilliant e Opallis (p=0,00). A resistência à flexão dos materiais estudados não foi afetada pelo clareamento caseiro (p=0,28).

This study investigated the effect of 16% carbamide peroxide (Whiteness Perfect/FGM) on the Vickers microhardness and flexural strength of the restorative composites Filtek Z100 (hybrid), Filtek Z350 (nanofill), Brilliant (micro-hybrid) and Opallis (micro-hybrid). Disc-shaped (4x2 mm; n=5) and bar-shaped (12x2x1 mm; n=10) specimens of each restorative material were randomly divided into 2 groups: (G1) 16 weeks stored in distilled water; (G2) 16 weeks stored in distilled water, with 16% carbamide peroxide application during 6 h per day for the last 4 weeks. The mechanical properties were evaluated using a Vickers microhardness tester and a mechanical testing machine. Data were analyzed by two-way ANOVA and Tukey's (HSD) post-hoc test (α=0.05). Filtek Z100 presented the highest microhardness value, followed by Filtek Z350 and finally by Brilliant and Opallis (p=0.00). Filtek Z100 and Brilliant exhibited the highest flexural strength value, followed by Filtek Z350 and Opallis (p=0.00). Bleaching treatment decreased significantly microhardness of Brilliant and Opallis (p=0.00). The flexural strength of all studied materials was not affected by the home bleaching (p=0.28).