Abstract This study aimed to produce soil-cement brick with wood ash incorporation coming from the textile industry. The wood ash was a partial substitute for soil and cement in the manufacture of bricks. 7 formulations were made with different proportions of substitution: 10%, 20%, and 30%. It was noticed that the substitution of cement by wood ash in 10% resulted in brick with enhanced properties, showing a 20% increase for compressive strength and a reduction of 44% for mass loss, thus, with higher durability and a reduction of water absorption of 3%, when comparing to the reference brick (soil-cement). It was shown that the reuse of wood ash in the production of soil-cement bricks is a viable and sustainable option, as it is an alternative for the destination of the waste and a reduction in the consumption of Portland cement, which generates a high volume of carbon dioxide (CO2) during its production.

Resumo O presente trabalho avaliou os parâmetros de corrosão das barras de aço revestidas com Zinco (Zn) e com a liga Zinco-Níquel (Zn-Ni), por eletrodeposição, comparando-as com as tradicionalmente utilizadas, sem revestimento. Para isso, utilizaram-se amostras de concreto armado que foram submetidas a ensaios acelerados de corrosão por ação de cloretos (câmara de névoa salina – “salt spray” e ciclos de imersão e secagem). O potencial de corrosão das armaduras foi medido para monitoramento qualitativo do processo e, após o fim dos ensaios, estimaram-se as taxas de corrosão das barras, através da perda de massa, para análise quantitativa. As barras revestidas com Zn e Zn-Ni se mostraram mais resistentes à corrosão, quando comparadas com as barras convencionais, em ambientes com forte ação de cloretos e o envelhecimento por ciclos se mostrou muito mais eficiente na aceleração do processo de corrosão.

Abstract This paper shows the analysis performed on the corrosion parameters of three groups of reinforcing steel bars, two of these coated by electroplating process with Zinc (Zn) and Zinc-Nickel (Zn-Ni), and the other without any coating. It was used reinforced concrete specimens, which ones were grouped and then subjected to two different corrosion accelerating methods: aging wetting/drying cycles and salt spray exposure. Corrosion potential was measured to qualitative monitoring of the process and, after the end of the tests, corrosion rate was estimated by measuring the mass loss, to quantitative analyses. As it was expected, coated bars presented a better performance than the average bars regarding the corrosion resistance in chloride ions containing environments. It was also observed that the drying/ NaCl solution wetting cycles seems to be more severe than salt spray fog apparatus with respect to the acceleration of corrosion process.

Os modelos de bielas e tirantes são procedimentos de análise apropriados para projetar elementos de concreto armado em casos de regiões onde há alterações geométricas ou concentrações de tensões, denominadas regiões "D". Trata-se de bons modelos de representação da estrutura para avaliar melhor o seu comportamento estrutural e seu mecanismo resistente. O presente artigo aplica a técnica da otimização topológica para identificar o fluxo de tensões nas estruturas, definindo a configuração dos membros de bielas e tirantes, e quantifica seus valores para dimensionamento. Utilizam-se o método ESO, e uma variante desse, o SESO (Smoothing ESO) com o método dos elementos finitos em elasticidade plana. A filosofia do SESO baseia-se na observação de que se o elemento não for necessário à estrutura, sua contribuição de rigidez vai diminuindo progressivamente. Isto é, sua remoção é atenuada nos valores da matriz constitutiva, como se este estivesse em processo de danificação. Para validar a presente formulação, apresentam-se alguns exemplos numéricos onde se comparam suas respostas com as advindas de trabalhos científicos pioneiros sobre o assunto.

The strut-and-tie models are appropriate to design and to detail certain types of structural elements in reinforced concrete and in regions of stress concentrations, called "D" regions. This is a good model representation of the structural behavior and mechanism. The numerical techniques presented herein are used to identify stress regions which represent the strut-and-tie elements and to quantify their respective efforts. Elastic linear plane problems are analyzed using strut-and-tie models by coupling the classical evolutionary structural optimization, ESO, and a new variant called SESO - Smoothing ESO, for finite element formulation. The SESO method is based on the procedure of gradual reduction of stiffness contribution of the inefficient elements at lower stress until it no longer has any influence. Optimal topologies of strut-and-tie models are presented in several instances with good settings comparing with other pioneer works allowing the design of reinforcement for structural elements.

Estudou-se a exigência de proteína bruta e energia metabolizável para codornas européias em crescimento, em cinco períodos experimentais, de sete dias cada. Foram utilizadas 384 codornas de ambos os sexos, com sete dias de idade em delineamento experimental utilizado inteiramente ao acaso, em esquema fatorial de 2×4, dois níveis de energia (2900 e 3100kcal de EM/kg de ração) e quatro níveis de proteína (22, 24, 26 e 28% de PB), com seis repetições de oito animais cada. Foram estudadas as variáveis ganho de peso (g), peso acumulado (g), consumo de ração (g) e conversão alimentar (g de ração/g de peso). Observou-se efeito linear dos níveis de proteína no primeiro período e quadrático nos demais períodos sobre o ganho de peso das aves. Os níveis de proteína foram estimados em 28,0% (2900kcal de EM/kg), 25,7% (3100kcal de EM/kg), 27,9%, 24,8% (3100kcal de EM/kg) e 23,1% (2900kcal de EM/kg) para o segundo, terceiro, quarto e quinto período, respectivamente.

Crude protein (CP) and metabolizable energy (ME) levels during five experimental periods of seven days each of the growing phase for European quail were determined. A total of 384 quails of both sexes were used in a completely randomized design in a 2×4 (energy and crude protein) factorial treatment with six replications of eight quails each. The metabolizable energy levels were 2900 and 3000kcal of ME/kg of diet and the crude protein levels were 22, 24, 26 and 28%. The analyzed variables were weight gain (g), accumulated weight (g), feed consumption (g), feed:gain ratio (g/g). Performance responses were evaluated by linear and quadratic regression of the traits on crude protein levels. Higher weight gains from the following protein and metabolizable energy levels combinations: 28.0% PB and 2900 kcal EM/kg (first period); 25.7% CP and 3100kcal ME/kg (second period); 27.9% and 2900kcal ME/kg (third period); 24.8% PB and 3100kcal/kg (fourth period) and 23.1% CP and 2900kcal/kg (fifth period).

Estudou-se a exigência de metionina + cistina total para codornas de corte em crescimento durante os períodos inicial (sete a 21 dias) e final (22 a 42 dias de idade). O delineamento experimental foi inteiramente casualizado, com cinco repetições de 13 codornas por unidade experimental. Os tratamentos consistiram de seis níveis de metionina + cistina total (0,73; 0,79; 0,85; 0,91; 0,97 e 1,03%). Foram estudadas as variáveis: ganho de peso (g), peso final no período (g), consumo de dieta (g) e conversão alimentar (g de dieta/g de peso). As respostas de desempenho foram obtidas por meio de modelos de regressão linear e quadrática. Codornas de corte alimentadas com dietas contendo 0,95% de metionina + cistina total no período inicial (sete a 21 dias) e 0,73% de metionina + cistina total no período final (22 a 42 dias) de criação obtêm máximo ganho de peso.

Total methyonine + cystine requirements during the initial (7-21 days of age) and final period ( 22-42 days of age) of the growing phase were estimated for meat type quails in a completely randomized experimental design with six treatments, five replicates and 13 quails per experimental unit. Weight gain (g), body weight (g), feed consumption (g) and feed : weight gain ratio (g/g) were evaluated for quails fed on .73, .79, .85, .91, .97 and 1.03% methyonine + cystine diets. Meat type quails fed .95% and .73% methyonine + cystine diets during the initial (7-21days of age) and final period (22-42 days of age) of the growing phase show maximum weight gain.