ABSTRACT Ischemia-reperfusion injury was seen in strokes, myocardial infarctions, acute kidney injury, mesenteric ischemia, liver and systemic shock. Renal ischemia-reperfusion is more importance in the setting of kidney transplantation that affects distant organs. In this study forty Male Albino Wistar rats (200-250g) were randomly divided in four group (n=10) including control, sham operation group, nephrectomy and IRI group. All rats anesthetized with intraperitoneal injection of ketamine (50 mg/kg) and xylazine (10 mg/kg) and maintained the core body temperature at approximately 37°C. For inducing IRI group, it was performed right nephrectomy, and in continuing, the left kidney pedicle occluded to 45 min via nontraumatic microvascular clamp for making ischemia that followed 24 hours reperfusion. TUNEL assay was used to detect the cardiac apoptotic cells. Hematoxylin-Eosin staining and periodic acid-Schiff (PAS) procedure was used to histopathological assessment and glycogen accumulation respectively. There was more heart damage at 24 h reperfusion in IRI group. Renal IRI group showed myocardial degeneration, necrosis and increasing connective tissue in myofibril. There were apparent hypertrophy and swelling of myofibril, fragmentation and vacuolization of sarcoplasm. In addition, it was shown elevated apoptotic cell at 24 hours reperfusion in renal IRI group than sham group. There were increases of glycogen accumulation in cardimyocyte of renal IRI group. Our findings suggest that renal IRI-induced cardiac damage, accompanied by an accumulation of glycogen granules, induced apoptosis and histological changes in cardiomyocytes.

The potential use of nanoclay was examined to modify fluid transfer properties of medium density fiberboard (MDF). For this, Na+ montmorillonite (Na+MMT) nanoclay was added to urea formaldehyde resin to produce MDF. Then, the air permeability and mass diffusivity of MDF were evaluated. Scanning electron microscope (SEM) images and X-ray diffraction (XRD) confirmed a dispersion and exfoliation of Na+MMT in the modified MDF. The air permeability presented a systematic decrease with increasing nanoclay amount. This reduction agreed with the simple ‘‘tortuous path’’ model. The nanoclay had no effect on the mass diffusivity.