Abstract Plywood panel has a promising market in Wood Frame Construction System. Like any wood-based product, it can suffer deterioration, and preservative treatment is imperative. The preservative treatment can be done directly on a pressed panel - a conventional method that supposedly causes a decrease in physical-mechanical performance - or incorporated into the production process, by the previous treatment of veneers to develop panels with durability and quality. We compared the performance of these two processes. Panels were produced with Pinus taeda L., using 360 g m-2 of phenolic adhesive in a double line, a pre-pressing and hot pressing for 20 minutes under 1.2 MPa pressure and 130°C and treatement on veneers and panels with CCA-C. Tests followed Brazilian standards. Panels with previous treatment had lower water absorption and swelling. Preservation of the veneers also promoted higher retention levels and better penetration of preservatives. Both treatments did not affect the mechanical performance.

ABSTRACT Latex is the main product extracted from rubber trees (Hevea brasiliensis). In Brazil, at the end of the production cycle of latex, the wood of rubber tree is traditionally used for energy purposes, but several international studies have reported consolidated practices of adding value to it. The objective of this paper was to evaluate the quality of wood and classify it structurally based on its mechanical properties. Six 20-year-old trees of the clone GT 1 of rubber tree proceeding from Itajobi, State of Sao Paulo, Brazil were sampled. Reduced dimensions specimens in the radial direction of the wood were produced to evaluate the quality by compression parallel to the grain, static bending and Janka hardness tests. Two specimens, one from the lower log (since the ground up to breast height) and one from the higher log (from breast height up to 2.50 m) were produced for structural classification of the wood based on the characteristic strength in compression parallel to the grain (NBR 7190 norm, 1997). The wood was classified as C40 (fc0k ≥ 40 MPa) class. Results revealed that the strength was not statistically different in the radial direction (except for the Janka hardness), though tending to increase from pith to bark.

RESUMO O látex é o principal produto extraído das árvores de seringueira (Hevea brasiliensis). No Brasil, ao final do ciclo produtivo de látex, a madeira dessas árvores é utilizada tradicionalmente para fins energéticos, mas diversos trabalhos internacionais relatam práticas consolidadas de agregação de valor a ela. O objetivo deste trabalho foi avaliar a qualidade da madeira e classificá-la estruturalmente a partir de propriedades mecânicas do lenho de árvores do clone comercial GT 1 de seringueira. Foram utilizadas seis árvores provenientes de plantio de 20 anos de idade da cidade de Itajobi-SP. Da tora inferior (desde a base até a altura do DAP), foram produzidos corpos de prova de dimensões reduzidas, na direção radial do lenho, para avaliação da qualidade pelos ensaios de compressão paralela às fibras, flexão estática e dureza Janka; da tora superior (do DAP até a altura de 2,50 m), foram produzidos dois corpos de prova por árvore, para a classificação estrutural baseada no ensaio de compressão paralela às fibras (NBR 7190, 1997 (ABNT, 1997)). A madeira foi classificada estruturalmente como classe C40. Os resultados revelaram que a resistência não apresentou diferença estatisticamente significativa na direção radial (a menos da dureza Janka), sendo observada, no entanto, tendência de aumento no sentido medula-casca.

ABSTRACT After concluding the main phase of commercial exploration of latex (about 30 years ago), rubber wood plantations can be utilized as an alternative source of wood for sawmills and other wood based products with more aggregate value; tendency already confirmed in countries of southeastern Asia. The main purpose of this research was to evaluate the influence of dynamic modulus of elasticity veneers on the mechanical performance in the bending of plywood made from Hevea brasiliensis. For this study, rubber tree veneers were sorted in three classes of dynamic modulus of elasticity: low (from 4887-7323 MPa), medium (from 8200-8948 MPa) and high (from 10979-13010 MPa). Panels were produced according to five treatments with different veneer classes and arrangements. Results showed significant effect of the treatments in the mechanical performance in the bending of panels. Panels with better mechanical performance were produced exclusively with medium and high dynamic modulus of elasticity. Panels made with low modulus of elasticity veneers presented lower mechanical performance even when combined with high modulus of elasticity veneers.

RESUMO Depois de concluída a fase principal de exploração comercial do látex (cerca de 30 anos), os plantios de seringueira apresentam-se como fonte alternativa de madeira para serraria e para outros produtos à base de madeira com valor agregado superior ao da lenha, tendência já consagrada em países do sudeste asiático. O presente trabalho teve como objetivo principal avaliar a influência do módulo de elasticidade dinâmico (Ed) das lâminas no desempenho mecânico à flexão de painéis compensados de Hevea brasiliensis. Para este estudo, as lâminas de seringueira foram selecionadas em três classes de módulo de elasticidade dinâmico, definidas como baixo (de 4887-7323 MPa), médio (de 8200-8948 MPa) e alto (de 10979-13010 MPa) módulo de elasticidade. Foram confeccionados painéis compensados com cinco tratamentos, variando-se as classes das lâminas utilizadas e seus arranjos. Os resultados obtidos revelaram influência significativa dos tratamentos na resistência à flexão dos painéis. Os painéis com melhor desempenho mecânico foram confeccionados exclusivamente com lâminas de alto e médio módulo de elasticidade dinâmico. Os painéis que utilizaram lâminas com baixo módulo de elasticidade apresentaram menor desempenho mecânico, mesmo quando elas estavam combinadas com lâminas de alto módulo.

RESUMO O presente trabalho teve como objetivo principal avaliar as propriedades físicas e mecânicas de painéis LVL (Laminated veneer lumber) confeccionados com lâminas de Eucalyptus grandis, provenientes de reflorestamentos da região de Sengés, Paraná - Brasil. Foram confeccionados painéis LVL de 23 lâminas, de dimensões comerciais de 2500 mm de comprimento, 1200 mm de largura e espessura nominal de 50 mm (lâminas de 2,4 mm). Em vigas retiradas dos painéis LVL foram analisadas as propriedades de flexão estática (rigidez e resistência), nas condições de menor inércia (flatwise) e de maior inércia (edgewise), compressão paralela, cisalhamento paralelo nos planos L-X e L-Y e densidade, atendendo às prescrições das normas ASTM-D 5456/4761 e ASTM-D 198/143. Os valores médios obtidos para o módulo de elasticidade e resistência à flexão estática foram, respectivamente, 13114 MPa e 88,76 MPa para o ensaio na condição de menor inércia e de, respectivamente, 15871 MPa e 88,63 MPa para o ensaio na condição de maior inércia. A densidade aparente (a 12% de umidade) dos painéis LVL e das lâminas foram, respectivamente, 690 kg/ m3 e 649 kg/m3. Os valores médios obtidos nos ensaios de compressão paralela foram 16856 MPa para o módulo de elasticidade e 58,05 MPa para a resistência. Os valores médios da resistência no ensaio de cisalhamento paralelo no plano L-Y e no plano L-X foram 5,96 MPa e 5,91 MPa, respectivamente. Todos esses valores atingiram parcialmente ou ultrapassaram os limites médios de referência estabelecidos para painéis LVL e para a madeira sólida originária, atestando, sobretudo, a qualidade dos painéis produzidos com essa madeira.

ABSTRACT This paper mainly aimed to evaluate the physical and mechanical properties of LVL panels made from Eucalyptus grandis, from reforestation at the region of Sengés, in Paraná state, Brazil. LVL panels were manufactured using 23 veneers (2,4mm thick each one) in commercial dimension of 2.500 mm long and 1,200 mm wide. The properties of static bending were analyzed (strength and rigidity) in beams of the LVL, in the flatwise and edgewise positions. The properties of compression parallel to grain and shear parallel in the plans L-X and L-Y and density in this LVL panels were also analyzed according to ASTM-D 5456/4761 and ASTM-D 198 codes. The mean values to flatwise bending MOE and MOR were 13114 MPa and 88.76 MPa, respectively, and for edgewise bending MOE and MOR were 15871 MPa and 88.63 MPa, respectively. The density (12%) of the LVL panels and of the veneers were 690 kg/m3 and 649 kg/m3. The mean values to parallel compression MOE and MOR were 16856 MPa and 58.05 MPa, respectively. The mean values of the maximum resistance to shear parallel in the plans L-X and L-Y were 5.96 MPa and 591 MPa, respectively. All these values reached partially or they passed the medium limits of reference (normative codes, researches and commercial catalogs) established for LVL panels and original solid wood, attesting overall the quality of those panels produced with this wood.

O objetivo do presente trabalho foi o estudo da variabilidade das propriedades de resistência e rigidez à flexão estática e à densidade aparente (12%) entre a madeira juvenil e adulta de Pinus taeda L., de 37 anos de idade, procedente do Horto Florestal de Manduri, Estado de São Paulo. Na primeira parte do trabalho foram determinadas a região de madeira juvenil, a região de transição e a região de madeira adulta, por meio de estudos anatômicos (comprimento dos traqueídes axiais), segundo as recomendações das normas ABNT e IAWA. Os resultados mostraram que a região de madeira juvenil dessa espécie ocorre aproximadamente até o 18º anel de crescimento. Na segunda parte do trabalho foram analisados a resistência (módulo de ruptura - MOR) à flexão, o módulo de elasticidade (MOE) nessa mesma solicitação e a densidade aparente (12%) para as madeiras juvenil e adulta. Os resultados mostraram que o MOE e o MOR da madeira juvenil foram menores e mais variáveis que aqueles obtidos para madeira adulta. A densidade apresentou a mesma tendência observada nas propriedades avaliadas no ensaio de flexão estática.

This paper aimed to study the variability on rigidity (MOE) and strength (MOR) properties in static bending and density (12 %) between juvenile and mature wood of 37-year-old Pinus taeda L. trees from Horto Florestal, Manduri, Sao Paulo, Brazil. In the first part of the experimental program, the juvenile, transition and mature wood zones were determined using anatomical analysis (tracheids length) according to the ABNT and IAWA codes. Results showed that juvenile wood zone occurs approximately up to the 18th growth ring. In the second part of the experimental setup, bending tests were performed with both juvenile and mature wood samples gathered in two distinct groups to obtain their modulus of rupture - MOR, modulus of elasticity -MOE and density (12%). Results showed that MOE and MOR of juvenile wood were always smaller and presented more variability, when compared to mature wood. Density at 12% showed the same tendency observed in the mechanical tests.

RESUMO O presente trabalho teve por objetivo a determinação de relações entre as propriedades de resistência e rigidez à flexão estática e a massa especifica de painéis compensados de 5 lâminas feitos de madeira de Pinus elliottii Engelm, proveniente de plantios de 30 anos de idade. Foram estudadas várias relações lineares simples, múltiplas e polinomiais, envolvendo o módulo de ruptura (MOR), o módulo de elasticidade (MOE), a tensão no limite proporcional (TLP) e a massa específica (Me) dos compensados. A massa específica mostrou não ser indicador muito preciso das propriedades de resistência e rigidez dos painéis. As propriedades dos compensados à flexão estática, em termos de MOE, MOR e TLP mostraram baixos coeficientes de correlação e determinação ajustados por regressão linear simples, indicando pouca dependência de massa específica. O módulo de ruptura à flexão nas direções principais (x e Y), teve uma forte dependência do módulo de elasticidade e de tensão no limite proporcional. Os coeficientes de correlação dos melhores modelos de regressão nas duas direções variaram de 0,85 a 0,91, Histogramas de frequência da massa específica dos compensados mostraram uma distribuição unimodal homogênea, enquanto que o MOE e o MOR apresentaram uma distribuição unimodal com assimetria positiva.

ABSTRACT The objetive of this work was to determine the relation between the rigidity and strength properties in static bending and specific gravity of plywood manufactured from five veneers of Pinus elliottii Engelm from 30 year-old plantations. Linear simples, multiple and polynomial relations involving the modulus of rupture (MOR), modulus of elasticity (MOE), stress at proportional limit (TLP) and specific gravity (Me) of the plywood were studied. The specific gravity did not prove to be a very exact indicator of the rigidity and strength properties of the plywood. The MOE, MOR and TLP in static bending of the plywood showed low coefficients of correlations and determination adjusted for simple linear regression, indicating a little dependence of the specific gravity, the modulus of rupture in static bending on the principal directions (X and Y) had a strong dependence of the modulus of elasticity and stress at proportional limit. The coefficients of correlations of the best models of regression in the two directions varied from 0.85 to 0,91. The frequency histograms of the specific gravity of plywood showed a unimodal homogeneous distribution, while MOE and MOR showed a unimodal distribution with positive asymmetric skewness.