Abstract A silane coupling agent, namely γ-aminopropyltriethoxysilane (APS), was used to modify kenaf powder (KP). It was then used as filler in a thermoplastic elastomer (TPE) based on Recycled High Density Polyethylene/Natural Rubber Blends (rHDPE/NR). The attachment of silane onto KP was verified by Fourier Transform Infrared Spectroscopy (FTIR), while the performance of the TPE was assessed in terms of mechanical and thermal properties. The results revealed that specific functional groups of APS were efficiently grafted onto the KP. Tensile strength was improved by the modification with silane and this also affected Young’s modulus of the TPE. Also, improved thermal stability was confirmed by thermogravimetric analysis (TGA), as the degradation temperature increased upon inclusion of silane. These effects are attributed to improved compatibility of the KP and rHDPE/NR blend. Such compatibilizing effect was confirmed by Differential Scanning Calorimetry (DSC) that indicated significantly increased crystallinity after the modification with silane.

Abstract Recycling of plastic waste is considered a key intention in regards to the continuous growth of plastic industry. In this work, new composite based on recycled polystyrene (R-PS) was prepared in the presence of eggshell powder (ESP). This was to make a value-added plastic material based on polystyrene. To further extend its performance, calcium carbonate (CaCO3) was used as secondary filler to optimize its performance. It is observed that the stabilization torque of composites decreased with increasing the weight percent of CaCO3. Increasing the amount of CaCO3 has increased the mechanical properties such as Young’s modulus, tensile strength, elongation at break and impact strength of the composites. These findings corresponded well to SEM images. It revealed homogenous dispersions of CaCO3 throughout R-PS matrix in comparison to ESP alone which formed agglomerations in R-PS matrix. Further evidence on thermal stability has confirmed that CaCO3 provided better heat resistance over the ESP.

Abstract Recycling of rubber waste and finding the effective methods to extend its use are one of major challenges nowadays. In the present study, waste natural rubber glove (wNRg) was used in an attempt to extend its use and create a value-added composite based on natural rubber (NR) and wNRg. Another interesting focus was to develop such material into a new Magnetorheological Elastomer (MRE). This MRE can be prepared by incorporating Ferromagnetic particles namely carbonyl iron (CI) to the rubber composite. Carbon black (CB) was also added to obtain MRE with remarkably mechanical properties. CI was fixed at 60 phr where the CB was varied from 10 – 30 phr. Higher thermal conductivity and magneticity in nature of CI had made the composites faster cure and higher magnetic strength. On the contrary, superior tensile strength, modulus and elongation at break were found in the presence of CB. From the experimental results, hybridization of 60/10 phr/phr of CI and CB is highly suggested to gain the synergistic strength and magneticity. This is expected to solve a big problem in the application of MRE.

The use of mineral fillers in rubber industry has been increasingly focused. Sepiolite is considered as one of the mineral fillers that exploits unique characteristics. This is due to its unique needle-like fibrous and a tunnel-like micro-pore channel structures. Therefore, adding this filler in natural rubber (NR) matrix would bring tremendous advantage. The study was carried out in the form of curing characteristics, tensile properties and morphology together with the dynamic properties. Filling sepiolite to NR has brought to a noticeable enhancement of curing characteristics, tensile properties and morphology. This is contributed to the distinctive structure of sepiolite itself, it provides a better dispersion to the NR. Surface roughness of the composites is visibly found which is responsible for the mechanical properties. Further verification was also monitored through the dynamic properties of the composites. The obtained profiles are in good agreement to the tensile properties and morphological characteristics observed.