Aim The purpose of this study was to investigate the biofilm effect on the hybrid ceramic-resin cement bond strength (BS) by comparing two methods. Methods Teeth were distributed into groups (n=5), according to the resin cement (Maxcem Elite-(MC) or NX3 Nexus-(NX)) and degradation method (24h or 7 days in distilled water; 7 or 30 days incubated with biofilm and 30 days in sterile media). Treated surfaces of Vita Enamic blocks (5x6x7mm) were luted to treated or no treated dentin surfaces and light-cured. After 24h, beams were obtained (1x1x10mm) and stored accordingly. The flexural bond strength (FBS) was assessed by four-point bending test. Additional beams were obtained from new teeth (n=5), stored for 24h or 7 days in distilled water, and submitted to a microtensile bond strength (µTBS) assay. Failure modes were determined by scanning electron microscopy (100X). The flexure strength of the cements (n=10) was assessed by a four-point bending test. Data were analyzed by 1 and 2-ways ANOVA, and Tukey’s test (α=0.05). Results There was no significant difference between the degradation methods for the FBS groups. For the µTBS, the significant difference was as follows: NX 7days > NX 24h > MC 7days = MC 24h. Failure mode was mainly adhesive and mixed, but with an increase of cohesive within cement and pre-failures for the MC groups assessed by µTBS. NX had better performance than MC, regardless of the method. Conclusions The biofilm had no effect on the materials BS and FBS test was a useful method to evaluate BS of materials with poor performance.

Aim To evaluate the influence of cobalt-chromium (Co-Cr) coping fabrication methods and ceramic application on the marginal and internal fit of metal-ceramic crowns. Methods Co-Cr copings for metal-ceramic crowns were prepared by lost wax casting or CAD-CAM machining of sintered blocks. The fit was analyzed using the silicone replica technique at four assessment points: marginal gap (MG), axial wall (AW), axio-occlusal (AO) angle, and central occlusal (CO) wall. After the initial analysis, the copings were ceramic-veneered with the layering technique, and the fit was again determined. Data were statistically analyzed by paired and unpaired Student’s-t test (α=0.05). Results Marginal and internal fit before ceramic application according to the coping manufacturing method showed significant differences only at CO (p < 0.001), with milled copings (137.98±16.71 μm) showing higher gap values than cast copings (112.86±8.57 μm). For cast copings, there were significant differences at MG (before 109.13±8.79 μm; after 102.78±7.18 μm) and CO (before 112.86±8.57 μm; after 104.07±10.63 μm) when comparing the fit before and after ceramic firing. For milled copings, there was significant difference only at AO (before 116.39±9.64 μm; after 108.54±9.26 μm). Conclusion This study demonstrated that the coping fabrication method influenced the internal fit. Ceramic firing maintained or improved the fit of the metal-ceramic crowns. The marginal discrepancy of all restorations, before and after ceramic firing, can be considered clinically acceptable.

Resumo O objetivo deste trabalho foi avaliar os efeitos da biodegradação in vitro e in situ nas características superficiais de dois cimentos resinosos e de um sistema cerâmico híbrido. Cento e oitenta espécimes (4X1,5mm) de cada material (Maxcem Elite, NX3 Nexus e Vita Enamic) foram distribuídos aleatoriamente em doze grupos (n=15) de acordo com o material e o método de biodegradação. Os espécimes foram então submetidos aos seguintes desafios: armazenamento em água destilada 37ºC por 24 horas ou 7 dias, armazenamento por 7 dias, a 37ºC, em saliva estimulada ou in situ. O estágio in situ correspondeu à preparação de 15 dispositivos intra-orais palatinos, utilizados por 7 dias. Cada dispositivo apresentou 3 nichos, onde uma amostra de cada material foi acomodada. As amostras dos grupos saliva e in situ sofreram um desafio cariogênico, correspondendo à aplicação de uma solução de 20% de sacarose, 10 vezes ao longo de cada dia. Após cada método de biodegradação, foram realizadas as análises de rugosidade superficial (Ra), dureza Vickers (VHN) e microscopia eletrônica de varredura (MEV). Os dados coletados foram analisados por meio do teste de Levene, ANOVA two-way e teste de Tukey (α=5%). O desafio in situ promoveu maior degradação, independentemente do material. Em relação aos materiais, a VHN do Vita Enamic foi afetada negativamente por todos os métodos de degradação e o Nexus NX3 apresentou melhor desempenho que o cimento autoadesivo testado. Portanto, dentro das condições deste trabalho, concluiu-se que a biodegradação in situ pode afetar negativamente as características superficiais de materiais restauradores indiretos.

Abstract The objective of this work was to evaluate the effects of in vitro and in situ biodegradation on the surface characteristics of two resin cements and a hybrid ceramic system. One hundred and eighty specimens (4X1.5mm) of each material (Maxcem Elite, NX3 Nexus and Vita Enamic) were made and randomly distributed in twelve groups (n=15) according to the material and biodegradation method. The specimens were then submitted to the following challenges: storage in distilled water 37 ºC for 24 h or 7 days, storage for 7 days, at 37 ºC, in stimulated saliva or in situ. The in situ stage corresponded to the preparation of 15 intraoral palatal devices, used for 7 days. Each device presented 3 niches, where a sample of each materials was accommodated. Specimens from both saliva and in situ groups suffered a cariogenic challenge, corresponding to the application of a solution of 20% of sucrose, 10 times throughout each day. After each biodegradation method, the surface roughness (Ra), Vickers hardness (VHN) and scanning electron microscopy (SEM) analyzes were performed. The data collected were evaluated by Levene test, two-way ANOVA and Tukey`s test (α=5%). The in situ challenge promoted the greater biodegradation, regardless of the material. Regarding the materials, the Vita Enamic VHN was negatively affected by all biodegradation methods and the Nexus NX3 presented better performance than the self-adhesive cement tested. Therefore, within the conditions of this work, it was concluded that in situ biodegradation can affect negatively the surface characteristics of indirect restorative materials.

Resumo O objetivo deste estudo foi avaliar o efeito da sepse aguda no ligamento periodontal, osso alveolar e osso da furca por meio de análise histológica e imunohistoquímica. O modelo de sepse em ratos foi estabelecido pelo procedimento de ligação e perfuração do ceco (CLP). Doze ratos foram divididos de forma randomizada em ratos sépticos (n=6) e controle - grupo Sham (n=6). Os animais foram eutanasiados após 24 horas e suas hemimandíbulas foram submetidas aos procedimentos histotécnicos para análise histomorfométricos (matriz óssea, fibras colágenas, fibroblastos, osteócitos, células inflamatórias e vasos sanguíneos) e imunohistoquímicos (BMP-2/4, RANKL e osteocalcina) no osso alveolar, osso de furca e ligamento periodontal. Nossos resultados demonstraram que os parâmetros histomorfométricos foram similares no osso alveolar, osso de furca e ligamento periodontal dos animais do grupo sepse e do grupo Sham. Em relação à análise por imunohistoquímica, o número de células imunomarcadas para BMP-2/4 e RANKL também foi similar em ambos os grupos. Entretanto, houve redução (p=0.0014) no número de células imunomarcadas para osteocalcina no ligamento periodontal de ratos sépticos em relação ao grupo Sham. Como conclusão, o estabelecimento de sepse aguda resultou em um número reduzido de células imunomarcadas para osteocalcina na região do ligamento periodontal (p=0,0014). Além disso, não foram observadas diferenças histológicas significativas no periodonto de ratos na presença de sepse aguda. Considerando o papel da osteocalcina na remodelação óssea, este estudo contribui para revelar a importância da avaliação periodontal cuidadosa na presença de sepse.

Abstract The aim of this study was to evaluate the effect of acute sepsis in the periodontal ligament, alveolar and furcation bone in absence of periodontitis induction through histological and immunohistochemical analyses. A septic rat model was established by cecal ligation and puncture (CLP). Twelve rats were randomly divided into CLP (n=6) and Sham (n=6) groups. The animals were euthanized at 24 h and hemimandibles were submitted to histomorfometric (bone matrix, collagenous fibers, fibroblasts, osteocytes, inflammatory cells, and blood vessels) and immunohistochemical (BMP-2/4, RANKL and osteocalcin) evaluation in alveolar bone, furcation bone and periodontal ligament. Our results demonstrated that histomorphometric parameters were similar in alveolar bone, furcation bone and periodontal ligament of Sham and CLP rats. Regarding to immunohistochemical analyses, the number of BMP-2/4 and RANKL immunolabeled cells was also similar in both groups. Furthermore, it was detected a reduction in the osteocalcin immunolabeled cells in periodontal ligaments of CLP compared to Sham rats (p=0.0014). In conclusion, the acute sepsis induction resulted in reduced number of osteocalcin labelled cells in periodontal ligament region. Moreover, no significant histological differences were observed in the periodontium of rats under acute sepsis. Considering the role of osteocalcin in bone remodeling, the study contributes to revealing the importance of careful periodontal evaluation in the presence of sepsis.

Resumo O objetivo foi avaliar a estabilidade de cor de laminados cerâmicos de fina espessura, após a cimentação com cimentos resinosos e resinas compostas em temperatura ambiente e aquecida (60oC), durante 12 meses; bem como determinar o grau de conversão dos diferentes materiais para cimentação. Foram utilizados dois cimentos resinosos [AllCem Veneer, cimento resinoso fotoativado (LRC) e AllCem, cimento resinoso dual (DRC)] e três resinas compostas [Z100 (MNCR - resina composta de partículas finas), Herculite Classic (MHCR - resina composta micro-híbrida) e Durafill (MCCR - resina composta microparticulada)] para cimentação de laminados cerâmicos a base de silicato de lítio (Suprinity, cor B2-HT, Vita Zahnfabrik) com 0,8 mm de espessura, sobre esmalte bovino. Oitenta espécimes foram distribuídos aleatoriamente em 8 grupos de acordo com o material para cimentante (n=10). Os espécimes foram armazenados a 37oC em água destilada. Os parâmetros do CIELab foram determinados 24h após a cimentação (baseline), 7, 30, 90, 180 dias e 12 meses. Outros três espécimes foram preparados para avaliação de grau de conversão, realizada por espectroscopia micro-Raman. Os dados foram analisados por ANOVA e teste de Tukey (a=5%). Para ΔEab e ΔE00, houve diferenças estatisticamente significantes para o material de cimentação (p<0,001), tempo (p<0,001) e interação dupla (p<0,001). Os grupos cimentados com o MHCR (1 ano), MCCR (90 dias e 1 ano) e MCCR-PH (1 ano) foram os únicos com valores de ΔE maiores que o limite de aceitabilidade. Todos os demais grupos mantiveram seu ΔE menor que o limite de aceitabilidade ao final de 1 ano de armazenamento em água destilada. Em relação ao grau de conversão, não foram observadas diferenças estatisticamente significantes entre os materiais para cimentação avaliados (p=0,127). O grau de conversão variou entre 64,0% (MNCR-PH) e 85,1% (DRC). Correlações negativas moderadas a fortes não significativas foram observadas entre a média ΔEab e grau de conversão (R=-0,65) e ΔE00 e grau de conversão (R=-0,64). Observou-se uma correlação positiva forte significativa nos valores médios de ΔEab e ΔE00 (R=0,99). Pode-se concluir que os diferentes agentes cimentantes utilizados na cimentação de laminados cerâmicos de espessura fina influenciaram na cor final das restaurações. O aquecimento das resinas compostas não implicou em alteração do grau de conversão.

Abstract The objective was to evaluate the color stability of ceramic veneers luted with resin cements and pre-heated composite resins (60oC) for 12 months, and determine the degree of conversion (DC) of the luting agents. Two resin cements (AllCem Veneer, light-cured (LRC) and AllCem, dual-cured (DRC)] and three composite resins [Z100 (MNCR-minifilled), Herculite Classic (MHCR-micro-hybrid) and Durafill (MCCR-microfilled)] were used for cementing 0.8-mm-thick lithium-silicate glass-ceramic laminates (Suprinity, shade B2-HT, Vita) on bovine enamel (n=10). The specimens were stored at 37oC in distilled water. CIELab parameters were determined at 24h after luting (baseline), 7, 30, 90, 180 days and 12 months. Three specimens were prepared for DC evaluation, performed by micro-Raman spectroscopy. Data were analyzed by ANOVA and Tukey’s test (a=5%). For ΔEab and ΔE00, there were significant differences for luting material (p<0.001), time (p<0.001), and double interaction (p<0.001). The groups cemented with MHCR (1 year), MCCR (90 days and 1 year) and MCCR-PH (1 year) were the ones with ΔE values greater than the acceptability threshold. All other groups maintained their ΔE lower than the acceptability threshold after 1 year in distilled water. Regarding DC, there were no significant differences (p=0.127) among the materials. Non-significant negative correlations were observed between the mean ΔEab and DC (R=-0.65) and ΔE00 and DC (R=-0.64). A significant positive correlation was observed mean ΔEab and ΔE00 (R=0.99). It was concluded that the different luting agents influenced the final color of the restorations. The heating of the composite resins did not affect their DC.

Abstract The aim of this research was to evaluate the influence of MDP (10-methacryloyloxydecyl dihydrogen phosphate) concentration and application mode of experimental adhesives on microshear bond strength (μSBS) to dentin after storage in distilled water at 37°C for 24h and 6 months. Five experimental adhesives were prepared with: CQ, DABE, BHT, ethanol, HEMA, TEGDMA, Bis-EMA, UDMA, and Bis-GMA. Concentrations of 0 wt%, 3 wt%, 9 wt%, 12 wt% or 15 wt% of MDP were added to their composition. The adhesives were applied to flat dentin surfaces in etch-and-rinse or self-etching modes. Cylindrical molds filled with light-cured composite resin were placed above the dentin. The specimens were stored in distilled water at 37oC for 24h or 6 months and submitted to μSBS testing. The adhesives were also submitted to pH analysis. The data were analyzed by one-way ANOVA, three-way ANOVA and Tukey’s test (α = 5%). All the adhesives used in the etch-and-rinse mode showed significantly higher bond strength than the adhesives applied in the self-etching approach. The 9 wt% adhesive showed the highest bond strength values, and 3 wt% was most stable after storage. A strong negative correlation between MDP concentration and pH was observed. It was concluded that the formulations with low concentrations of MDP (up to 9 wt%) showed better results for bond strength and bond strength degradation over time.

Resumo O objetivo deste estudo foi avaliar a estabilidade de cor de laminados cerâmicos de espessura fina em função do momento de ativação de diferentes sistemas adesivos na superfície interna das cerâmicas. Foram utilizados 5 sistemas adesivos (Scotchbond Multiuso, Single Bond Universal, Gluma 2 Bond, Ambar and Ambar APS) e o cimento resinoso fotoativado (Allcem Veneer) para cimentação de lâminas de cerâmica feldspática (Mark II) com 0,6 mm de espessura, sobre substratos de resina composta (Charisma Diamond). Os grupos, de acordo com o sistema adesivo utilizado, foram divididos em dois subgrupos (n=10): i) adesivo e cimento resinoso foram polimerizados separadamente (polimerização isolada do adesivo), ii) adesivo e cimento resinoso foram polimerizados ao mesmo tempo (polimerização simultânea). Os parâmetros de cor do sistema CIELab foram determinados com um espectrofotômetro nos tempos de 24 h (baseline), 7 dias, 30 dias e 12 meses. Os dados foram analisados por ANOVA a dois fatores e teste de Tukey (α=0,05). Os resultados indicaram diferenças estatísticas significantes para os sistemas adesivos e tempo. O momento da fotoativação do sistema adesivo não foi estatisticamente significante: polimerização prévia (2,6±1,3) e polimerização simultânea (2,8±1,4). Para o sistema adesivo, os valores médios de ΔE variaram na seguinte ordem: Ambar APS (1,6±0,5)<Scotchbond Multi-Purpose (2,6±1,2)=Gluma 2 Bond (2,7±1,2)=Ambar (2,9±1,2)<Single Bond Universal (3,5±1,5). Para o fator tempo o ΔE foi: 7 dias (1,7±0,7), 30 dias (3,5±1,2) e 12 meses (2,9±1,3). Pode-se concluir que os diferentes sistemas adesivos utilizados na cimentação de laminados cerâmicos de espessura fina influenciaram na cor final das restaurações. O momento da fotoativação, isolada ou simultânea ao cimento resinoso, não apresentou efeito significativo na estabilidade de cor dos laminados cerâmicos de espessura fina.

Abstract The objective was to evaluate the color stability of thin ceramic veneers as a function of the curing mode (with and without pre-cure) of different adhesive systems applied to the internal surface of ceramics. Five adhesive systems (Scotchbond Multi-Purpose, Single Bond Universal, Gluma 2 Bond, Ambar, and Ambar APS) and photo-cured resin cement (Allcem Veneer) were used for cementing 0.6 mm-thick feldspathic veneers (Mark II) on composite resin substrates (Charisma Diamond). The groups, according to adhesive system, were divided into two subgroups (n=10): i) adhesive and resin cement were polymerized separately (pre-cure of the adhesive), ii) adhesive and resin cement were polymerized simultaneously. The CIELab color parameters were determined with a spectrophotometer at 24h (baseline), 7 days, 30 days and 12 months. Data were analyzed by two-way ANOVA and Tukey’s test (α=0.05). The results indicated statistically significant differences for adhesive systems and time. The mode of curing of the adhesive system was not statistically significant: pre-cured adhesives (2.6±1.3) and not pre-cured adhesives (2.8±1.4). For the adhesives, ΔE values varied in the following order: Ambar-APS (1.6±0.5) < Scotchbond Multi-Purpose (2.6±1.2) = Gluma 2 Bond (2.7±1.2) = Ambar (2.9±1.2) < Single Bond Universal (3.5±1.5). For time, ΔE values were: 7 days (1.7±0.7), 30 days (3.5±1.2) and 12 months (2.9±1.3). It can be concluded that the different adhesive systems used for cementing thin ceramic veneers influenced the final color of the indirect restorations. The adhesives curing mode did not present a significant effect in the color stability of thin ceramic veneers.

Resumo A adaptação marginal e interna é fundamental para o sucesso das restaurações indiretas e novos sistemas de imagem permitem avaliar esses parâmetros de maneira não-destrutiva e com precisão. Este estudo avaliou a adaptação marginal e interna de copings de zircônia fabricados com dois sistemas diferentes, utilizando as técnicas da réplica em silicone e micro-CT. Um modelo-mestre de metal, representando um preparo para uma coroa totalmente cerâmica foi digitalizado e copings de zirconia policristalina (Ceramill Zi, Amann Girrbach e inCoris Zi, Dentslpy Sirona, n=10) foram fabricados. Para cada coping, a adaptação marginal e interna foi avaliada pelas técnicas da réplica em silicone e micro-CT. Foram avaliados quatro pontos de cada seção transversal e imagem de micro-CT: adaptação marginal (MG), parede axial (AW), ângulo axial-oclusal (AO) e parede centro-oclusal (MO) utilizando um software de imagem. Os dados foram analisados estatisticamente por ANOVA e teste de Tukey (a=0,05). Não houve diferença estatisticamente significativa entre as duas técnicas para MG e AW. Para AO, houve diferenças significativas entre as técnicas para copings da Amann, enquanto que para copings da Dentsply Sirona foram observados valores semelhantes. Para o MO, ambas as técnicas apresentaram diferenças estatisticamente significativas. Observou-se uma correlação positiva entre os valores de adaptação determinados pelas duas técnicas. O método de avaliação influenciou a avaliação da adaptação marginal e interna de copings de zircônia. Pode-se concluir que a micro-CT mostrou menores valores de adaptação marginal e interna quando comparado com a técnica de réplica em silicone. Os pontos de avaliação da margem e da parede axial mostraram os menores valores de adaptação, independente do sistema cerâmico e da técnica de avaliação utilizados.

Abstract Marginal and internal adaptation is critical for the success of indirect restorations. New imaging systems make it possible to evaluate these parameters with precision and non-destructively. This study evaluated the marginal and internal adaptation of zirconia copings fabricated with two different systems using both silicone replica and microcomputed tomography (micro-CT) assessment methods. A metal master model, representing a preparation for an all-ceramic full crown, was digitally scanned and polycrystalline zirconia copings were fabricated with either Ceramill Zi (Amann-Girrbach) or inCoris Zi (Dentslpy-Sirona), n=10. For each coping, marginal and internal gaps were evaluated by silicone replica and micro-CT assessment methods. Four assessment points of each replica cross-section and micro-CT image were evaluated using imaging software: marginal gap (MG), axial wall (AW), axio-occlusal angle (AO) and mid-occlusal wall (MO). Data were statistically analyzed by factorial ANOVA and Tukey test (a=0.05). There was no statistically significant difference between the methods for MG and AW. For AO, there were significant differences between methods for Amann copings, while for Dentsply-Sirona copings similar values were observed. For MO, both methods presented statistically significant differences. A positive correlation was observed determined by the two assessment methods for MG values. In conclusion, the assessment method influenced the evaluation of marginal and internal adaptation of zirconia copings. Micro-CT showed lower marginal and internal gap values when compared to the silicone replica technique, although the difference was not always statistically significant. Marginal gap and axial wall assessment points showed the lower gap values, regardless of ceramic system and assessment method used.

Resumo Vibrações sônicas podem melhorar a resistência e a durabilidade da união de pinos de fibra de vidro, melhorando a penetração do sistema adesivo à dentina, bem como o escoamento do cimento. O objetivo deste estudo foi avaliar o efeito da vibração sônica na resistência de união de pinos de fibra de vidro à dentina radicular, através de ensaio pull out. Raízes bovinas tratadas endodonticamente foram preparadas e divididas aleatoriamente em quatro grupos (n=12): Grupo C - cimentação convencional, (controle); Group SA - vibração sônica (Smart Sonic Device(r), FGM) do sistema adesivo e assentamento convencional do pino; grupo SP - aplicação convencional do sistema adesivo e vibração sônica no assentamento do pino; e SASP - vibração sônica do sistema adesivo e no assentamento do pino. Os retentores foram limpos, tratados com silano e sistema adesivo (Ambar, FGM) e cimentados com cimento resinoso dual (Allcem Core, FGM). Após 24 h as amostras foram submetidas ao teste mecânico e análise de falha. Amostras representativas foram avaliadas sob microscópio eletrônico de varredura, para avaliação da linha de cimentação. Os resultados foram analisados por meio de análise de variância e teste de Tukey (a=5%). Os resultados obtidos foram: SASP (90,9±27,1 N, C (121,4±60,6 N), SA (127,6±31,8 N) e SP (156,4±41,3 N). A vibração sônica para aplicação apenas do sistema adesivo ou pino não afetou a resistência de união, entretanto interferiu negativamente quando utilizada para ambos procedimentos.

Abstract Sonic vibrations may improve the bond strength and durability of fiberglass posts by improving adhesive penetration into dentin as well as the cement flow. The objective of this study was to evaluate the effect of sonic vibrations on the bond strength between fiberglass posts and root dentin using the pull-out test. Bovine roots were endodontically treated and divided randomly into four groups (n=12): Group C - conventional cementation (control); Group SA - sonic vibration (Smart Sonic Device, FGM) of the adhesive system and conventional post accommodation; SP group - conventional adhesive application and sonic vibration of the post during accommodation; and SASP - sonic vibration of the system adhesive and the post during accommodation. The posts were cleaned, treated with a silane and adhesive system (Ambar, FGM), and cemented with a dual-cured resin cement (Allcem Core, FGM). After 24 h, the specimens were subjected to mechanical tests and failure analyses. Representative specimens were analyzed by a scanning electron microscope to observe the cementation line. The results were analyzed using ANOVA and Tukey's test (a=5%). The bond strengths were as follows: SASP (90.9±27.1 N), C (121.4±60.6 N), SA (127.6±31.8 N) and SP (156.4±41.3 N). The use of sonic vibrations during the application of adhesive or post cementation separately did not affect the bond strength but had a negative effect when used for both procedures.

Resumo O objetivo do estudo foi avaliar o efeito de tratamentos de superfície em esmalte e dentina na resistência de união (RU) de um cimento auto-adesivo. As coroas de setenta e dois terceiros-molares foram incluídas em resina acrílica e desgastadas para obtenção de áreas planas em esmalte e dentina. Os espécimes de esmalte e dentina foram aleatoriamente distribuídos em 8 grupos (n=12) de acordo com: tratamento de superfície (sem tratamento ou aplicação de solução de ácido poliacrílico a 11,5%), condição do substrato (seco ou úmido) e período de armazenamento (1 dia ou 90 dias). Após, cilindros (1 x 1 mm) foram confeccionados na superfície dos espécimes utilizando cimento resinoso auto-adesivo (Rely X U200) segundo as instruções do fabricante. Os espécimes foram armazenados em água destilada a 37 oC por 1 dia ou 90 dias e submetidos ao ensaio mecânico de microcisalhamento (EMIC DL 2000 a 0,5 mm/min). O tipo de falha de cada espécime foi determinado após ensaio. Os dados foram submetidos à análise estatística (a=0,05). De acordo com os resultados, a aplicação de ácido poliacrílico a 11,5% diminuiu a RU em ambos substratos, esmalte e dentina. Os grupos mantidos úmidos mostraram maiores valores de RU do que os secos, independentemente do substrato ou tratamento de superfície. O período de armazenamento não influenciou nos valores de RU. Concluiu-se que o tratamento de superfície com ácido poliacrílico a 11,5% e a ausência de umidade no substrato diminuíram os valores de RU para o cimento resinoso auto-adesivo, independentemente do período de armazenamento.

Abstract The aim of this study was to evaluate the effect of enamel and dentin surface treatment on the micro-shear bond strength of self-adhesive cement. Seventy-two extracted third molars had their crowns embedded in acrylic resin and worn to obtain a flat enamel or dentin surface. The enamel and dentin specimens were randomly assigned to 8 groups (n=12) that were based on surface treatment (11.5% polyacrylic acid solution or no treatment), substrate condition (wet or dry) and storage period (1 day or 90 days), and treated accordingly. Cylinders (1 × 1 mm) were fabricated using self-adhesive resin cement (RelyX U200) following the manufacturer's instructions. The specimens were stored in distilled water at 37 °C for either 1 day or 90 days and subjected to micro-shear bond strength test (EMIC DL 2000 at 0.5 mm/min). After this, the failure type of the specimens was determined. Data were subjected to statistical analysis (a=0.05). According to the results, the 11.5% polyacrylic acid application decreased the bond strength in both enamel and dentin samples. The moist groups showed higher bond strength than the dry ones, regardless of the substrate and surface treatment. Storage period did not influence bond strength. In conclusion, surface treatment with 11.5% polyacrylic acid and absence of moisture decreased the bond strength of the resin-cement (RelyU200), regardless of the storage period.

Resumo O objetivo deste estudo foi avaliar a influência da espessura da linha de cimento na resistência de união de pinos de fibra de vidro após armazenamento em água destilada. Trinta dentes humanos hígidos unirradiculares tiveram os canais tratados endodonticamente. As raízes foram distribuídas em três grupos: THIN (linha de cimento fina): conduto preparado com broca 0,5 e cimentação de pino 0,5; THICK (linha de cimento espessa): conduto preparado com broca 1 e cimentação de pino 0,5; e CUSTOM (linha de cimento personalizada): conduto preparado com broca 1 e cimentação de pino personalizada (pino 0,5 personalizado com resina composta). Os pinos foram cimentados com cimento auto-adesivo. Após armazenamento das raízes em água destilada a 37 °C por 24 h e 90 dias, o teste de cisalhamento por extrusão push-out foi realizado. Os resultados foram analisados estatisticamente por ANOVA a três fatores e teste de Tukey (a=0,05). A resistência de união foi significativamente maior para CUSTOM (9,37 MPa), do que para THIN (7,85 MPa) e THICK (7,07 MPa), que foram semelhantes entre si. Considerando-se os terços radiculares, a resistência de união variou na sequência: apical (7,13 MPa) < médio (8,22 MPa) = coronal (8,94 MPa). A resistência de união após 24 h de armazenamento em água foi significativamente maior (8,80 MPa) do que para 90 dias (7,40 MPa). Pode-se concluir que houve influência da espessura da linha de cimento na resistência de união de pinos de fibra de vidro, sendo que o uso de pinos personalizados apresentou maiores valores de resistência de união. O armazenamento em água por 90 dias afetou negativamente os valores de resistência de união, especialmente no terço apical, no grupo com linha de cimento mais espessa.

Abstract The objective of the present study was to evaluate the influence of resin cement thickness on the bond strength of prefabricated and customized glass fiber posts after storage in distilled water. Thirty human uniradicular roots were treated endodontically. The roots were divided into 3 groups: THIN (thin cement layer) - post space preparation with #0.5 drill and cementation of #0.5 post; THICK (thick cement layer) - post space preparation with #1 drill and cementation of #0.5 post; and CUSTOM (customized cement layer) - post space preparation with #1 drill and cementation of a customized post (#0.5 glass fiber posts customized with resin composite). All posts were luted with self-adhesive resin cement. The push-out test was carried out after storage for 24 h and 90 days in distilled water at 37 °C. The data were analyzed with three-way ANOVA and Tukey's test (a=0.05). Bond strengths were significantly higher for CUSTOM (9.37 MPa), than for THIN (7.85 MPa) and THICK (7.07 MPa), which were statistically similar. Considering the thirds, the bond strength varied in the sequence: apical (7.13 MPa) < middle (8.22 MPa) = coronal (8.94 MPa). Bond strength for 24 h storage was significantly higher (8.80 MPa) than for 90-day storage (7.40 MPa). It may be concluded that the thickness of resin cement influenced the bond strength of glass fiber posts. The customized posts presented higher bond strength. Storage in water for 90 days affected negatively the values of bond strength, especially for thick cement layers in the apical third.

RESUMO Objetivo: Avaliar o desempenho in vitro de radiografia digital e de dois localizadores apicais eletrônicos, Propex II e Root ZX na determinação do comprimento de canal em molares decíduos. Métodos: Foram selecionados 25 molares decíduos divididos em dois grupos, G1, sem reabsorção radicular e G2 com reabsorção radicular. Os exames foram realizados utilizando todos os métodos por dois examinadores experientes, com intervalo de 1 semana. O padrão ouro foi determinada por exame visual. Os métodos foram analisados estatisticamente em relação aos valores de reprodutibilidade e correlacionada com o padrão ouro pelo coeficiente de correlação de Pearson. Resultados: A determinação de comprimento de canal coincidiu com padrão-ouro em 22,7% para o Root ZX, 17,5% para Propex II e 12,5% para a radiografia digital. valores de correlação foram maiores no G1, o Root ZX apresentou os maiores valores. Em G2 da radiografia digital apresentou a menor correlação. No G1, os valores de reprodutibilidade intra-examinador variou 0,925-0,523 e interexaminadores 0,863-0,670. No G2, os valores da reprodutibilidade intra-examinador varia 0,864-0,097, e inter era 0,774-0,379. Conclusão: Concluiu-se que o desempenho dos métodos varia de acordo com a experiência do examinador. O Root ZX apresentou maior reprodutibilidade e precisão.

ABSTRACT Objective: The aim of the study was to evaluate performance of digital radiographic and two electronic apex locators, Propex II and Root ZX in root canal length determination in primary molars. Methods: 25 primary molars were divided into two groups, G1 without root resorption and G2 with root resorption. The exams were performed using all methods by two experienced examiners, with 1-week interval. The gold standard was determined by visual examination. The methods were statistically analyzed regarding the values of reproducibility and correlated with the gold standard by Pearson´s correlation coefficient. Results: The root canal length determination coincided with gold standard in 22.7% for Root ZX, 17.5% for Propex II and 12.5% for digital radiography. Correlation values were higher in G1, the Root ZX presented the highest values. In G2 the digital radiography showed the lowest correlation. In G1, the intra-examiner reproducibility values ranged from 0.925 to 0.523, and interexaminer 0.863 to 0.670. In G2, the values of intra-examiner reproducibility ranges from 0.864 to 0.097, and inter was 0.774 to 0.379. Conclusion: It was concluded that the methods performance varying according to examiner's experience. The Root ZX presented the highest reproducibility and accuracy.

Abstract The objective of this study was to evaluate the marginal and internal fit of zirconia copings obtained with different digital scanning methods. A human mandibular first molar was set in a typodont with its adjacent and antagonist teeth and prepared for an all-ceramic crown. Digital impressions were made using an intraoral scanner (3Shape). Polyvinyl siloxane impressions and Type IV gypsum models were also obtained and scanned with a benchtop laboratory scanner (3Shape D700). Ten zirconia copings were fabricated for each group using CAD-CAM technology. The marginal and internal fit of the zirconia copings was assessed by the silicone replica technique. Four sections of each replica were obtained, and each section was evaluated at four points: marginal gap (MG), axial wall (AW), axio-occlusal edge (AO) and centro-occlusal wall (CO), using an image analyzing software. The data were submitted to one-way ANOVA and Tukey’s test (α = 0.05). They showed statistically significant differences for MG, AO and CO. Regarding MG, intraoral scanning showed lower gap values, whereas gypsum model scanning showed higher gap values. Regarding AO and CO, intraoral digital scanning showed lower gap values. Polyvinyl siloxane impression scanning and gypsum model scanning showed higher gap values and were statistically similar. It can be concluded that intraoral digital scanning provided a lower mean gap value, in comparison with conventional impressions and gypsum casts scanned with a standard benchtop laboratory scanner.

Abstract The color stability of resin cements is essential for aesthetic restorations. Aim: To evaluate the influence of shade and aging time on the color stability of two light-cured and two dual-cured resin cements. Methods: The CIE-Lab color parameters (n=6) were measured immediately after sample preparation and at 7, 30 and 90 days of aging in distilled water. The color difference (ΔE) was calculated and then analyzed by three-way ANOVA for repeated measures and Tukey's HSD test (α=0.05). Results: ΔE was higher for transparent resin colors, followed by dark and light colors. The mean values of ΔE were lower for both light-cured resin cements compared to the dual-cured cements. As the aging time increased, ΔE values increased. Conclusions: The light-cured resin cements showed greater color stability. The lighter shades of luting were more likely to display a greater color change.

Resumo O objetivo deste trabalho foi avaliar o efeito da aplicação de clorexidina 2% (CHX) na resistência de união (RU) ao microcisalhamento de dois sistemas adesivos após armazenagem em diferentes meios. Setenta e duas coroas de molares humanos foram cortadas e incluídas em cilindros de PVC. Os espécimes foram distribuídos aleatoriamente nos grupos (n=12), segundo o sistema adesivo (Ambar e Single Bond 2), uso ou não de CHX e o tempo (24 h e 15 dias) e meio de armazenamento (água destilada, óleo mineral e hipoclorito de sódio 1% - NaOCl). Os sistemas adesivos foram aplicados de acordo com as recomendações do fabricante, com e sem o uso de CHX, e cilindros de resina composta (Z350 XT) foram colocados sobre a dentina já hibridizada. Após a fotoativação, os espécimes foram armazenados em um dos três meios (água destilada, óleo mineral e NaOCl a 1%) a 37 ºC por 24 h e 15 dias. RU foi determinada pelo ensaio de microcisalhamento, com velocidade de 0,5 mm/min. Os dados foram analisados por ANOVA a quatro fatores e teste de Tukey (α=5%). O uso da CHX não provocou perda de RU em nenhuma das situações avaliadas, independentemente do tempo e meio de armazenamento. Não houve influência do meio de armazenamento na RU após 15 dias quando foi utilizado o protocolo adesivo sem a aplicação de CHX. Porém, a utilização de CHX influenciou negativamente os valores de RU para o Single Bond 2 após 15 dias de armazenamento em água destilada e NaOCl a 1%.

The aim of this study was to evaluate the effect of 2% chlorhexidine (CHX) application during the bonding protocol on microshear bond strength of two adhesive systems, after storage in different media. Seventy-two human molars had their crowns cut in half and embedded in PVC cylinders with acrylic resin. The specimens were randomly divided into experimental groups (n=12) according to the adhesive system (Ambar and Single Bond 2), use of CHX in the bonding protocol, and time interval (24 h and 15 days) in the storage media (distilled water, mineral oil and 1% sodium hypochlorite - NaOCl). Adhesive systems were applied in accordance to manufacturers' recommendations, with or without the use of CHX, and resin composite (Z350 XT) cylinders were placed on the hybridized dentin. After photoactivation, the specimens were stored in distilled water, mineral oil and 1% NaOCl for 24 h and 15 days. Microshear bond strength was determined at a crosshead speed of 0.5 mm/min until fracture. The bond strength data were analyzed statistically by 4-way ANOVA and Tukey's test (α=5%). Use of CHX in the bonding protocol did not cause loss of bond strength in any of the evaluated situations, irrespective of time and storage medium. The storage medium had no influence on bond strength values after 15 days when the bond protocol without CHX application was used. However, the use of CHX in the protocol influenced negatively the bond strength values for Single Bond 2 after 15 days storage in distilled water and 1% NaOCl.