Concrete is the most used material in the construction industry worldwide. Built concrete infrastructure is exposed to specific environments conditions during the asset’s life, which impose chemical and physical actions that may lead to premature deterioration. Poor concrete durability and corrosion of reinforcement bars are the primary cause of structural deterioration and reduced service life. Most concrete deterioration mechanisms are driven by transport properties, in particular, the chloride diffusion coefficient. In this paper, the effect of curing in the chloride diffusion coefficient of conventional concrete is investigated through Electrochemical Impedance Spectroscopy (EIS). Reinforced concrete samples cured for 3, 7 and 28 days were exposed to accelerated chloride testing for 300 days (40 wet-dry cycles). Results indicate that the chloride diffusion coefficient reduces significantly with curing time, evidencing that prolonged curing may decrease the likelihood of corrosion in reinforced concrete structure when combined with appropriate design and construction processes.

RESUMO O objetivo deste trabalho foi verificar a possibilidade de utilização de compósitos cimento-madeira na fabricação de componentes leves para alvenaria, visando reduzir os prejuízos ambientais causados pela disposição final da serragem proveniente do desdobro da madeira. Primeiramente foram analisadas as propriedades físicas (teor de umidade, absorção de água, índice de vazios e massa específica) e mecânicas (resistência à compressão e módulo de elasticidade dinâmico) de diferentes traços cimento:areia, cimento:areia:serragem e cimento:serragem. A partir de traços selecionados foram fabricados tijolos maciços de alvenaria com dimensões 90 × 90 × 190 mm, submetidos a ensaios para determinação da massa específica, teor de umidade, absorção de água e resistência à compressão. As propriedades físicas e mecânicas desses componentes foram comparadas com as exigências de normas brasileiras prescritivas referentes a componentes de alvenaria. Foram obtidos resultados satisfatórios, indicando que resíduos da indústria madeireira têm potencial para serem utilizados na produção de componentes leves de alvenaria, podendo ser aplicados como material de construção alternativo.

ABSTRACT The main objective of this work was to investigate the use of cement-wood composites to produce lightweight masonry elements, aiming to reduce environmental damages arising from the disposal of the sawdust originated from wood sawing process. Physical (moisture content, water absorption, void ratio and specific gravity) and mechanical (compressive strength and dynamic Young’s modulus) properties of different cement:sand, cement:sand:sawdust and cement:sawdust mix proportions were evaluated. Specific gravity, moisture content, water absorption and compressive strength of 90 × 90 × 190 mm bricks, produced from selected mix proportions, were determined and compared to the requirements of the Brazilian standards for masonry elements. The satisfactory results obtained indicate that lightweight masonry bricks produced with wastes from wood industry have the potential to become an alternative for traditional building materials.

RESUMO O objetivo desse trabalho foi avaliar traços para o desenvolvimento de compósitos cimentícios leves,fabricadoscom serragem de Eucalyptus grandis. A partir de variações nos proporcionamentos madeira: cimento, água: cimento e aditivo: cimento, foram avaliadas propriedades físicas (absorção, índice de vazios e massa específica) e mecânicas (resistência à compressão e módulo de elasticidade estático e dinâmico) dos compósitos cimento-madeira. Os resultados mostraram que para compósitos com mesma relação água:cimento, sem utilização de superplastificante, a massa especifica é diretamente proporcional à resistência à compressão e ao módulo de elasticidade, e, inversamente proporcional percentual de madeira. O superplastificante, utilizado com a função de aumentar a fluidez da pasta, melhora o desempenho compósitos com relação às suas propriedades mecânicas. Valores mais elevados de massa específica estão relacionados com mais baixos índices de vazios e absorção de água, bem como a resistências à compressão e módulos de elasticidade mais elevados.

ABSTRACT The main objective of this work was to assess mix proportions for developing lightweight cementitious composites, manufactured with Eucalyptus grandis sawdust. Different wood:cement, water:cement and admixture:cement ratios were used to evaluate physical (water absorption, void ratio and density) and mechanical (compressive strength, static and dynamic modulus of elasticity) properties of the cement-wood composites. Results shows that, bulk density is directly proportional to the compressive strength and elastic modulus, and inversely proportional to the percentage of timber, considering composites with same water:cement ratio, without superplasticizer. The performance of the cement-wood composites, regarding mechanical properties, can be improved if superplasticizer is used to increase paste fluidity. Higher values of bulk density are related to lower void ratio and water absorption and higher compressive strength and modulus of elasticity.

RESUMO O presente artigo relata a elaboração de um modelo dinâmico de sistemas com o estudo de material reciclado proveniente de escombros para a fabricação de blocos de concreto do tipo não estruturais, utilizando para a modelagem das variáveis o programa computacional Stella. Essa modelagem permite que seja feita uma análise de cada variável do processo de produção, servindo como base para a definição das atividades críticas e as possibilidades de melhora e otimização do processo de produção, além de ser um critério de validação para uma adequada reutilização dos resíduos da construção, tendo em vista as legislações atuais e especificações técnicas e ambientais. Este estudo permitiu o desenvolvimento de um modelo conceitual de análise do processo de produção dos blocos através do comportamento que apresenta as variáveis que intervém no processo, demonstrando que a utilização de resíduos de construção e demolição neste estudo de caso é uma alternativa socioambiental com potencial econômico.

ABSTRACT This work presents the development of a system dynamic model for the use of recycled material from construction and demolition waste in the production of non-structural concrete blocks, using the software Stella for modeling of parameters. The modeling allows the individual analysis of the production process parameters, serving as a base for the definition of critical activities and possibilities for the improvement and optimization of the production. The modeling is also a validation criterion to ensure an efficient reuse of construction waste, given the current regulations, environmental and technical specifications. This study resulted in a conceptual analysis model considering several variables related to the production process. It was possible to demonstrate that the use of construction and demolition waste is a feasible social and environmental activity with economic potential.