Abstract The aim of this research was to evaluate the influence of MDP (10-methacryloyloxydecyl dihydrogen phosphate) concentration and application mode of experimental adhesives on microshear bond strength (μSBS) to dentin after storage in distilled water at 37°C for 24h and 6 months. Five experimental adhesives were prepared with: CQ, DABE, BHT, ethanol, HEMA, TEGDMA, Bis-EMA, UDMA, and Bis-GMA. Concentrations of 0 wt%, 3 wt%, 9 wt%, 12 wt% or 15 wt% of MDP were added to their composition. The adhesives were applied to flat dentin surfaces in etch-and-rinse or self-etching modes. Cylindrical molds filled with light-cured composite resin were placed above the dentin. The specimens were stored in distilled water at 37oC for 24h or 6 months and submitted to μSBS testing. The adhesives were also submitted to pH analysis. The data were analyzed by one-way ANOVA, three-way ANOVA and Tukey’s test (α = 5%). All the adhesives used in the etch-and-rinse mode showed significantly higher bond strength than the adhesives applied in the self-etching approach. The 9 wt% adhesive showed the highest bond strength values, and 3 wt% was most stable after storage. A strong negative correlation between MDP concentration and pH was observed. It was concluded that the formulations with low concentrations of MDP (up to 9 wt%) showed better results for bond strength and bond strength degradation over time.

Resumo O presente estudo teve como objetivo avaliar as propriedades de polimerização de materiais bulk-fill (baixa e alta viscosidade) utilizando luz contínua de alta intensidade e fotoativação intermitente em relação ao estresse de contração de polimerização e grau de conversão (DC). As seguintes resinas compostas Bulk-fill e nanohíbridas convencionais foram avaliadas: Filtek Z350XT Flow (3M/ESPE), SureFil SDR Flow (Dentsply), Filtek Bulk Fill Flow (3M/ESPE), Filtek Z350XT (3M/ESPE) e Filtek Bulk Fill Posterior (3M/ESPE). Um dispositivo de LED (DB 685, Dabi Atlante) foi utilizado nos dois protocolos: fotoativação contínua e intermitente contínua (ciclos de liga e desliga) com exposição idêntica (14 J/cm2). A tensão de contração de polimerização (n=6) foi avaliada através da inserção de um incremento único de 12 mm3 entre duas placas de aço inoxidável (6×2 mm) adaptadas a uma Máquina de Ensaio Universal (UTM), em tempos diferentes. As medições foram registradas após a fotoativação. O grau de conversão foi avaliado por FTIR-ATR (n=5). Os dados foram analisados pelos testes ANOVA a três fatores e teste de Tukey (α=0,05). A resina Bulk Fill Posterior apresentou maiores valores de tensão de contração quando fotoativadas com a técnica intermitente (p<0,05). A fotoativação intermitente aumentou o grau de conversão nas resinas bulk-fill de baixa viscosidade (p<0,05). Portanto, o uso de fotoativação modulada (intermitente) deve ser indicado com cautela, uma vez que seu uso pode influenciar a tensão de contração e o grau de conversão dos compósitos, o que varia de acordo com as formulações da resina.

Abstract This study aimed to evaluate the polymerization properties of bulk-fill materials (low and high-viscosity) by using high-intensity continuous light and intermittent photo-activation in terms of polymerization shrinkage stress and degree of conversion (DC). The following Bulk-fill and Conventional nanofilled resin composites were evaluated: Filtek Z350XT Flow (3M/ESPE), SureFil SDR Flow (Dentsply), Filtek Bulk Fill Flow (3M/ESPE), Filtek Z350XT (3M/ESPE) and Filtek Bulk Fill Posterior (3M/ESPE). A LED device (DB 685, Dabi Atlante) was used for both protocols: continuous uniform and intermittent photo-activation (light-on and light-off cycles) with identical radiant exposure (14 J/cm2). The polymerization shrinkage stress (n=6) was evaluated by inserting a single increment of 12 mm3 between two stainless steel plates (6×2 mm) adapted to a Universal Testing Machine (UTM), at different times. Measurements were recorded after photo-activation. The degree of conversion was evaluated by Fourier transformed infrared spectroscope (FTIR) with an attenuated total reflectance (ATR) accessory (n=5). Data were analyzed by three-way ANOVA and Tukey’s HSD (α=0.05) tests. Bulk Fill Posterior presented higher shrinkage stress values when photo-activated with the intermittent technique (p<0.05). The intermittent photo-activation increased the degree of conversion for the low-viscosity bulk-fills (p<0.05). Therefore, the use of modulated photo-activation (intermittent) must be indicated with caution since its use can influence the shrinkage stress and degree of conversion of composites, which varies according to the resin formulations.

Abstract Extensive restorations in posterior teeth always bring doubts to the clinicians regarding the best protocol, mainly when structures of reinforcement were lost. Objective This study aimed to evaluate the effect of beveling on the fracture resistance and pattern of class II (MOD) restored teeth. Methodology Ninety human premolars were randomly assigned into 9 groups: CTR (control/sound); NC (cavity preparation, non-restored); RU (restored, unbeveled); RTB (restored, entire angle beveling); RPB (restored, partial/occlusal beveling); EC (endodontic access/EA, non-restored); EU (EA, unbeveled); ETB (EA, entire angle beveling); EPB (EA, partial/occlusal beveling). Teeth were restored with Esthet X resin composite and stored in distilled water for 24 h before the inclusion in PVC cylinders. The axial loading tests were performed with 500 kgF at 0.5 mm/min crosshead speed until fracture of the specimens. Fracture resistance and pattern were accessed and data were analyzed using one-way ANOVA and Tukey’s HSD test (α=0.05). Results Mean (±SD) failure loads ranged from 136.56 (11.62) to 174.04 (43.5) kgF in the groups tested without endodontic access. For endodontically accessed teeth, fracture resistance ranged from 95.54 (13.05) to 126.51 (19.88) kgF. Beveling of the cavosurface angle promoted the highest fracture resistance values (p<0.05) and prevented catastrophic fractures. Conclusions Cavosurface angle beveling is capable of improving fracture resistance and pattern for both endodonticaly accessed and non-accessed teeth.

Abstract Bulk-fill composites were introduced in dentistry to accelerate clinical procedures while providing adequate outcomes. Concerns regarding the use of bigger composite increments rely on the polymerization shrinkage and shrinkage stress, which may generate gaps on the adhesive interface and result in a reduced success rate. Objective: To evaluate the polymerization shrinkage stress of different bulk-fill resin composites and their elastic modulus. Materials and Methods: Fourteen specimens were made for each of the nine different resin composites (seven with 12 mm3 and seven with 24 mm3): Surefill SDR flow (SDR), X-tra Base (XB), Filtek Bulk Fill Flowable (FBF), Filtek Z350XT Flow (Z3F); Tetric Evo Ceram Bulk Fill (TBF), X-tra Fil (XF), Filtek Bulk Fill (FBP), Admira Xtra Fusion (ADM) and Filtek Z350 XT (Z3XT). Linear shrinkage stress was evaluated for 300 s with the aid of a linear shrinkage device adapted to a Universal Testing Machine. For each composite group, seven additional specimens (2x2x25 mm) were made and Young's modulus was evaluated with a 3-point bending device adapted in a Universal Testing Machine with 0.5 mm/min crosshead speed and 50 KgF loading cell. Results: For 12 mm3 specimens, three-way ANOVA showed that only SDR and TBF generated lower stress after 20 s. Considering 300 s, TBF, SDR, and XF generated the lowest stress, followed by ADM, FBP, XB, and FBF, which were similar to Z3XT. Z3F generated the highest stress values for all time points. Considering 24 mm3 specimens after 20 s, all bulk fill composites generated lower stress than Z3XT, except XB. After 300 s, SDR, FBP, and ADM generated the lowest stress, followed by TBF and XF. For elastic modulus, one-way ANOVA showed that FBF, SDR, Z3F, and ADM presented the lowest values, followed by XB and TBF. FBP, Z3XT, and XF presented the highest elastic modulus among the evaluated composites. Conclusions: Bulk-fill resin composites presented equal to lower shrinkage stress generation when compared to conventional composites, especially when bigger increments were evaluated. Bulk-fill composites showed a wide range of elastic modulus values, but usually similar to “regular” composites.

Abstract We assessed the effect of a new coating material based on resin-modified glass-ionomer with calcium (Ca) in inhibiting the demineralization of underlying and adjacent areas surrounding caries-like lesions in enamel. The measures used were surface hardness (SH) and cross-sectional hardness (CSH). Thirty-six bovine enamel specimens (3 × 6 × 2 mm) were randomly allocated into three groups (n = 12): No treatment (NT); resin-modified glass-ionomer with Ca (Clinpro XT Varnish, 3M ESPE) (CL), and fluoride varnish (Duraphat, Colgate) (DU). The specimens were subjected to alternated immersions in demineralizing (6 h) and remineralizing solutions (18 h) for 7 days. SH measurements were conducted at standard distances of 150, 300, and 450 µm from the treatment area. CSH evaluated the mean hardness profile over the depth of the enamel surface and at standard distances from the materials. The energy-dispersive X-ray spectroscopy analysis was conducted to evaluate the demineralization bands created on the sublayer by % of calcium (Ca), phosphorus (P), and fluoride (F). Ca/P weight ratio was also calculated. Based on SH and CSH measurements, there was no difference between groups at the distances 150 µm (p = 0.882), 300 µm (p = 0.995), and 450 µm (p = 0.998). Up to 50 µm depth (at 150 µm from the treatment area), CL showed better performance than DU ( p< 0.05). NT presented higher loss of Ca and P than CL and DU (p < 0.05). There was no significant difference in the % of F ion among the three groups. The new coating material was similar to F varnish in attenuating enamel demineralization.

Abstract Objective This study aims to evaluate the effect of sonochemical treatment on the surface of yttria-stabilized tetragonal zirconia (Y-TZP) before and after the final sintering. Material and Methods Twenty-eight Y-TZP discs were divided into four groups (n=7), according to surface treatment: PRE: pre-sintering sonication with 30% nominal power for 15 min; POS: post-sintering sonication with 30% nominal power for 15 min; JAT: air abrasion with 50-μm alumina particles; and CON: control group with no treatment. The POS and JAT groups were sintered before sonication and the PRE group after sonication. Surface roughness was analyzed using confocal microscopy, after which resin cement cylinders were placed on the surface of the Y-TZP discs and subjected to mechanical microshear bond strength test until fracture. Surface roughness and microshear bond strength values underwent ANOVA and the Tukey tests. Results The surface roughness values for the PRE group (299.91 nm) and the POS group (291.23 nm) were not significantly different (p≥0.05), statistically, and the surface roughness value of the JAT group (925.21 nm) was higher than those of PRE and POS (p=0.007) groups. The mechanical microshear bond strength test showed that there was no statistically significant difference between the groups (p=0.08). Conclusions Therefore, the results showed that sonochemical treatment modifies the Y-TZP surface and is similar to the well-established sandblasting surface treatment regarding the strength of the bond with the resin cement.

Abstract Sandblasting is a common method to try to improve the Y-TZP/veneer bond strength of dental prostheses, however, it may put stress on zirconia surfaces and could accelerate the t→m phase transformation. Y-TZP sandblasting before sintering could be an alternative to improve surface roughness and bonding strength of veneering ceramic. Objectives. The aim of this study was to analyze the effect of Y-TZP pre-sintering sandblasting on surface roughness, phase transformation, and the Y-TZP/veneer shear bond strength. Material and Methods. The Y-TZP specimen surface underwent sandblasting with aluminum oxide (50 μm) pre-sintering (Z-PRE) and post-sintering (Z-POS). Z-CTR was not subjected to surface treatment. After ceramic veneer application, the specimens were subjected to shear bond testing. Surface roughness was analyzed by confocal microscopy. Y-TZP monoclinic and tetragonal phases were evaluated by micro-Raman spectroscopy. Shear bond strength and surface roughness data were analyzed by One-way ANOVA and Tukey tests (α=0.05). Differences in the wave numbers and the broadening bands of the Raman spectra were compared among groups. Results. Z-POS (9.73±5.36 MPa) and Z-PRE (7.94±2.52 MPa) showed the highest bond strength, significantly higher than that of Z-CTR (5.54±2.14 MPa). The Ra of Z-PRE (1.59±0.23 µm) was much greater and significantly different from that of Z-CTR (0.29±0.05 µm) and Z-POS (0.77±0.13 µm). All groups showed bands typical of the tetragonal (T) and monoclinic (M) phases. Y-TZP sandblasting before sintering resulted in rougher surfaces but did not increase the shear bond strength compared to post-sintering and increased surface defects. Conclusions. Surface treatment with Al3O2, regardless of the moment and application, improves the results of Y-TZP/veneer bonding and is not a specific cause of t→m transformation.

Resumo O objetivo do presente estudo in vitro foi avaliar a variação de temperatura dentro da câmara pulpar durante a fotoativação de um sistema adesivo e de camadas de resina composta com diferentes fontes de luz. Cavidades com dimensões de 8x10 mm foram preparadas na superfície vestibular de incisivos bovinos deixando uma espessura de dentina remanescente de 1 mm. Os espécimes foram inseridos em uma cuba térmica com água à temperatura de 37±1 °C. A temperatura no interior da câmara foi medida a cada 10 s durante 40 s de ativação de luz do sistema adesivo (SBMP; 3M/ESPE) e três camadas de 1 mm de espessura consecutivas de resina composta (Z250; 3M/ESPE ). Três fonte de luz foram avaliadas: Elipar 2500 (QTH), LD Max (LED de baixa densidade de potência), VALO (LED alta densidade de potência). Os resultados foram submetidos a ANOVA de medidas repetidas a um critério e teste de Tukey (ambos com p<0,01). O aquecimento da reação exotérmica foi observado nos incrementos de resina composta, mas não no sistema adesivo. O LED de alta densidade de potência mostrou uma média de temperatura mais elevada (42,7±1,56 °C) seguido pela luz halogéna (40,6±0,67 °C) e o LED de menor densidade de potência (37,8±0,12 °C). Maiores aumentos de temperatura foram observados na fotoativação do sistema adesivo e do primeiro incremento de resina composta, independente da fonte de luz utilizada. A partir do segundo incremento de resina composta, o material restaurador agiu como estrutura dispersiva de calor, reduzindo o aumento de temperatura. Independente da fonte de luz e da etapa restauradora, a temperatura aumentou com o tempo de irradiação. Pode-se concluir que a fonte de luz, o tempo de irradiação, a espessura resina composta interferiram na variação de temperatura no interior da câmara pulpar.

Abstract The aim of the present in vitro study was to evaluate the temperature variation inside the pulp chamber during light-activation of the adhesive and resin composite layers with different light sources. Cavities measuring 8x10 mm were prepared on the buccal surface of bovine incisors, leaving a remaining dentin thickness of 1 mm. Specimens were placed in a 37±1 °C water bath to standardize the temperature. The temperature in the pulp chamber was measured every 10 s during 40 s of light activation of the adhesive system (SBMP-3M/ESPE) and in the three consecutive 1-mm-thick layers of resin composite (Z250-3M/ESPE). Three light source devices were evaluated: Elipar 2500 (QTH), LD Max (LED low irradiance) and VALO (LED high irradiance). The results were submitted to one-way ANOVA with repeated measures and Tukey's test, both with p<0.001. The exothermic reaction warming was observed in the Z250 increments, but not in the SBMP. The high irradiance LED showed a higher temperature average (42.7±1.56 °C), followed by the quartz-tungsten-halogen light (40.6±0.67 °C) and the lower irradiance LED (37.8±0.12 °C). Higher temperature increases were observed with the adhesive and the first resin composite increment light-activation, regardless of the employed light source. From the second increment of Z250, the restorative material acted as a dispersive structure of heat, reducing temperature increases. Regardless the light source and restorative step, the temperature increased with the irradiation time. It may be concluded that the light source, irradiation time and resin composite thickness interfered in the temperature variation inside the pulp chamber.

Resumo O objetivo do estudo foi avaliar o efeito de tratamentos de superfície em esmalte e dentina na resistência de união (RU) de um cimento auto-adesivo. As coroas de setenta e dois terceiros-molares foram incluídas em resina acrílica e desgastadas para obtenção de áreas planas em esmalte e dentina. Os espécimes de esmalte e dentina foram aleatoriamente distribuídos em 8 grupos (n=12) de acordo com: tratamento de superfície (sem tratamento ou aplicação de solução de ácido poliacrílico a 11,5%), condição do substrato (seco ou úmido) e período de armazenamento (1 dia ou 90 dias). Após, cilindros (1 x 1 mm) foram confeccionados na superfície dos espécimes utilizando cimento resinoso auto-adesivo (Rely X U200) segundo as instruções do fabricante. Os espécimes foram armazenados em água destilada a 37 oC por 1 dia ou 90 dias e submetidos ao ensaio mecânico de microcisalhamento (EMIC DL 2000 a 0,5 mm/min). O tipo de falha de cada espécime foi determinado após ensaio. Os dados foram submetidos à análise estatística (a=0,05). De acordo com os resultados, a aplicação de ácido poliacrílico a 11,5% diminuiu a RU em ambos substratos, esmalte e dentina. Os grupos mantidos úmidos mostraram maiores valores de RU do que os secos, independentemente do substrato ou tratamento de superfície. O período de armazenamento não influenciou nos valores de RU. Concluiu-se que o tratamento de superfície com ácido poliacrílico a 11,5% e a ausência de umidade no substrato diminuíram os valores de RU para o cimento resinoso auto-adesivo, independentemente do período de armazenamento.

Abstract The aim of this study was to evaluate the effect of enamel and dentin surface treatment on the micro-shear bond strength of self-adhesive cement. Seventy-two extracted third molars had their crowns embedded in acrylic resin and worn to obtain a flat enamel or dentin surface. The enamel and dentin specimens were randomly assigned to 8 groups (n=12) that were based on surface treatment (11.5% polyacrylic acid solution or no treatment), substrate condition (wet or dry) and storage period (1 day or 90 days), and treated accordingly. Cylinders (1 × 1 mm) were fabricated using self-adhesive resin cement (RelyX U200) following the manufacturer's instructions. The specimens were stored in distilled water at 37 °C for either 1 day or 90 days and subjected to micro-shear bond strength test (EMIC DL 2000 at 0.5 mm/min). After this, the failure type of the specimens was determined. Data were subjected to statistical analysis (a=0.05). According to the results, the 11.5% polyacrylic acid application decreased the bond strength in both enamel and dentin samples. The moist groups showed higher bond strength than the dry ones, regardless of the substrate and surface treatment. Storage period did not influence bond strength. In conclusion, surface treatment with 11.5% polyacrylic acid and absence of moisture decreased the bond strength of the resin-cement (RelyU200), regardless of the storage period.

Resumo O objetivo deste trabalho foi avaliar o efeito da aplicação de clorexidina 2% (CHX) na resistência de união (RU) ao microcisalhamento de dois sistemas adesivos após armazenagem em diferentes meios. Setenta e duas coroas de molares humanos foram cortadas e incluídas em cilindros de PVC. Os espécimes foram distribuídos aleatoriamente nos grupos (n=12), segundo o sistema adesivo (Ambar e Single Bond 2), uso ou não de CHX e o tempo (24 h e 15 dias) e meio de armazenamento (água destilada, óleo mineral e hipoclorito de sódio 1% - NaOCl). Os sistemas adesivos foram aplicados de acordo com as recomendações do fabricante, com e sem o uso de CHX, e cilindros de resina composta (Z350 XT) foram colocados sobre a dentina já hibridizada. Após a fotoativação, os espécimes foram armazenados em um dos três meios (água destilada, óleo mineral e NaOCl a 1%) a 37 ºC por 24 h e 15 dias. RU foi determinada pelo ensaio de microcisalhamento, com velocidade de 0,5 mm/min. Os dados foram analisados por ANOVA a quatro fatores e teste de Tukey (α=5%). O uso da CHX não provocou perda de RU em nenhuma das situações avaliadas, independentemente do tempo e meio de armazenamento. Não houve influência do meio de armazenamento na RU após 15 dias quando foi utilizado o protocolo adesivo sem a aplicação de CHX. Porém, a utilização de CHX influenciou negativamente os valores de RU para o Single Bond 2 após 15 dias de armazenamento em água destilada e NaOCl a 1%.

The aim of this study was to evaluate the effect of 2% chlorhexidine (CHX) application during the bonding protocol on microshear bond strength of two adhesive systems, after storage in different media. Seventy-two human molars had their crowns cut in half and embedded in PVC cylinders with acrylic resin. The specimens were randomly divided into experimental groups (n=12) according to the adhesive system (Ambar and Single Bond 2), use of CHX in the bonding protocol, and time interval (24 h and 15 days) in the storage media (distilled water, mineral oil and 1% sodium hypochlorite - NaOCl). Adhesive systems were applied in accordance to manufacturers' recommendations, with or without the use of CHX, and resin composite (Z350 XT) cylinders were placed on the hybridized dentin. After photoactivation, the specimens were stored in distilled water, mineral oil and 1% NaOCl for 24 h and 15 days. Microshear bond strength was determined at a crosshead speed of 0.5 mm/min until fracture. The bond strength data were analyzed statistically by 4-way ANOVA and Tukey's test (α=5%). Use of CHX in the bonding protocol did not cause loss of bond strength in any of the evaluated situations, irrespective of time and storage medium. The storage medium had no influence on bond strength values after 15 days when the bond protocol without CHX application was used. However, the use of CHX in the protocol influenced negatively the bond strength values for Single Bond 2 after 15 days storage in distilled water and 1% NaOCl.

Resumo: O objetivo do estudo foi avaliar o efeito da técnica de silanização na resistência de união de cimentos resinosos a uma vitrocerâmica. Trinta e dois discos de vitrocerâmica foram distribuídos em 2 grupos (n=16) (G1: cimento dual e G2: cimento fotoativado) e subdivididos em 4 grupos de acordo com a técnica de silanização. A vitrocerâmica foi condicionada com ácido fluorídrico a 10% por 20 s e o silano aplicado por 1 min de acordo com os subgrupos: CTL: de acordo com as instruções do fabricante, HA: secagem do silano com ar quente, NWA: lavagem e secagem com água e ar a temperatura ambiente, HWA: lavagem e secagem com água e ar quente. Após, o sistema adesivo foi aplicado e polimerizado por 20 s, e cilindros (1 x 1 mm) foram confeccionados com os cimentos sobre a superfície da cerâmica. Os espécimes foram armazenados em água destilada por 48 h e submetidos ao ensaio de microcisalhamento. Os dados foram submetidos à análise estatística (?#61537;=0,05). O grupo G1 apresentou maiores valores de resistência do que G2, exceto no subgrupo CTL e NWA. Houve diferença na técnica de silanização apenas para G1: HWA (25,13±6,83)≥ HA (22,95±7,78)≥ CTL (17,44±7,24)≥ NWA (14,63±8,76). Para G2 não houve diferença entre os subgrupos. Conclui-se que a técnica de silanização interferiu na resistência de união cimento/cerâmica dependendo do material utilizado. A lavagem e secagem com água e ar aquecidos promoveu maior valor de resistência apenas para o cimento dual.

Abstract: The aim of this study was to evaluate the effect of silanization protocols on the bond strength of two resin cements to a lithium disilicate glass-ceramic. Thirty-two ceramic discs were assigned to 2 groups (n=16): G1 - dual-cured resin cement and G2 - light-cured resin cement. Four subgroups were evaluated according to the used silanization protocol. The glass-ceramic was etched with 10% hydrofluoric acid for 20 s and silane was applied for 1 min, as follows: CTL - according to the manufacturer's instructions; HA - dried with hot air; NWA - washed and dried with water and air at room temperature; HWA - washed and dried with hot water and hot air. Thereafter, adhesive was applied and light-cured for 20 s. Silicon molds were used to prepare resin cement cylinders (1x1 mm) on the ceramic surface. The specimens were stored in deionized water at 37 °C for 48 h and subjected to a micro-shear test. The data were submitted to statistical analysis (?#61537;=0.05). Group G1 showed higher bond strengths than G2, except for the CTL and NWA subgroups. Differences as function of the silanization protocol were only observed in G1: HWA (25.13±6.83)≥HA (22.95±7.78)≥CTL(17.44±7.24) ≥NWA(14.63±8.76). For G2 there was no difference among the subgroups. In conclusion, the silanization protocol affected the resin cement/ceramic bond strengths, depending on the material. Washing/drying with hot water and/or hot air increased only the bond strength of the dual-cured resin cement.

Abstract The cementation of thin ceramic veneers employing fluid light-activated resin-based materials is a common procedure in the dental practice. Aim: To evaluate the influence of ceramic thickness and shade on the degree of conversion (DC) of a flowable light-activated material. Methods: flowable resin composite (Tetric N-Flow - shade A1) was light-activated through ceramic discs of two shades (IPS Classic - A1 and A3) in three thicknesses (0.5, 0.7 and 1.0 mm). For control, the resin composite was light-activated without ceramic interposition. DC was evaluated by FTIR (n=5). Data were analyzed by one-way ANOVA and Dunnett's T3 test (α=0.05). Results: Statistically significant differences between groups were observed (p<0.001). Control group (without the interposition of ceramic) showed the highest mean for DC (71.9± 1.7). Considering the interposed ceramic disc groups, the highest DC values were obtained when 0.5 and 0.7 mm A1 ceramics were used (64.6±1.2 and 64.4 5.0, respectively) and the lowest DC values were obtained for 0.7 and 1 mm A3 ceramics (61.74±0.9 and 62.0±1.9, respectively). Conclusions: No flowable resin composite group with interposing ceramics reached a DC similar to the control group.

AbstractObjective This study evaluated the effect of root canal disinfectants on the elimination of bacteria from the root canals, as well as their effect on glass-fiber posts bond strength.Material and Methods Fifty-three endodontically treated root canals had post spaces of 11 mm in length prepared and contaminated with E. faecalis. For CFU/ml analysis, eight teeth were contaminated for 1 h or 30 days (n=4). Teeth were decontaminated with 5% NaOCl, 2% CHX, or distilled water. As control, no decontamination was conducted. After decontamination, sterile paper points were used to collect samples, and CFU/ml were counted. For push-out, three groups were evaluated (n=15): irrigation with 2.5% NaOCl, 2% CHX, or sterile distilled water. A bonding agent was applied to root canal dentin, and a glass-fiber post was cemented with a dual-cured cement. After 24 h, 1-mm-thick slices of the middle portion of root canals were obtained and submitted to the push-out evaluation. Three specimens of each group were evaluated in scanning electron microscopy (SEM). Data were analyzed with one-way ANOVA and Dunnett’s T3 test (α=0.05).Results The number of CFU/ml increased from 1 h to 30 days of contamination in control and sterile distilled water groups. Decontamination with NaOCl was effective only when teeth were contaminated for 1 h. CHX was effective at both contamination times. NaOCl did not influence the bond strength (p>0.05). Higher values were observed with CHX (p<0.05). SEM showed formation of resin tags in all groups.Conclusion CHX showed better results for the irrigation of contaminated root canals both in reducing the bacterial contamination and in improving the glass-fiber post bonding.

There is no consensus about the waiting time necessary for the patient to start consuming beverages containing colorants again after bleaching. Objective: To evaluate the influence of beverages with coloring agents on bleached bovine incisors considering the time elapsed after bleaching. Materials and methods: Sixty bovine incisors were bleached with 35% hydrogen peroxide for in-office use (Whiteness HP Max) and divided into 10 groups. The color was evaluated with a spectrophotometer (Spectro Shade MICRO) before and after bleaching, employing the CIE-Lab system. After bleaching, the teeth were exposed for 5 min to coffee or cola-based soft drink (CBSD) at different periods after bleaching: 10 min, 1 h, 24 h, 48 h, and 72 h. Color (∆E) and lightness (∆L) variations were obtained from the CIE-Lab coordinates. Data were subjected to two-way ANOVA and Tukey HSD tests (p<0.05). Results: Significant differences were observed between groups for both the ∆L and ∆E values (p<0.001). All specimens presented a decrease in brightness (negative ∆L). The highest ∆E values were observed for teeth stained with a CBSD at 10 min and 1 h (4.12 and 4.16, respectively). Teeth pigmented with coffee presented ∆E values below 3.3 units for all evaluation times. Conclusion: The exposure to coffee after bleaching causes less color changes than the exposure to a CBSD regardless of the time after bleaching.

Durante a cimentação de facetas cerâmicas, a polimerização de cimentos resinosos pode ser comprometida se a cerâmica atenuar a irradiância do aparelho fotopolimerizador. O objetivo deste estudo foi avaliar o efeito de diferentes tipos e espessuras de facetas cerâmicas sobre o grau de conversão de um cimento resinoso fotopolimerizável (RelyX Veneer). O cimento foi fotoativado após a interposição de facetas cerâmicas [IPS InLine, IPS Empress Esthetic, IPS e.max LT (baixa translucidez) e IPS e.max HT (alta translucidez) - Ivoclar Vivadent] de quatro espessuras (0,5 mm; 1,0 mm; 1,5 mm e 2,0 mm). Como controle, o cimento foi polimerizado sem interposição de cerâmica. O grau de conversão foi avaliado por espectroscopia FTIR (n=5). Os dados foram analisados através de ANOVA a um critério e teste de Tukey (α=0,05). Foram observadas diferenças significativas entre os grupos (p<0,001). O grau de conversão foi semelhante ao do controle para todos os grupos polimerizados com interposição de cerâmicas de 0,5 mm e 1,0 mm (p>0,05). Entre as facetas de 1,5 mm de espessura, IPS e.max LT foi a única que apresentou resultados diferentes do controle (p<0,05). Com a espessura de 2,0 mm, apenas IPS e.max LT e HT foram capazes de produzir cimentos com grau de conversão semelhantes aos do controle (p>0,05). O grau de conversão do cimento resinoso fotopolimerizável avaliado depende da espessura e do tipo de cerâmica utilizados quando facetas mais espessas do que 1,5 mm são cimentadas.

During the cementation of ceramic veneers the polymerization of resin cements may be jeopardized if the ceramics attenuate the irradiance of the light-curing device. The aim of this study was to evaluate the effect of different types and thicknesses of ceramic veneers on the degree of conversion of a light-cured resin-based cement (RelyX Veneer). The cement was light-cured after interposing ceramic veneers [IPS InLine, IPS Empress Esthetic, IPS e.max LT (low translucency) and IPS e.max HT (high translucency) - Ivoclar Vivadent] of four thicknesses (0.5 mm, 1.0 mm, 1.5 mm and 2.0 mm). As control, the cement was light-cured without interposition of ceramics. The degree of conversion was evaluated by FTIR spectroscopy (n=5). Data were analyzed with one-way ANOVA and Tukey's test (α=0.05). Significant differences were observed among groups (p<0.001). The degree of conversion was similar to the control for all light-cured groups with interposition of ceramics of 0.5 mm and 1.0 mm (p>0.05). Among 1.5-mm-thick veneers, IPS e.max LT was the only one that showed different results from the control (p<0.05). At the thickness of 2.0 mm, only the IPS e.max LT and HT veneers were able to produce cements with degrees of conversion similar to the control (p>0.05). The degree of conversion of the evaluated light-cured resin cement depends on the thickness and type of ceramics employed when veneers thicker than 1.5 mm are cemented.