In the present work, the sol-gel synthesis method was employed as strategy to obtain a magnetic and mesoporous silica-niobia material. The planned synthesis was based on the hetero-condensation of niobium and silicon alkoxide precursors, in the presence of spherical magnetite particles. The resulting material presented interesting characteristics such as magnetism, large mesopores, in the range from 20 to 50 nm, and 68 m2 g-1 of surface area. These features allowed its use as modifier of carbon paste electrode for p-nitrophenol determination, since niobia has never been used in electrochemical sensors for the determination of nitrophenol compounds. By using differential pulse voltammetry technique, the electrode can be applied in a wide range of p-nitrophenol concentration, from 10 to 490 μmol L-1, with a limit of detection of 1.2 µmol L-1 and sensitivity up to 0.60 µA L µmol-1. The proposed electrode presented good sensitivity and selectivity and it was applied in real water samples.

A mesoporous, high surface area and conductive silica/titania graphite composite modified with chitosan and functionalized with tyrosinase was prepared. The composite was obtained by the sol-gel method and the surface of the resultant material was modified with chitosan solutions containing 5, 10 and 15% by mass. The textural characterization showed that even after modification with chitosan, the composite maintains a pore volume near 0.70 cm3 g-1 and pore diameter between 10 and 50 nm, adequate for enzyme immobilization. The tyrosinase was immobilized on the composite that was modified with 5% chitosan solution. A carbon ceramic electrode was manufactured with this material and was used as an electrochemical biosensor for phenolic compounds, showing low detection limits in the linear range from 40 to 350 µmol L-1 and good sensitivity of 0.284, 0.141 and 0.165 µA µmol-1 L for catechol, dopamine and pyrogallol, respectively. In this composite the enzyme showed to be operative and stable after several months.

In this work, we report the preparation of a copper-silica material (Cu/SiO2) by a sol-gel methodology and its characterization concerning composition and textural properties. The Cu/SiO2 material was successfully applied as a Lewis acid heterogeneous catalyst for the A3-coupling from 2-aminopyridine, aldehydes and alkynes to imidazo[1,2-a]pyridines (45-82%), which are relevant pharmacological scaffolds. The synthesis shows a number of advantages, such as easy separation from the reaction media and the minimal formation of metal aqueous wastes. Investigation of the mechanism supports the involvement of the formation of reaction intermediates inside the pores of the mesoporous material prior to 5-exo-dig cyclization.

We carried out the physico-chemical characterization of Immobead 150, a hydrophobic support for the immobilization of lipases. Thermomyces lanuginosus lipase (TLL) was immobilized on Immobead 150 by multipoint covalent attachment (ImmTLL) and the morphological, textural, structural, thermal, and physico-chemical properties of the support, before and after enzyme immobilization, were investigated. Immobead 150 presents approximately 1,000 µmol of epoxy groups per gram of support, a high hydrophobicity, and good thermal stability. The spherical particles of Immobead 150 present average diameters of 155 µm, specific surface areas of 137 m2 g-1 and pore volumes of 0.37 cm3 g-1, showing pores in the region of the micro and meso sizes. The immobilization process of TLL (150 mg g-1) caused a decrease of the specific area and pore volumes, to 63 m2 g-1 and 0.25 cm3 g-1, respectively, as a result of coating of the support surface by the enzyme molecule. However, the immobilization process did not affect the morphology of the support. The obtained biocatalyst was effective for the syntheses of fatty acid ethyl esters (biodiesel), and of aroma esters, showing yields of 68 and 70%, respectively, similar to commercial preparations used as controls.

Thin films containing silver nanoparticles homogeneously dispersed, with narrow size distribution below 10 nm, were synthesized on flat glass surface, by using an ionic silsesquioxane as stabilizer and crosslinking agent. The films can be prepared without previous functionalization of substrate surfaces and without addition of other components. The films were heat treated up to 200 ºC and characterized by ultraviolet-visible, transmission electron microscopy, atomic force microscopy, thermogravimetric analysis and ellipsometry. The films were thermally stable when heated up to 200 ºC, presenting the same thickness, and maintaining both optical and morphological properties of silver nanoparticles. The antibacterial activity of the films, containing the silver nanoparticles, was evaluated against Staphylococcus aureus by using the film applicator coating method, showing an excellent performance even after the third cycle of sterilization.

This review deals with silica based hybrid materials obtained by the sol-gel method. It involves concepts, classifications and important definitions regarding the sol-gel method that allows obtaining materials with organic and inorganic components dispersed in a molecular or nanometric level. We discuss the properties and characteristics of hybrid materials related to experimental synthesis conditions. We devote a special attention to the nanostructured materials, where the self-organization is imposed by the organic component. Finally, we present some important applications of these materials based on their specific properties.

Uma nova série de amostras de material híbrido à base de sílica, contendo o grupo catiônico amoniopropil ligado na forma pendente, foi obtida usando-se o método sol-gel de síntese, variando-se a razão molar entre o precursor inorgânico e o precursor orgânico. A análise termogravimétrica mostrou que as amostras são termicamente estáveis até 260 ºC. Os resultados obtidos por difratometria de raios X, microscopia eletrônica de transmissão, ressonância magnética nuclear de 29Si e análise elementar são compatíveis com o modelo estrutural de camadas de silsesquioxano com distâncias basais de até 5,4 nm, contendo sílica amorfa no espaço entre as camadas.

An innovative series of silica-based hybrid materials containing pendant cationic ammoniumpropyl groups was obtained using the sol-gel method, by varying the molar ratio of the inorganic and organic precursors. Thermogravimetric analysis showed that samples were thermally stable up to 260 ºC. Results obtained by X-ray diffractometry, transmission electron microscopy, 29Si nuclear magnetic resonance and elemental analysis were compatible with a silsesquioxane layered structural model showing basal distances up to 5.4 nm, containing amorphous silica in the interlayer space.

Silica gel was chemically modified with the aromatic amines p-anisidine, p-phenytidine and p-phenylenediamine, using grafting reactions. The resulting modified silicas were characterized by infrared spectroscopy and N2 adsorption/desorption isotherms. The organic groups were covalently immobilized in a monolayer form. These modified silicas were investigated as adsorbents for Pb2+, Cu2+, Cd2+ and Ni2+ in aqueous and ethanol solutions. In a general way, the adsorption capacity values for all adsorbents presented the following sequence: Pb2+ >> Cu2+ <FONT FACE=Symbol>@</FONT>Cd2+ <FONT FACE=Symbol>@</FONT> Ni2+. Adsorption studies for all adsorbents, in competitive medium, showed better selectivity for Cu2+ and Pb2+ in aqueous medium and for Pb2+ in ethanol solution. Desorption studies were carried out using HCl and HNO3 as eluents.

Neste trabalho, o corante azul de metileno foi imobilizado na superfície do acetato de celulose modificado com dióxido de titânio produzindo um material híbrido sólido denominado de CA-TiO2MB. O experimento produziu uma quantidade de 1,8 mmol g-1 de TiO2 incorporado no acetato de celulose e uma quantidade de 0,170 ± 0,005 mmol g-1 de azul de metileno adsorvido na superfície do CA-TiO2. Um eletrodo de pasta de carbono desse material foi usado para estudar a oxidação eletrocatalítica do ácido ascórbico pelas técnicas de voltametria cíclica e cronoamperometria. O pH da solução não afetou o potencial de pico de anódico nem a corrente de pico anódico ao variar de 3,0 a 7,0. A oxidação do analito ocorreu em 75 mV versus ECS em solução de KCl 1,0 mol L-1 e pH 7,0. A intensidade da corrente de pico anódico variou com a concentração de ácido ascórbico na faixa de 5,0 × 10-4 mol L-1 to 4,5 × 10-3 mol L-1, sendo observada uma correlação linear com um limite de detecção de 15 µmol L-1, limite de quantificação de 50 µmol L-1 e uma sensibilidade de 7,1 µA L mol-1. A resposta do eletrodo foi muito rápida, com um tempo decorrido de 1,0 s, mostrando potencial para ser utilizado como um sensor eletroquímico para a determinação de ácido ascórbico em produtos comerciais.

In this work, methylene blue dye was immobilized on the surface of cellulose acetate modified with titanium dioxide, producing a solid hybrid material designated as CA-TiO2MB. The experiment yielded an amount of 1.8 mmol g-1 of TiO2 incorporated in the cellulose acetate and an amount of 0.170 ± 0.005 mmol g-1 of methylene blue adsorbed onto CA-TiO2 surface. A carbon paste electrode of this material was used to study the electrocatalytic oxidation of ascorbic acid by cyclic voltammetric and chronoamperometric techniques. The pH of the solution had no effect on the anodic peak potential and anodic peak current when ranging from 3.0 to 7.0. The oxidation of the analyte occurred at 75 mV versus SCE in 1.0 mol L-1 KCl solution and pH 7.0. The intensity of the anodic peak current varied with the concentration of ascorbic acid from 5.0 × 10-4 mol L-1 to 4.5 × 10-3 mol L-1 and a linear correlation was observed, with a detection limit of 15 µmol L-1, quantification limit of 50 µmol L-1 and a sensitivity of 7.1 µA L mol-1. The electrode response was very fast, with an elapsed time of about 1.0 s, showing the potentiality to be utilized as an electrochemical sensor for determination of ascorbic acid in commercial samples.

Nesse trabalho foi estudada a influência do ácido acético na estrutura de poros e na área superficial de sílicas preparadas pelo método sol-gel. Condições experimentais de síntese, tais como temperatura de policondensação e solventes, também foram estudadas. Isotermas de adsorção de N2 das amostras foram classificadas como do tipo 1, típicas de materiais microporosos, o que explica os altos valores de área superficial obtidos. A adição simultânea dos ácidos acético e clorídrico como catalisadores e de acetona como solvente, bem como o emprego de uma temperatura de policondensação de 20 ºC, possibilitaram a preparação de sílicas amorfas com valores de área superficial de até 850 m² g-1. O alto valor de área superficial dessas amostras pode ser explicado principalmente pela microporosidade e também pelo tamanho nanométrico das partículas.

The influence of acetic acid on the pore structure and surface area of silica prepared by the sol-gel method was investigated. Experimental conditions of synthesis, such as gelation temperature and solvents, were also studied. N2 adsorption isotherms of the samples were type 1, typical of microporous materials, explaining the high surface area values (BET) observed. The simultaneous addition of acetic and hydrochloric acids as catalysts and of acetone as solvent, together with the use of a gelation temperature of 20 ºC, made it possible to prepare amorphous silica materials with surface area values up to 850 m² g-1. The high surface area value of these samples could be explained by the microporosity and the nanometric size of the particles.

As propriedades eletroquímicas dos corantes catiônicos, azul de meldola e azul de toluidina, imobilizados na superfície do acetato de celulose modificado com dióxido de titânio foram investigadas por voltametria cíclica. Os materiais sintetizados foram empregados como eletrodos de pasta de carbono. As propriedades mediadoras redox dos eletrodos modificados quimicamente com azul de meldola e azul de toluidina foram otimizadas utilizando um planejamento fatorial consistindo de dois níveis e quatro fatores com dois pseudo-pontos centrais (n=20 experimentos). A análise fatorial foi realizada para investigar as melhores condições de reversibilidade do processo redox tais como uma diminuição na separação entre os picos de potenciais anódico e catódico e razão de corrente próxima da unidade. Os fatores que apresentaram efeitos significantes na otimização global do sistema e que permitiram alcançar as melhores condições de reversibilidade de transferência de elétrons foram os fatores principais velocidade de varredura e tipo de eletrodo (azul de meldola ou azul de toluidina) além dos fatores de interação concentração do KCl × tipo de eletrodo (B×D) e a interação pH × [KCl] × velocidade de varredura (A×B×C). As melhores condições de reversibilidade eletroquímica obtidas foram: o eletrodo CA-TiO2-MB, KCl 1,0 mol L-1 como eletrólito suporte e velocidade de varredura de 10,0 mV s-1. Adicionalmente, o eletrodo modificado CA-TiO2-MB foi testado como sensor amperométrico para a determinação de NADH com um limite de detecção de 0,1 µmol L-1.

The electrochemical properties of meldola blue and toluidine blue cationic dyes immobilized on cellulose acetate surface modified with titanium dioxide were investigated by cyclic voltammetry. The materials synthesized were employed as carbon paste electrodes. The redox mediator properties of the meldola blue and toluidine blue chemically modified electrodes were optimized using a factorial design, consisting of two levels and four factors with two pseudo-central points (n= 20 experiments). The factorial analysis was carried out by searching for better reversibility of the redox process, such as the lowest separation between anodic and cathodic potential peaks and a current ratio near unity. The factors that presented significant effects on the overall optimization of the system to achieve the best conditions of the reversibility of electron transfer were the main factors scan rate and type of electrode (meldola blue or toluidine blue), besides the interaction factors KCl concentration × type of electrode (B×D) and the pH × [KCl] concentration × scan rate (A×B×C) interaction. The best electrochemical reversibility conditions obtained were: using the CA-TiO2-MB electrode, 1.0 mol L-1 KCl as supporting electrolyte, at scan rate of 10.0 mV s-1. Afterwards, the CA-TiO2-MB modified electrode was tested as an amperometric sensor for the determination of NADH, with a detection limit of 0.1 µmol L-1.

The influences of the spray-drying parameters and the type of nanoparticles (nanocapsules or nanospheres) on the characteristics of nanoparticle-coated diclofenac-loaded microparticles were investigated by using a factorial design 3². Gastrointestinal tolerance following oral administration in rats was evaluated. Formulations were selected considering the best yields, the best encapsulation efficiencies and the lowest water contents, presenting surfaces completely coated by nanostructures and a decrease in the surface areas in relation to the uncoated core. In vitro drug release demonstrated the influence of the nanoparticle-coating on the dissolution profiles of diclofenac. Nanocapsule-coated microparticles presented a protective effect on the gastrointestinal mucosa.

The electrochemical properties of methylene blue immobilized on cellulose/TiO2 and mixed oxide SiO2/TiO2 matrices were investigated by means of cyclic voltammetry. The electron mediator property of the methylene blue was optimized using a factorial design, consisting of four factors in two levels. The experimental observations and data analyses on the system indicate that the lowest peak separation occurs for Sil/TiOAM, 1.0 mol L-1 KCl solution and 20 mV s-1 scan rate, while values of current ratio closest to unity were found for Cel/TiOAM independent of electrolyte concentration, 0.2 or 1.0 mol L-1, and scan rate, 20 mV s-1 or 60 mV s-1.

Micropartículas com revestimento nanoestruturado, contendo diclofenaco, foram preparadas e caracterizadas apresentando um rendimento de 80% e taxa de encapsulação de 83%. A análise morfológica (MEV) permitiu a visualização de nanoestruturas adsorvidas à superfície das micropartículas, que apresentaram uma diminuição da área superficial e do volume de poros em relação ao núcleo. A liberação in vitro do fármaco (pH 5,0 e 7,4) mostrou eficiência de dissolução de 34% e 78% (núcleo), 74% e 83% (mistura física), e 58% e 85% (micropartículas nanorrevestidas), respectivamente. A modelagem matemática mostrou os modelos biexponencial (pH 5,0) e monoexponencial (pH 7,4) como aqueles que melhor descreveram os perfis de liberação. Na tolerância digestiva, os índices lesionais totais foram de 156,1 ± 48,5 para a solução do diclofenaco sódico, de 132,4 ± 45,7 para o núcleo, de 109,1 ± 35,8 para a mistura física e de 29,9 ± 12,1 para as micropartículas, demonstrando o efeito protetor destas micropartículas frente à toxicidade do diclofenaco. Esta estratégia de revestimento apresenta um emprego potencial no desenvolvimento de sistemas de administração oral de fármacos.

This work reports the preparation and characterization of polymeric nanostructure-coated diclofenac-loaded microparticles. After spray-drying, powders presented 80% of yield and encapsulation efficiency of 83%. SEM analyses showed nanostructures adsorbed onto the surface of microparticles presenting surface area (BET) and pore volumes (BJH) (83 m² g-1, 0.10 cm³ g-1) smaller than the uncoated-core (163 m² g-1, 0.25 cm³ g-1). In vitro drug release experiments at pH 5.0 and 7.4 showed dissolution efficiencies of 34% and 78% (uncoated-core), 74% and 83% (physical mixture of raw materials), and 58% and 85% (nanostructure-coated microparticles), respectively. Mathematical modeling of the dissolution profiles fitted a biexponential model at pH 5.0 and a monoexponential model at pH 7.4. Regarding the digestive tolerance experiments, the total lesional indexes were 156.1 ± 48.5 for sodium diclofenac aqueous solution, 132.4 ± 45.7 for uncoated-core, 109.1 ± 35.8 for physical mixture and 29.9 ± 12.1 for microparticles showing a protective effect of these microparticles against the mucosal diclofenac damage. This strategy of coating presents a potential use for oral administration of drugs.

Aluminum oxide was dispersed on a commercial silica gel surface, using successive grafting reactions. The reaction products were characterized by N2 adsorption-desorption isotherms, scanning electron microscopy and infrared spectroscopy. The progressive incorporation of aluminum, up to 5.5% (w/w), does not produce agglomeration of alumina, since changes in the original pore size distribution of the silica matrix were not observed. The aluminum oxide covers homogeneously the silica surface.