Abstract During the last few years, researchers have demonstrated steel fiber reinforced concrete as a promising composite. This composite can replace part of the conventional reinforcement such as like stirrups in beams once the steel fiber increases the shear strength and stiffness, reducing the possibility of sudden rupture. An experimental study was conducted to evaluate the influence of the addition of steel fiber in the nominal shear strength and failure mode of reinforced concrete beams without transverse reinforcement to the variation of longitudinal reinforcement ratio, steel fiber content and concrete compressive strength. A total of twelve beams were tested using a four point bending test. The experimental results indicated that the use of hooked steel fiber increase the shear strength of beams and alter the pattern of cracks with the formation of at least two diagonal cracks and a greater number of bending cracks providing a warning of the impending beam failure.

Resumo Nos últimos anos, pesquisas demonstram o concreto reforçado com fibras de aço como um compósito promissor que pode substituir parte das armaduras convencionais como estribos em vigas, uma vez que as fibras de aço aumentam a resistência ao cisalhamento e tenacidade, o que reduz a possibilidade de ruptura súbita. Neste trabalho foi desenvolvida uma pesquisa experimental para avaliar a influência da adição da fibra de aço na resistência ao cisalhamento e modo de ruptura de vigas de concreto armado sem armadura transversal com a variação da taxa de armadura longitudinal, teor de fibras de aço e resistência do concreto à compressão. Um total de doze vigas foi ensaiado à flexão em quatro pontos. Os resultados experimentais encontrados indicaram que o uso de fibras de aço com ganchos nas extremidades aumentam a resistência ao cisalhamento em vigas e alteram o padrão de fissuração com a formação de pelo menos duas fissuras diagonais e maior número de fissuras de flexão, que proporcionam uma ruptura mais avisada.

Abstract The elastic modulus is an important property for professionals in the construction industry, since its value is crucial for deformation control. This study evaluates the elastic modulus of three different classes of concrete (C20, C30 and C40), produced with two lithologic types of rocks, basalt and dolomite, from the Triângulo Mineiro region, Brazil. In the experimental study, 324 cylindrical test specimens were cast. The experimental results of the elastic modulus were compared to six formulations proposed in four concrete norms and codes: ABNT NBR 6118, version 2007 and 2014, ACI 318, EUROCODE 2, FIB Model Code and IBRACON (2003). The elastic modulus values obtained with the formulation proposed by FIB Model Code (2010) and ABNT NBR 6118 (2014) were closest to the experimental results of this study.

Resumo O módulo de elasticidade do concreto é uma propriedade importante para os profissionais envolvidos na indústria da construção civil, uma vez que seu valor é determinante para o controle das deformações. Este trabalho avaliou o módulo de elasticidade de três classes distintas de concreto (C20, C30 e C40) produzidas com dois tipos litológicos de rochas, basalto e dolomito, de diferentes jazidas da região do Triângulo Mineiro. Como parte do estudo experimental, foram moldadas 324 amostras cilíndricas de 10 cm × 20 cm. Os valores de módulo de elasticidade obtidos foram comparados com seis formulações propostas em quatro normas, institutos e códigos do concreto: ABNT NBR 6118 versão 2007 e 2014, ACI 318, EUROCODE 2 and FIB Model Code, Ibracon 2003. Dentre as formulações propostas pelas normas, as indicadas pela FIB Model Code (2010) e ABNT NBR 6118 (2014) apresentaram valores mais próximos aos resultados experimentais deste estudo.