Selective laser melting (SLM) is an additive manufacturing process used to produce parts with complex geometries layer by layer. This rapid solidification method allows fabricating samples in a non-equilibrium state and with refined microstructure. In this work, this method is used to fabricate 3 mm diameter rods of a Cu-based shape memory alloy. The phase formation, thermal stability and mechanical properties were investigated and correlated. Samples with a relative density higher than 92% and without cracks were obtained. A single monoclinic martensitic phase was formed with average grain size ranging between 28 to 36 μm. The samples exhibit a reverse martensitic transformation temperature around 106 ± 2 °C and a large plasticity in compression (around 15±1%) with a typical “double-yielding” behaviour.

The effect of minor additions of Gd and Sm on the glass-forming ability (GFA) of Cu-Zr-Al alloys is investigated here. The rationale for these additions is the fact that the atomic size distribution can increase GFA by changing the topology of the alloy as a function of cluster stability, which is tied to the electronegativity and ionic and covalent nature of alloys. Ingots with nominal compositions of Cu40Zr49Al10.5Gd0.5, Cu40Zr49Al10.5Sm0.5 and Cu39Zr50Al9Gd2 were prepared by arc-melting and rapidly quenched ribbons were produced by the melt-spinning technique. Bulk samples with a thickness of up to 10 mm were also produced by casting, using a wedge-shaped copper mold. The samples were characterized by differential scanning calorimetry, X-ray diffractometry and scanning electron microscopy. The three compositions showed a fully amorphous structure in the ribbons and a predominantly homogeneous amorphous structure with a thickness of up to 10 mm, although some gadolinium oxide crystals as well as samarium compounds were found to be scattered in the amorphous matrix in 5-mm-thick samples. The amorphous phases in the alloys showed high thermal stability with a supercooled liquid region (ΔTx) of about 70 K.