Sol-gel modified Pechini's method was used to prepare WO3 nanopowders using dicarboxylic acid and polyethylene glycol as the chelating agent and polymeric source, respectively. WO3 powders were first prepared by calcination of resin precursor at 550ºC under various initial concentrations of metal ion (12.5-50 mmol), acid (125-500 mmol), a complexing agent (32-262 mmol), and polyethylene glycol (1-16.5 mmol) in the air atmosphere. The products were characterized using X-ray powder diffraction, field emission scanning electron microscopy, and energy dispersive spectroscopy. The results revealed that the WO3 nanopowders prepared with different amounts of chelating agent and polyethylene glycol, crystallized in monoclinic phase. The nanopowders were impurity-free due to the presence of the complexing agent and polyethylene glycol as carbon sources. Morphological evolution indicated that the nanopowders evolved from rod-like to regular and spherical shapes, depending on complexing agent and polyethylene glycol amounts. Nanopowders with an average particle size of approximately 58 nm and a narrow size distribution were obtained.

Effect of calcium addition on microstructure, hardness value and corrosion behavior of five different Mg-xCa binary alloys (x = 0.7, 1, 2, 3, 4 wt. (%)) was investigated. Notable refinement in microstructure of the alloy occurred with increasing calcium content. In addition, more uniform distribution of Mg2Ca phase was observed in a-Mg matrix resulted in an increase in hardness value. The in-vitro corrosion examination using Kokubo simulated body fluid showed that the addition of calcium shifted the fluid pH value to a higher level similar to those found in pure commercial Mg. The high pH value amplified the formation and growth of bone-like apatite. Higher percentage of Ca resulted in needle-shaped growth of the apatite. Electrochemical measurements in the same solution revealed that increasing Ca content led to higher corrosion rates due to the formation of more cathodic Mg2Ca precipitate in the microstructure. The results therefore suggested that Mg-0.7Ca with the minimum amount of Mg2Ca is a good candidate for bio-implant applications.