In this work we present results and analysis concerning the processing and characterization of Gallium Nitride (GaN) thin films (TF) grown on Si (111) substrates by pulsed laser deposition technique (PLD), which were analyzed by X-ray diffraction (XRD), scanning electron microscopy (SEM), photoluminescence (PL) and Raman spectroscopy (RS). The GaN films showed the hexagonal phase with a preferential orientation in the (100) direction, SEM pictures showed a cauliflower-like morphology. Room temperature PL studies showed the so called GaN-yellow band, at 2.29 eV, as well as the donor-acceptor (DA) pair luminescent transition around 3.0 eV. At 10 K, phonon replicas, separated by 69 meV, were observed. By RS, the optical mode on 710 cm-1 was observed, corresponding to the longitudinal optical phonon, A1(LO), as reported for this material.

Ammonobasic reactive sublimation (ARS) is proposed as a novel method to synthesize GaN and related oxides. Results indicate that GaN growth occurs by a nitriding process of Ga and related oxides, establishing a direct dependence on NH4OH amount added as a primary chemical reactive. The samples were grown on p-type Si (111) substrates inside a tube furnace, employing GaN powder and NH4OH. The characterizations of the samples were carried out by XRD, SEM, EDS and PL techniques, revealing the influence of NH4OH on the improvement of GaN synthesis and the enhancement of its optical and structural properties.