The decomposition of the solid solution of potassium jarosite with chromium(VI) in Ca(OH)2 media was studied in the present work. According to experimental results, the incorporation of CrO42- into the crystal structure of jarosite resulted in a solid solution with the following approximate formula: [K0.86(H3O)0.14]Fe2.67[(SO4)1.23(CrO4)0.77][(OH)5.01(H2O)0.99]. The experimental data describe a reaction based on the shrinking core model with chemical control for spherical particles. A reaction order of n = 0.67 and an activation energy (Ea) of 63.75 kJ mol-1 were obtained in the induction period (tind). The progressive conversion period is characterized by the diffusion of K+, SO42- and CrO42- ions into the solution. In this stage, n = 1.99 with respect to OH-, and Ea = 51.56 kJ mol-1. The CrO42- diffusion is slower compared to that of sulfate, a slight amount of chromate is adsorbed in the layer of the solid residue consisting on Fe(OH)3. Finally, the equations that satisfactorily describe the reaction process were established from the data obtained.

Objective This study evaluated the hydrophobicity of dentin surfaces that were modified through chemical silanization with octadecyltrichlorosilane (OTS). Material and Methods An in vitro experimental study was performed using 40 human permanent incisors that were divided into the following two groups: non-silanized and silanized. The specimens were pretreated and chemically modified with OTS. After the chemical modification, the dentin hydrophobicity was examined using a water contact angle measurement (WCA). The effectiveness of the modification of hydrophobicity was verified by the fluid permeability test (FPT). Results and Conclusions Statistically significant differences were found in the values of WCA and FPT between the two groups. After silanization, the hydrophobic intraradicular dentin surface exhibited in vitro properties that limit fluid penetration into the sealed root canal. This chemical treatment is a new approach for improving the sealing of the root canal system.