This study evaluates the properties of chitosan (CS) membranes modified with different percentages (0.5%, 3%, and 5% w/w) of a graphene-based material. Graphene oxide (GO) and reduced graphene oxide (RGO) were obtained by the chemical exfoliation of graphite and thermal reduction. Then, they were characterized by electrical conductivity measurements, FESEM, XRD, AFM, and Raman spectroscopy. The composites’ morphology was evaluated by FESEM. The degree of swelling over a 48 h period and mass loss behavior in phosphate-buffered saline solution for up to 70 days were also studied. The hydrophilicity of the CS and CS/graphene nanocomposites was examined by water contact angle. The graphene materials showed small stacks (6-8 sheets) with low defect density and nanoscale thickness (1.3-5.9 nm). The dispersion of the graphene material in the CS matrix significantly decreased the degree of swelling (460%) but did not modify the hydrolytic degradation process and the hydrophilicity of membranes.

Abstract Cashew nut shell liquid (CNSL) is an abundant and renewable by-product of the cashew nut industry. It appears to be a valuable raw material for generating semiconductive polyaniline (PAni) nanomaterial with enhanced thermal stability and well-defined nanofiber morphology following a polymerization dispersion process. This study confirms that CNSL acts as a soft template during PAni synthesis, leading to an improvement in the nanofiber aspect. CNSL also improves the thermal stability of the PAni nanomaterial. Moreover, CNSL is an effective surfactant that promotes and stabilizes the dispersion of PAni nanofibers within water, allowing the more ecofriendly preparation of PAni nanomaterial by substituting the commonly used organic solvent with aqueous media. Finally, although CNSL promotes the formation of the conductive emeraldine salt form of PAni, increasing CNSL concentrations appear to plasticize the PAni polymer, leading to reduced electrical conductivity. However, this reduction is not detrimental, and PAni nanofibers remain semiconductive even under high CNSL concentrations.

This work aimed to produce graphene oxide with few graphene layers, a low number of defects, good conductivity and reasonable amount of oxygen, adequate for use as filler in polymeric composites. Two starting materials were evaluated: expanded graphite and graphite flakes. The method of oxidation used was the Staudenmaier one, which was tested over different lengths of time. No appreciable differences were found among the oxidation times and so the lowest oxidation time (24 h) was chosen as the most adequate. An investigation was also conducted into suitable temperatures for the reduction of graphite oxide. A temperature of 1000 ºC gave the best results, allowing a good quality material with few defects to be obtained. The reduction was also evaluated under inert and normal atmosphere. The best results were obtained when the least modified material, e. g., graphite flakes, was used as a starting material, oxidized for 24h and reduced at 1000 ºC for 30 s in a quartz ampoule under a normal atmosphere.

A new titanium catalyst easily synthesized from ethylmaltol bidentate chelator ligand was studied in homogeneous and heterogeneous ethylene polymerization. The dichlorobis(3-hydroxy-2-ethyl-4-pyrone)titanium(IV) complex was characterized by 1H and 13C NMR (nuclear magnetic resonance), UV-Vis and elemental analysis. Theoretical study by density functional theory (DFT) showed that the complex chlorines exhibit cis configuration, which is important for the activity in olefin polymerization. The complex was supported by two methods, direct impregnation or methylaluminoxane (MAO) pre-treatment, in five mesoporous supports: MCM-41 (micro and nano), SBA-15 and also the corresponding modified Al species. All the catalytic systems were active in ethylene polymerization and the catalytic activity was strongly influenced by the method of immobilization of the catalyst and the type of support.

The difficult processability of polyaniline (PAni) can be overcome by preparing composites with high density polyethylene (HDPE), resulting in a conducting material with improved mechanical properties. PAni nanofibers were synthesized in this research using a rapid mixing method, while HDPE/PAni composites were prepared by in situ polymerization using Cp2ZrCl2/MAO as a catalyst system. Different experimental conditions for polymerization and an electrochemical study were performed. The findings confirmed that the addition of small amounts of Pani (up to 7%) and longer impregnation (120 min) with methylaluminoxane (MAO) before polymerization are important factors contributing to increased catalytic activity. Analysis by cyclic and differential pulse voltammetry indicates that MAO reacts with the PAni in the ethylene polymerization process, and forms active species in the presence of the catalyst. Changes in catalytic activity may be due to the kinetic consumption of the active species, which become less important in the presence of PAni.