The analysis of supramolecular arrangement is essential to understand the role of this key factor on the optical and electrical properties of organic thin films. In this work, thin solid films of bis(phenethylimido) perylene (PhPTCD) fabricated using physical vapor deposition (PVD) technique (thermal evaporation), deposited simultaneously onto different substrates (Ag mirror, Ge, and quartz plates) contingent on the characterization technique. The main objective is to study the PhPTCD supramolecular arrangement and the thermal stability of this arrangement in PVD films. The ultraviolet-visible absorption reveals a controlled growth of the PVD films, and the micro-Raman scattering data show that the PhPTCD molecule is not thermally degraded in the conditions of these experiments. The microscopy also shows a homogeneous morphological surface of the PVD film at macro and micro scales, with molecular aggregates at nanoscale. Besides, the PVD film roughness does not follow substrate roughness. The X-ray diffraction indicates a crystalline structure for PhPTCD powder and an amorphous form for PhPTCD PVD film. The infrared absorption spectroscopy points to a preferential flat-on organization of the molecules in the PVD films. In addition, the annealing process (200 ºC for 20 minutes) does not affect the supramolecular arrangement of the PhPTCD PVD films.

The supramolecular structure of organic thin films is a key factor in their optical and electrical properties and, consequently, in the technological applications involving organic electronic. Here, thin films of a perylene derivative, the bis butylimido perylene (BuPTCD), were produced by vacuum thermal evaporation (PVD, physical vapor deposition). The main objective is to investigate the supramolecular structure of the BuPTCD in these PVD films, which implies to control their thickness at nanometer scale and to determine their molecular organization, morphology at micro and nanometer scales and crystallinity. The ultraviolet-visible absorption reveals a uniform growth of the PVD films. The optical and atomic force microscopy images show a homogeneous surface of the film at micro and nanometer scales, respectively. The X-ray diffraction indicates that both powder and PVD film are in the crystalline form. Complementary, a preferential head-on orientation of the molecules in the PVD films is determined via infrared absorption spectroscopy. Besides, the annealing process (200oC) did not affect the molecular organization of the PVD films, revealing a thermal stability of the BuPTCD molecules within the PVD films. Through DC electrical measurements, an electrical conductivity of 7.45x10-10 S/m was determined for BuPTCD PVD films onto Au interdigitated electrodes (IDE-structured devices), which can be enhanced, under illumination, by two orders of magnitude (photoconductivity effect). As proof-of-concept, the IDE-structured devices are tested as gas sensor for trifluoroacetic acid.