ABSTRACT This research aimed to evaluate the effect of the number of fatigue cycles (NC, 0 – reference, 450, 4500, 45000, and 90000) for frequencies (Fr) of oscillation equal to 0.5 and 1.0 Hz on the modulus of elasticity (Em) and operating stress (σm) in the static bending of Pinus caribaea wood. Em and σm were determined taking into account three specimens (SPEC) manufactured for reference condition and another three for each of the four NC levels and each Fr level, resulting in 27 SPEC. Sixty experimental determinations were obtained, being the approximate total time of sample exposure to fatigue of 350 hours. The same specimens used to determine Em and σm for the reference condition were also used (via non-destructive tests) to obtain these properties for all fatigue cycles. The frequency and number of cycles significantly influenced both investigated properties. Reductions in Em and σm values were observed after 45000 cycles. The progressive increase in the number of fatigue cycles caused more marked reductions in mechanical properties when compared to the increase in the frequency of oscillation.

ABSTRACT Wood has been used for several purposes such as in civil and rural construction. Knowing wood mechanical behavior under short-term loading is essential for safer structural designs. However, wood toughness is a mechanical property little investigated for this purpose. Thus, this study aimed to evaluate, using exponential and polynomial regression models (linear, quadratic, and cubic), the possibility of estimating toughness as a function of apparent density, compression parallel to grain strength, and modulus of rupture in static bending. Thirty-six Brazilian tropical wood species from south of Roraima, Mato Grosso do Sul, and north and northeast of Mato Grosso were tested. Our results showed the significance and representativeness of all investigated fits, among which a cubic polynomial function is the most indicated for wood toughness estimates.

ABSTRACT Wood is one of the main materials used in the constructing of covering structures (roofs) because of its versatility. Under this situation, due to solar radiation incidence, the temperature can exceed 60 °C and, such as other environmental conditions, influence the mechanical properties of the wood in use. The aim of this research was to study the influence of exposure time of the wood of four different hardwood species at a temperature of 60 °C on the shear strength parallel to fibers. The wood of the following species was used: Cupiúba (Goupia glabra), Eucalyptus (Eucalyptus saligna), Garapeira (Apuleia leiocarpa), and Jatobá Tamarindo (Hymenaea sp.). In order to investigate the effect of exposure time (0, 168, 456, 720, and 2160 hours) of the wood species in an oven (60 °C) on the values of shear strength in the direction parallel to fibers, an analysis of variance (ANOVA) was carried out at 5% significance level. According to the results, the time the wood was exposed to the operating temperature significantly influenced the shear strength in the direction parallel to fibers. In addition, all species showed a decrease in shear strength after 456 hours of exposure at a constant temperature of 60 °C.

ABSTRACT The aim of this research was to analysis the feasibility of production of wood particleboard with two alternative adhesives: epoxy ink waste and polyhydroxybutyrate polymer (BTH). Particleboard were produced with Pinus sp. wood specie wastes from sawmill process. For each alternative adhesive was proposed different combinations of parameters: time and temperature of press, pressure; alternative adhesive content and mass of wood particles. Two alternative adhesive contents were adopted, 10% and 20% replacing ureaformaldehyde adhesive. Mechanical properties (perpendicular tensile strength, pullout strengths of screw on face and top; modulus of elasticity and rupture) were determined according to ABNT NBR 14810:3 Brazilian Standard Code. The obtained results were compared to ABNT NBR 14810:3 and ANSI A.2018:1 Standard Codes requirements values. Particleboards produced with epoxy ink waste showed perpendicular tensile strength according to the minimum Standards requirements values. All proposed combinations to manufacture BTH polymer particleboards didn't show satisfactory mechanical properties in comparison to the Standard Codes values. Other combinations of wood species, time, pressure and temperature, epoxy ink waste and BTH polymer contents should be studied so that the requirements can be met.